Stable and Efficient White Electroluminescent Devices Based on a Single Emitting Layer of Polymer Blends

Abstract An efficient orange‐light‐emitting polymer (PFTO‐BSeD5) has been developed through the incorporation of low‐bandgap benzoselenadiazole (BSeD) moieties into the backbone of a blue‐light‐emitting polyfluorene copolymer (PFTO poly{[9,9‐bis(4‐(5‐(4‐tert‐butylphenyl)‐[1,3,4]‐oxadiazol‐2‐yl)phenyl)‐9′,9′‐di‐n‐octyl‐[2,2′]‐bifluoren‐7,7′‐diyl]‐stat‐[9,9‐bis(4‐(N,N‐di(4‐n‐butylphenyl)amino)phenyl)‐9′,9′‐di‐n‐octyl‐[2,2′]‐bifluoren‐7,7′‐diyl]}) that contains hole‐transporting triphenylamine and electron‐transporting oxadiazole pendent groups. A polymer light‐emitting device based on this copolymer exhibits a strong, bright‐orange emission with Commission Internationale de L'Eclairage (CIE) color coordinates (0.45,0.52). The maximum brightness is 13 716 cd m^–2 and the maximum luminance efficiency is 5.53 cd A^–1. The use of blends of PFTO‐BSeD5 in PFTO leads to efficient and stable white‐light‐emitting diodes—at a doping concentration of 9 wt %, the device reaches its maximum external quantum efficiency of 1.64 % (4.08 cd A^–1). The emission color remains almost unchanged under different bias conditions: the CIE coordinates are (0.32,0.33) at 11.0 V (2.54 mA cm^–2, 102 cd m^–2) and (0.31,0.33) at 21.0 V (281 mA cm^–2, 7328 cd m^–2). These values are very close to the ideal CIE chromaticity coordinates for a pure white color (0.33,0.33).