journal article·2021-12-23Open access

Synthesis, Structure, and Properties of EuLnCuSe3 (Ln = Nd, Sm, Gd, Er)

Oleg Andreev, Victor Atuchin, Alexander Aleksandrovsky, Yuriy Denisenko, Boris Zakharov, Alexander Tyutyunnik, Navruzbek Habibullayev, Dmitriy Velikanov, Dmitriy Ulybin, Daniil Shpindyuk

Crystals· Volume 12· Issue 1

Abstract

EuLnCuSe3 (Ln = Nd, Sm, Gd, Er), due to their complex composition, should be considered new materials with the ability to purposefully change the properties. Samples of the EuLnCuSe3 were prepared using Cu, rare earth metal, Se (99.99%) by the ampoule method. The samples were obtained by the crystallization from a melt and annealed at temperatures 1073 and 1273 K. The EuErCuSe3 crystal structure was established using the single-crystal particle. EuErCuSe3 crystallizes in the orthorhombic system, space group Cmcm, KCuZrS3 structure type, with cell parameters a = 4.0555 (3), b = 13.3570 (9), and c = 10.4602 (7) Å, V = 566.62 (6) Å3. In structure EuErCuSe3, erbium ions are coordinated by selenium ions in the octahedral polyhedron, copper ions are in the tetrahedral coordination, europium ions are between copper and erbium polyhedra layers and are coordinated by selenium ions as two-cap trigonal prisms. The optical band gap is 1.79 eV. At 4.7 K, a transition from the ferrimagnetic state to the paramagnetic state was detected in EuErCuSe3. At 85 and 293 K, the compound is in a paramagnetic state. According to XRPD data, EuLnCuSe3 (Ln = Nd, Sm, Gd) compounds have a Pnma orthorhombic space group of the Eu2CuS3 structure type. For EuSmCuSe3, a = 10.75704 (15) Å, b = 4.11120 (5) Å, c = 13.37778 (22) Å. In the series of EuLnCuSe3 compounds, the optical band gap increases 1.58 eV (Nd), 1.58 eV (Sm), 1.72 eV (Gd), 1.79 eV (Er), the microhardness of the 205 (Nd), 210 (Sm), 225 (Gd) 235 ± 4 HV (Er) phases increases, and the thermal stability of the phases increases significantly. According to the measurement data of differential scanning calorimetry, the EuNdCuSe3 decomposes, according to the solid-phase reaction T = 1296 K, ΔH = 8.2 ± 0.8 kJ/mol. EuSmCuSe3 melts incongruently T = 1449 K, ΔH = 18.8 ± 1.9 kJ/mol. For the EuGdCuSe3, two (Tα↔β = 1494 K, ΔHα↔β = 14.8 kJ/mol, Tβ↔γ = 1530 K, ΔHβ↔γ = 4.8 kJ/mol) and for EuErCuSe3 three polymorphic transitions (Tα↔β = 1561 K, ΔHα↔β = 30.3 kJ/mol, Tβ↔γ = 1579 K, ΔHβ↔γ = 4.4 kJ/mol, and Tγ↔δ = 1600 K, ΔHγ↔δ = 10.1 kJ/mol). The compounds melt incongruently at the temperature of 1588 K, ΔHmelt = 17.9 ± 1.8 kJ/mol and 1664 K, ΔHmelt = 25.6 ± 2.5 kJ/mol, respectively. Incongruent melting of the phases proceeds with the formation of a solid solution of EuSe and a liquid phase.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Crystal Structures and Properties · Iron-based superconductors research · Rare-earth and actinide compounds

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Institute of Chemistry, University of Tyumen, 625003 Tyumen, Russia

Laboratory of Optical Materials and Structures, Institute of Semiconductor Physics, SB RAS, 630090 Novosibirsk, Russia

Research and Development Department, Kemerovo State University, 650000 Kemerovo, Russia

Department of Industrial Machinery Design, Novosibirsk State Technical University, 630073 Novosibirsk, Russia

Kirensky Institute of Physics, Federal Research Center, KSC, SB RAS, 660036 Krasnoyarsk, Russia

Department of Photonics and Laser Technology, Siberian Federal University, 660036 Krasnoyarsk, Russia

Department of General and Special Chemistry, Industrial University of Tyumen, 625000 Tyumen, Russia

Boreskov Institute of Catalysis, SB RAS, 630090 Novosibirsk, Russia

Laboratory of Molecular Design and Ecologically Safe Technologies, Novosibirsk State University, 630090 Novosibirsk, Russia

Institute of Solid State Chemistry, UB RAS, 620990 Ekaterinburg, Russia

References (60)

