Structural and optical characterization of sol–gel derived Tm-doped BaTiO3 nanopowders and ceramics

Abstract Nanocrystalline Tm 3+ (5%)-doped BaTiO 3 (BT-Tm) has been synthesized by the sol–gel method. The morphology, structure, and optical properties of powders and ceramics were characterized. The average grain size of the gel precursor annealed at 700 and 900 °C was 20 nm and 30 nm, respectively. These powders were single phase and crystallized with a cubic structure while the BT-Tm sintered ceramics were crystallized with the tetragonal BaTiO 3 structure. The photoluminescence spectra showed typical transitions of Tm 3+ ions and a structure consistent with the Tm 3+ ions incorporation in the BaTiO 3 crystalline lattice. Thermoluminescence peaks recorded at 300 °C (for annealed samples) or at 230 °C for the ceramic sample were assigned to the recombination of the Tm 2+ -electron traps located mainly at the surface of the nano-crystals or inside the microcrystals, respectively.