Flexible Cellulose Paper‐based Asymmetrical Thin Film Supercapacitors with High‐Performance for Electrochemical Energy Storage

Cellulose paper (CP)‐based asymmetrical thin film supercapacitors (ATFSCs) have been considered to be a novel platform for inexpensive and portable devices as the CP is low‐cost, lightweight, and can be rolled or folded into 3D configurations. However, the low energy density and poor cycle stability are serious bottlenecks for the development of CP‐based ATFSCs. Here, sandwich‐structured graphite/Ni/Co₂NiO₄‐CP is developed as positive electrode and the graphite/Ni/AC‐CP as negative electrode for flexible and high‐performance ATFSCs. The fabricated graphite/Ni/Co₂NiO₄‐CP positive electrode shows a superior areal capacitance (734 mF/cm² at 5 mV/s) and excellent cycling performance with ≈97.6% C_sp retention after 15 000 cycles. The fabricated graphite/Ni/AC‐CP negative electrode also exhibits large areal capacitance (180 mF/cm² at 5 mV/s) and excellent cycling performance with ≈98% C_sp retention after 15 000 cycles. The assembled ATFSCs based on the sandwich‐structured graphite/Ni/Co₂NiO₄‐CP as positive electrode and graphite/Ni/AC‐CP as negative electrode exhibit large volumetric C_sp (7.6 F/cm³ at 5 mV/s), high volumetric energy density (2.48 mWh/cm³, 80 Wh/kg), high volumetric power density (0.79 W/cm³, 25.6 kW/kg) and excellent cycle stability (less 4% C_sp loss after 20 000 cycles). This study shows an important breakthrough in the design and fabrication of high‐performance and flexible CP‐based electrodes and ATFSCs.