A Rapid Synthesis of Amorphous LiTaOCl₄ Solid Electrolytes Through a Two‐Step Reaction Pathway for High‐Rate and Long‐Cycling Lithium Batteries

Abstract A simplified process to prepare solid electrolytes (SEs) that fulfill long cyclability, fast‐charging performance, and wide‐temperature feasibility in all‐solid‐state lithium batteries (ASSLBs) is important. Here, amorphous LiTaOCl₄ (aLTOC) SE is synthesized within only four hours via a two‐step reaction by high‐energy ball milling method, which exhibits high ionic conductivity and excellent interfacial compatibility. A bilayer SE based on aLTOC and sulfide along with corresponding ASSLBs, are constructed. Furthermore, slight evolution of the unusual microstructure in the chloride/sulfur interfacial region is observed and analyzed. Density functional theory calculations show that S tends to displace O sites in TaO₂Cl₄ octahedra instead of Cl sites. As a result of the enhanced interfacial stability and reduced formation of ionically insulating phases, the assembled ASSLBs achieve superior rate performance and cyclability in a wide temperature range. Notably, the ASSLBs show capacity retention of 84.4% and 77.6% after 2000 and 1000 cycles at current density of 10C at 30 and 60 °C, respectively. Importantly, even under −20 °C, the cell works stably over 1600 cycles with capacity retention of 76.3% at 0.5C. The work pave the way for the massive production of high‐performance amorphous chloride electrolytes and the realization of fast‐charging ASSLBs with long cycle life.