Ultrahigh Bonding Strength of Dissimilar Metals Manufactured through Additive Manufacturing
Source abstract
Abstract
Abstract Dissimilar metals have exceptional development prospects in many fields due to their unique properties. However, the formation of brittle intermetallic compounds (IMCs) in dissimilar metals significantly reduces the bonding strength and causes interface cracking. In this study, a novel solid solution design concept is proposed to solve the problem. And ultrahigh bonding strength of TC4 titanium alloy/316L stainless steel dissimilar metal is achieved through additive manufacturing, with a CrCuV solid solution alloy interlayer. By utilizing the high‐entropy effect, continuous solid solutions are formed and the brittle IMCs layer is completely inhibited at the heterogeneous interface. The excellent metallurgical bonding of TC4/316L dissimilar metal results in an unprecedented shear strength of 345 MPa. This strategy successfully breaks through the bottleneck of bonding strength in dissimilar metals, greatly promotes the development and application of dissimilar metals.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: High Entropy Alloys Studies · Titanium Alloys Microstructure and Properties · Additive Manufacturing Materials and Processes
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Institute of Laser Additive Manufacturing Soochow University Suzhou 215021 P. R. China
Funding
National Natural Science Foundation of China
References (49)
Show source-provided references
1. 10.1016/j.matdes.2013.07.04410.1016/j.matdes.2013.07.044 ↗
2. 10.1016/j.actamat.2016.06.06410.1016/j.actamat.2016.06.064 ↗
3. 10.3390/app1218903410.3390/app12189034 ↗
4. 10.1016/j.actamat.2023.11957210.1016/j.actamat.2023.119572 ↗
5. 10.1016/j.matdes.2009.06.02910.1016/j.matdes.2009.06.029 ↗
6. 10.1016/j.matdes.2016.03.07310.1016/j.matdes.2016.03.073 ↗
7. 10.1007/s00170-016-8732-z10.1007/s00170-016-8732-z ↗
8. 10.1016/j.matlet.2020.12806410.1016/j.matlet.2020.128064 ↗
9. 10.1016/j.matlet.2023.13546610.1016/j.matlet.2023.135466 ↗
10. 10.1016/j.jmrt.2019.11.06810.1016/j.jmrt.2019.11.068 ↗
11. 10.1016/j.matdes.2013.04.08810.1016/j.matdes.2013.04.088 ↗
12. 10.1016/j.matdes.2012.09.05810.1016/j.matdes.2012.09.058 ↗
13. 10.1016/j.msea.2014.10.08410.1016/j.msea.2014.10.084 ↗
14. 10.1016/j.optlastec.2023.10931910.1016/j.optlastec.2023.109319 ↗
15. 10.1016/j.matdes.2013.07.10310.1016/j.matdes.2013.07.103 ↗
16. 10.1016/j.optlastec.2019.10595710.1016/j.optlastec.2019.105957 ↗
17. 10.1016/j.jmatprotec.2018.02.02010.1016/j.jmatprotec.2018.02.020 ↗
18. 10.1016/j.jmapro.2018.08.02210.1016/j.jmapro.2018.08.022 ↗
19. 10.1016/j.jmrt.2023.09.14810.1016/j.jmrt.2023.09.148 ↗
20. 10.1038/s41570-024-00602-510.1038/s41570-024-00602-5 ↗
21. 10.1016/j.addma.2023.10352210.1016/j.addma.2023.103522 ↗
22. 10.1016/j.jmst.2024.04.02510.1016/j.jmst.2024.04.025 ↗
23. 10.1038/s41586-019-1783-110.1038/s41586-019-1783-1 ↗
24. 10.1038/s41467-019-13874-z10.1038/s41467-019-13874-z ↗
25. 10.1038/s41578-019-0121-410.1038/s41578-019-0121-4 ↗
26. 10.1016/j.actamat.2014.04.03310.1016/j.actamat.2014.04.033 ↗
27. 10.1002/adem.20070024010.1002/adem.200700240 ↗
28. 10.1016/j.intermet.2024.10829110.1016/j.intermet.2024.108291 ↗
29. 10.1016/j.jmrt.2018.06.00910.1016/j.jmrt.2018.06.009 ↗
30. 10.1007/s11661-018-5031-310.1007/s11661-018-5031-3 ↗
31. 10.1007/s00170-016-9453-z10.1007/s00170-016-9453-z ↗
32. 10.1007/s12666-021-02297-410.1007/s12666-021-02297-4 ↗
33. 10.1016/j.jallcom.2020.15665010.1016/j.jallcom.2020.156650 ↗
34. 10.1016/j.jallcom.2020.15438910.1016/j.jallcom.2020.154389 ↗
35. 10.3390/ma1401018010.3390/ma14010180 ↗
36. 10.1007/s00170-015-8244-210.1007/s00170-015-8244-2 ↗
37. 10.1016/j.jallcom.2022.16469810.1016/j.jallcom.2022.164698 ↗
38. 10.1016/j.jmrt.2022.09.06510.1016/j.jmrt.2022.09.065 ↗
39. 10.1016/j.msea.2021.14139010.1016/j.msea.2021.141390 ↗
40. 10.1016/j.actamat.2019.04.01810.1016/j.actamat.2019.04.018 ↗
41. 10.1080/21663831.2020.179683610.1080/21663831.2020.1796836 ↗
42. 10.1016/j.msea.2021.14250710.1016/j.msea.2021.142507 ↗
43. 10.1016/j.actamat.2016.06.02310.1016/j.actamat.2016.06.023 ↗
44. 10.1016/j.addma.2016.12.00610.1016/j.addma.2016.12.006 ↗
45. 10.1007/s40195-021-01316-z10.1007/s40195-021-01316-z ↗
46. 10.1038/s41467-020-16085-z10.1038/s41467-020-16085-z ↗
47. 10.1038/s41586-022-04914-810.1038/s41586-022-04914-8 ↗
48. 10.1038/s41467-020-20109-z10.1038/s41467-020-20109-z ↗
49. 10.1038/s41586-023-05952-610.1038/s41586-023-05952-6 ↗