Capillary Force Lithography: Fabrication of Functional Polymer Templates as Versatile Tools for Nanolithography
Source abstract
Abstract
Abstract The implementation of high‐resolution polymer templates fabricated by capillary force lithography (CFL) is explored both in nanoimprint lithography (NIL) and in the wet‐etching of metals. Several different thermoplastic and UV‐curable polymers and types of substrates are incorporated into the general CFL procedure to meet the diverging requirements of these two applications. The mechanical stability of UV‐curable templates for imprinting in polymers, as examined by atomic force microscopy (AFM), and their anti‐adhesive properties are excellent for application in NIL. The conditions for curing the UV‐curable polymer are optimized in order to obtain high‐stability polymer templates. Gold patterns on silicon with a lateral resolution of 150 nm are fabricated by subsequent lift‐off in acetone. Similar patterns with a lateral resolution of 100 nm are fabricated using templates of thermoplastic polymers on gold layers on silicon as an etch mask. The transfer of stamp residues during CFL with these polymer templates is proven by X‐ray photoelectron spectroscopy (XPS) and AFM friction analysis. For poly(methylmethacrylate) (PMMA), the presence of large amounts of silicon‐containing residues is found to compromise the processability of the resulting template in subsequent O2 reactive‐ion etching (RIE) treatment. The extent of silicon contamination is up to six times less for polystyrene (PS). At this level, the etch performance of the PS etch mask is not affected, as was the case for PMMA. Accurate downscaling of the lateral dimensions of the resulting metal patterns by several factors with respect to the dimensions of the PS etch mask is achieved by over‐etching of the gold. Overall, the results in this paper demonstrate the potential of CFL templates as tools for high‐resolution soft lithography.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Nanofabrication and Lithography Techniques · Force Microscopy Techniques and Applications · Advancements in Photolithography Techniques
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (45)
Show source-provided references
1. 10.1147/rd.411.000710.1147/rd.411.0007 ↗
2. 10.1116/1.58923110.1116/1.589231 ↗
3. 10.1116/1.58923210.1116/1.589232 ↗
4. 10.1016/0042-207X(92)90270-710.1016/0042-207X(92)90270-7 ↗
5. 10.1002/(SICI)1521-3773(19980316)37:5<550::AID-ANIE550>3.0.CO;2-G10.1002/(SICI)1521-3773(19980316)37:5<550::AID-ANIE550>3.0.CO;2-G ↗
6. 10.1126/science.272.5258.8510.1126/science.272.5258.85 ↗
7. 10.1063/1.11898810.1063/1.118988 ↗
8. 10.1021/ja020946410.1021/ja0209464 ↗
9. 10.1063/1.12262110.1063/1.122621 ↗
10. 10.1002/1521-4095(200104)13:8<604::AID-ADMA604>3.0.CO;2-J10.1002/1521-4095(200104)13:8<604::AID-ADMA604>3.0.CO;2-J ↗
11. 10.1038/2973010.1038/29730 ↗
12. 10.1021/ja990858s10.1021/ja990858s ↗
13. 10.1021/nl048497o10.1021/nl048497o ↗
14. 10.1002/1521-4095(200109)13:18<1386::AID-ADMA1386>3.0.CO;2-X10.1002/1521-4095(200109)13:18<1386::AID-ADMA1386>3.0.CO;2-X ↗
15. 10.1002/adma.20030652310.1002/adma.200306523 ↗
16. 10.1002/1616-3028(20020618)12:6/7<405::AID-ADFM405>3.0.CO;2-110.1002/1616-3028(20020618)12:6/7<405::AID-ADFM405>3.0.CO;2-1 ↗
17. For information on the effect of curing conditions on the material properties of PDMS stamps seehttp://www.zurich.ibm.com/st/microcontact/stamps/material.html(accessed September 2005).
18. 10.1063/1.146789810.1063/1.1467898 ↗
19. 10.1063/1.181021210.1063/1.1810212 ↗
20. 10.1088/0960-1317/14/8/01010.1088/0960-1317/14/8/010 ↗
21. 10.1021/ma011890l10.1021/ma011890l ↗
22. 10.1016/S0167-9317(04)00096-610.1016/S0167-9317(04)00096-6 ↗
23. 10.1016/S0169-4332(99)00014-810.1016/S0169-4332(99)00014-8 ↗
24. 10.1016/S0167-9317(02)00470-710.1016/S0167-9317(02)00470-7 ↗
25. The presence of fluorine‐containing additives that are well known for lowering the surface energy of any surface was excluded by XPS analysis of mr‐L6000. Although no specific elements were detected by XPS analysis that could confirm the presence of other types of surfactants in this commercial resist the product specifications confirm the use of such additives in mr‐L6000 (i.e. “surface smoothers”) in order to increase the surface smoothness of resist layers in spin‐coating. Furthermore the low pattern density can account in part for the excellent properties of the cured mr‐L6000 templates as NIL molds.
26. 10.1116/1.130527210.1116/1.1305272 ↗
27. 10.1021/cm00060a02310.1021/cm00060a023 ↗
28. 10.1116/1.58975210.1116/1.589752 ↗
29. 10.1039/a810043h10.1039/a810043h ↗
30. 10.1021/cm031024i10.1021/cm031024i ↗
31. 10.1002/amo.86004020610.1002/amo.860040206 ↗
32. G. Beamson D. Briggs High Resolution XPS of Organic Polymers: The Scienta ESCA300 Database John Wiley & Sons Chichester UK1992.
33. AFM height analysis demonstrates that 80 nm of the 150 nm thick residual layer is still present in the contact areas after 100 s O2RIE. Calculations suggest that the AFM height profile in Figure 8a is the result of an etch rate reduction of at least 60 % (from 1.9 to 0.7 nm s–1).
34. 10.1021/la026558x10.1021/la026558x ↗
35. H. Gokan Y. Saotome K. Saigo F. Watanabe Y. Ohnishi inPolymers for High Technology Electronics and Photonics(Eds: S. R. Turner M. J. Bowden) ACS Symposium Series American Chemical Society Washington DC1986 pp. 358–368.10.1021/bk-1987-0346.ch030 ↗
36. J. F. Moulder W. F. Stickle P. E. Sobol K. Bomben Handbook of X‐ray Photoelectron Spectroscopy(Ed: J. Chastain) Perkin–Elmer Corporation Eden Prairie MN1992.
37. 10.1021/cm98031410.1021/cm980314 ↗
38. W. Kern C. A. Deckert inThin Film Processes II(Eds: J. L. Vossen W. Kern) Academic Boston MA1978.
39. At these dimensions the standard deviation (σ) in the line width of the gold rings is ca. 30 nm: about 50 % of the ring in Figure 9c (and Fig. 10e for close‐up SEM image) has lateral dimensions in the sub‐100 nm range (> 70 nm).
40. At these dimensions the grain size of the metal layer is known to affect the ultimate resolution. For our gold layers a grain size distribution of 30–60 nm was determined by AFM.
41. 10.1002/1521-4095(20020304)14:5<346::AID-ADMA346>3.0.CO;2-Y10.1002/1521-4095(20020304)14:5<346::AID-ADMA346>3.0.CO;2-Y ↗
42. 10.1016/j.susc.2004.01.04210.1016/j.susc.2004.01.042 ↗
43. 10.1088/0960-1317/15/2/02110.1088/0960-1317/15/2/021 ↗
44. 10.1021/ma982034l10.1021/ma982034l ↗
45. 10.1021/la00024a03010.1021/la00024a030 ↗