Design of Nanocomposite Low‐Friction Coatings

O. Wilhelmsson, M. Råsander, M. Carlsson, E. Lewin, B. Sanyal, U. Wiklund, O. Eriksson, U. Jansson

Advanced Functional Materials· Volume 17· Issue 10
Publisher page

Abstract

Abstract Friction and wear between moving surfaces is unavoidable and is an important reason for failure of mechanical components. A wear‐resistant and low‐friction coating can prolong the lifetime of an engineered component. Here we demonstrate a new concept for the design of low‐friction nanocomposite carbide coatings with an intrinsic driving force to form amorphous carbon (C–C bonds). Ti–Al–C has been chosen as a model system, but the idea is general and should be applicable to a wide class of materials. The ability to intrinsically form amorphous carbon is achieved by a substitutional solid solution of the weak‐carbide‐forming metal (Al) into the thermodynamically stable monocarbide (TiC). This creates, in a controllable manner, a driving force for phase separation of carbide particles embedded in a matrix of amorphous carbon. In a tribological contact the amorphous carbon can be further graphitized and thereby lower the friction coefficient. Consequently, the model system has a self‐lubricating mechanism but at the same time a tunable share of the two phases, which gives excellent possibilities to design wear resistance and toughness. In this paper we show that the friction coefficient can be lowered by more than 50 % for Al‐containing TiC coatings without severe loss in mechanical characteristics.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Diamond and Carbon-based Materials Research · Metal and Thin Film Mechanics · Advanced materials and composites

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (29)

Show source-provided references
1. S. Jacobson S. Hogmark Tribologi: Friktion Smörjning och Nötning Berlings Arlöv Sweden1996.
2. 10.1016/0925-9635(96)00538-910.1016/0925-9635(96)00538-9 ↗
3. 10.1016/0925-9635(94)90042-610.1016/0925-9635(94)90042-6 ↗
4. 10.1016/S0925-9635(00)00429-510.1016/S0925-9635(00)00429-5 ↗
5. 10.1063/1.36578410.1063/1.365784 ↗
6. 10.1016/j.tsf.2004.04.00710.1016/j.tsf.2004.04.007 ↗
7. 10.1023/A:100430742688710.1023/A:1004307426887 ↗
8. 10.1116/1.210181010.1116/1.2101810 ↗
9. 10.1016/j.surfcoat.2004.10.04110.1016/j.surfcoat.2004.10.041 ↗
10. 10.1016/S0043-1648(00)00381-110.1016/S0043-1648(00)00381-1 ↗
11. 10.1016/S0257-8972(01)01493-110.1016/S0257-8972(01)01493-1 ↗
12. 10.1016/S0043-1648(03)00340-510.1016/S0043-1648(03)00340-5 ↗
13. 10.1016/S0272-8842(96)00069-710.1016/S0272-8842(96)00069-7 ↗
14. 10.1103/PhysRevB.43.1440010.1103/PhysRevB.43.14400 ↗
15. M. Hansen Constitution of Binary Alloys McGraw‐Hill New York1958.10.1149/1.2428700 ↗
16. 10.1016/j.jcrysgro.2006.03.00810.1016/j.jcrysgro.2006.03.008 ↗
17. 10.1103/PhysRev.136.B86410.1103/PhysRev.136.B864 ↗
18. 10.1103/PhysRev.140.A113310.1103/PhysRev.140.A1133 ↗
19. 10.1103/PhysRevB.50.1795310.1103/PhysRevB.50.17953 ↗
20. 10.1103/PhysRevB.54.1116910.1103/PhysRevB.54.11169 ↗
21. 10.1103/PhysRevB.59.175810.1103/PhysRevB.59.1758 ↗
22. 10.1103/PhysRevB.43.194010.1103/PhysRevB.43.1940 ↗
23. L. E. Toth Transition Metal Carbides and Nitrides Academic New York1971.
24. B. D. Cullity Elements of X‐Ray Diffraction Addison‐Wesley Reading MA1978.
25. 10.1016/j.surfcoat.2003.10.07710.1016/j.surfcoat.2003.10.077 ↗
26. 10.1016/j.surfcoat.2004.10.10610.1016/j.surfcoat.2004.10.106 ↗
27. 10.1016/S0257-8972(03)00911-310.1016/S0257-8972(03)00911-3 ↗
28. 10.1016/S0040-6090(01)00939-710.1016/S0040-6090(01)00939-7 ↗
29. 10.1103/PhysRevB.45.1324410.1103/PhysRevB.45.13244 ↗