Spontaneous Formation of Ordered Lateral Patterns in Polymer Thin‐Film Structures

T. Okayasu, H.‐L. Zhang, D. G. Bucknall, G. A. D. Briggs

Advanced Functional Materials· Volume 14· Issue 11
Publisher page

Abstract

Abstract The understanding of the lateral morphology stability of thin polymer devices is of fundamental importance. In this work, the lateral morphology in a model system consisting of thin polymer films capped with thin metal layers on a Si substrate is investigated. When the model system is heated above a critical temperature, a characteristic surface topographic structure is observed that has a well‐defined periodicity but random orientation. It is shown that the minimum temperature, Tmin, required for the surface pattern to be observed decreases with increasing polymer‐film thickness. Increasing either the metal‐ or polymer‐layer thickness increases the characteristic wavelength of the topography. It is believed that the dominating driving force for the surface corrugated‐pattern formation is the thermal‐expansion‐coefficient mismatch of the capping layer and the substrate. A theoretical model based on local bending of a thin, stiff surface film on a thin, elastic medium is used to provide a quantitative analysis of the surface morphology. The calculated minimum temperature required for the surface morphology and the periodicity of the surface patterns to form are in strong agreement with the experimental results. By contrast, systems with prefabricated topographic patterns within any of the three layers (polymer, metal, substrate) produce highly anisotropic surface topographies aligned perpendicular to the prefabricated topographic structure. It is also found that, in a model system with pre‐patterned polymer films, a much higher critical temperature is required for the surface morphology to be observed. The changes in apparent stability and morphological orientation in the pre‐patterned systems can be understood as a result of the anisotropic release of the lateral surface stress during the heat treatment.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Fluid Dynamics and Thin Films · Nanofabrication and Lithography Techniques · Adhesion, Friction, and Surface Interactions

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (41)

Show source-provided references
1. 10.1146/annurev.matsci.28.1.15310.1146/annurev.matsci.28.1.153 ↗
2. 10.1038/372344a010.1038/372344a0 ↗
3. 10.1021/jp011611w10.1021/jp011611w ↗
4. 10.1038/3500661010.1038/35006610 ↗
5. 10.1126/science.290.5499.212310.1126/science.290.5499.2123 ↗
6. 10.1103/PhysRevLett.81.125110.1103/PhysRevLett.81.1251 ↗
7. 10.1038/3500659710.1038/35006597 ↗
8. 10.1063/1.132263810.1063/1.1322638 ↗
9. 10.1038/3607510.1038/36075 ↗
10. 10.1063/1.47949710.1063/1.479497 ↗
11. 10.1016/S0042-207X(01)00206-810.1016/S0042-207X(01)00206-8 ↗
12. 10.1063/1.143494910.1063/1.1434949 ↗
13. 10.1016/S0377-0257(01)00180-X10.1016/S0377-0257(01)00180-X ↗
14. 10.1038/3500254010.1038/35002540 ↗
15. J. N. Israelachvili Intermolecular and Surface Forces 2nd ed. Academic London1985.
16. R. A. L. Jones R. W. Richards Polymers at Surfaces and Interfaces Cambridge University Press Cambridge UK1999.
17. H. G. Allen Analysis and Design of Structural Sandwich Panels Pergamon Oxford UK1969.10.1016/B978-0-08-012870-2.50006-7 ↗
18. D. Williams D. M. A. Leggett H. G. Hopkins Flat Sandwich Panels Under Compressive End Loads ARC Technical Report R&M 1987 1941.
19. 10.1063/1.155889710.1063/1.1558897 ↗
20. 10.1038/3019310.1038/30193 ↗
21. 10.1021/la991302l10.1021/la991302l ↗
22. 10.1103/PhysRevE.57.581110.1103/PhysRevE.57.5811 ↗
23. 10.1103/PhysRevLett.82.148610.1103/PhysRevLett.82.1486 ↗
24. 10.1063/1.153122310.1063/1.1531223 ↗
25. 10.1002/polb.108810.1002/polb.1088 ↗
26. 10.1002/1521-4095(20021002)14:19<1383::AID-ADMA1383>3.0.CO;2-D10.1002/1521-4095(20021002)14:19<1383::AID-ADMA1383>3.0.CO;2-D ↗
27. 10.1063/1.12507610.1063/1.125076 ↗
28. 10.2514/8.207110.2514/8.2071 ↗
29. Goodier J. N. · J. Appl. Mech. · 1946 · 13 · A25310.1115/1.4009582 ↗
30. 10.1021/ma00037a01510.1021/ma00037a015 ↗
31. 10.1103/PhysRevLett.83.56410.1103/PhysRevLett.83.564 ↗
32. 10.1063/1.136818010.1063/1.1368180 ↗
33. 10.1016/S1359-6454(02)00120-910.1016/S1359-6454(02)00120-9 ↗
34. No attempt was made to quantitatively analyze the topography‐forming kinetics in our system because of the lack of reliable viscosity values under the experimental conditions. A time limit of 2 h was set only for practical reasons.
35. Polymer Handbook 4th ed. (Eds: J. Brandrup E. H. Immergut E. A. Grulke) Wiley New York1999.
36. 10.1016/S0079-6700(02)00080-110.1016/S0079-6700(02)00080-1 ↗
37. CRC Handbook of Chemistry and Physics 76th ed. (Eds: D. R. Lide H. P. R. Frederikse) CRC Press Boca Raton FL1995.
38. J. J. Alkonis W. J. MacKnight Introduction to Polymer Viscoelasticity 2nd ed. Wiley New York1983.
39. When heated aboveTg the biaxially stretched PET substrate exhibits a negative thermal‐expansion coefficient along the stretching direction but a positive thermal‐expansion coefficient along the perpendicular direction.
40. 10.1016/S0022-5096(96)00104-410.1016/S0022-5096(96)00104-4 ↗
41. 10.1023/A:100672822397810.1023/A:1006728223978 ↗