Self‐Organized Nanoporous Anodic Titania Films and Ordered Titania Nanodots/Nanorods on Glass

Abstract We report a new method to fabricate self‐organized nanoporous titania films (pore diameter ≈ 30 nm; ≈ 1100 nm thick) and ordered titania nanorod arrays (rod diameter ≈ 30–60 nm; 70–260 nm high) by combined anodizing of superimposed Al/Ti layers sputter‐deposited on glass substrates. The titania nanostructures mimic the ordered nanoporous anodic alumina films via a through‐mask anodization. We propose a new anodizing electrolyte, i.e., a diluted nitric acid solution, for fabricating uniform, self‐organized, ordered nanoporous titania films with parallel cylindrical pores and without any thickness limit. More significantly, the nanoporous titania films contain a small amount of titanium nitride and dissociated nitrogen, and exhibit a moderate transparency and an enhanced absorption throughout the UV and visible light regions of the electromagnetic spectrum. After heating at 600 °C for 2 h, the nanoporous titania films develop a small absorption red‐shift and exhibit high photocatalytic activity under UV illumination.