Show source-provided references
1. New Quaternary Chalcogenides BaLnMQ3 (Ln-Rare Earth; M = Cu, Ag; Q = S, Se)10.1006/jssc.1994.1176 ↗
2. Three structure types for strontium copper(I) lanthanide(III) selenides SrCuMSe3 (M = La, Gd, Lu)10.1016/j.jallcom.2005.09.090 ↗
3. Crystal structures of the RCuPbSe3 (R = Gd, Tb, Dy, Ho, Er, Tm, Yb and Lu) compounds10.1016/j.jallcom.2004.06.023 ↗
4. Crystal structure and magnetic properties of YbCuPbSe310.1016/j.jallcom.2005.06.076 ↗
5. Crystal structures of the compounds YCuPbSe3, Y3CuSnSe7 and Y3Cu0.685Se610.1016/j.jallcom.2004.04.123 ↗
6. Open-framework chalcogenides as visible-light photocatalysts for hydrogen generation from water10.1002/anie.200500346 ↗
7. Three-dimensional open framework built from Cu-S icosahedral clusters and its photocatalytic property10.1021/ja805449p ↗
8. New layered materials: Syntheses, structures, and optical and magnetic properties of CsGdZnSe3, CsZrCuSe3, CsUCuSe3, and BaGdCuSe310.1021/ic0104353 ↗
9. Crystal structure of the R2PbS4 (R = Yb and Lu) compounds10.1016/j.jallcom.2006.11.110 ↗
10. Solvothermal syntheses and characterizations of four quaternary copper sulfides BaCu3MS4 (M = In, Ga) and BaCu2MS4 (M = Sn, Ge)10.1021/acs.inorgchem.9b01742 ↗
11. The system Ag2Se–Ho2Se3 in the 0–50 mol. % Ho2Se3 range and the crystal structure of two polymorphic forms of AgHoSe210.1016/j.materresbull.2006.09.012 ↗
12. Crystal and electronic structure of the new quaternary sulfides TlLnAg2S3 (Ln = Nd, Sm and Gd)10.1016/j.jssc.2017.08.028 ↗
13. Rare Earth chalcogels NaLnSnS4 (Ln = Y, Gd, Tb) for selective adsorption of volatile hydrocarbons and gases10.1002/zaac.201700082 ↗
14. DFT-investigation on anisotropy degree of electronic, optical, and mechanical properties of olivine ZnRE2S4 (RE = Er, Tm) compounds10.1088/2053-1591/ab6254 ↗
15. Ba5Cu8In2S12: A quaternary semiconductor with a unique 3D copper-rich framework and ultralow thermal conductivity10.1039/C6CC09904A ↗
16. Crystal structures and magnetic properties of novel rare-earth copper sulfides, EuRCuS3 (R = Y, Gd-Lu)10.1088/0953-8984/16/30/012 ↗
17. Synthesis, structure, and properties of EuScCuS3 and SrScCuS310.1016/j.jssc.2020.121926 ↗
18. New Quaternary Chalcogenides BaLnMQ3 (Ln = Rare Earth or Sc; M = Cu, Ag; Q = S, Se) II Structure and.pdf10.1006/jssc.1994.1177 ↗
19. Synthesis and Characterization of a Series of Quaternary Chalcogenides BaLnMQ3 (Ln = Rare Earth, M = Coinage Metal, Q = Se or Te)10.1006/jssc.1999.8359 ↗
20. Quaternary strontium copper(I) lanthanoid(III) selenides with cerium and praseodymium: SrCuCeSe3 and SrCuPrSe3, unequal brother and sister10.1515/znb-2004-0907 ↗
21. Synthesis, Structure, and Conductivity of the New Group IV Chalcogenides, KCuZrQ3 (Q = S, Se, Te)10.1016/0022-4596(92)90182-U ↗
22. Synthesis, structure, and properties of EuErCuS310.1016/j.jallcom.2019.07.059 ↗
23. Regularities of the property changes in the compounds EuLnCuS3 (Ln = La-Lu)10.1016/j.jallcom.2021.159968 ↗
24. Optical Materials Containing Rare Earth Ln2S3 Sulfides10.1016/0925-8388(94)07063-6 ↗
25. Sealed crucible technique for thermal analysis of volatile compounds up to 2500 °C: Melting points of EuO, EuS, EuSe and EuTe10.1016/0022-0248(72)90116-9 ↗
26. Crystal structure of erbium sesquiselenide, Er2Se310.1016/0925-8388(94)01394-2 ↗
27. Sm–Sm2Se3 phase diagram and properties of phases10.1134/S0036023616010095 ↗
28. Phase equilibria of the Gd-Se system10.1016/0025-5408(82)90062-9 ↗
29. Phase relations in the SnSe2-Er2Se3 system10.1023/A:1025501103988 ↗
30. The CuGaSe2–CuInSe2–2CdS system and single crystal growth of the g-phase10.1016/j.jcrysgro.2010.10.150 ↗
31. Cu2ZnSnS4 crystal growth using an SnCl2 based flux10.1039/D0CE01264E ↗
32. The Copper–Selenium System at Temperatures to 850 K and Pressures to 50 Kbar10.1139/v75-122 ↗
33. The Cu-Se (Copper-Selenium) system10.1007/BF02868284 ↗
34. The crystal structure and lattice parameters of some rare earth mono-seleno oxides10.1107/S0365110X60000339 ↗
35. Investigation by the use of profile refinement of neutron powder diffraction data of the geometry of the (Si2O7)6-ions in the high temperature phases of rare earth disilicates prepared from the melt in crucible-free synthesis
36. Antipov, E., Putilin, S., and Shpanchenko, R. (1994). ICDD Grant-in-Aid, Moscow State University.
37. Sur les systmes forms entre les slniures L2Se3 des lments des terres rares et le slniure EuSe d’europium
38. Synthesis and crystal structure of new rare-earth copper oxyselenides: R Cu Se O (R = La, Sm, Gd and Y)10.1016/0025-5408(94)90134-1 ↗
39. Valende change of Sm ion in Eu1-xSmxSe10.1016/0038-1098(83)90461-1 ↗
40. Powder X ray and IR studies of the new oxyselenides M O Cu Se (M = Bi, Gd, Dy)10.1006/jssc.1995.1312 ↗
41. EXPGUI, a graphical user interface for GSAS10.1107/S0021889801002242 ↗
42. Larson, A.C., and von Dreele, R.B. (2004). General Structure Analysis System (GSAS), APS, Aragone National Laboratory. Los Alamos National Laboratory Report LAUR.
43. STOE & Cie (2013). X-AREA, STOE & Cie GmbH.
44. Rigaku, O.D. (2019). CrysAlis PRO, Rigaku Oxford Diffraction Ltd.
45. SHELXT—Integrated space-group and crystal-structure determination10.1107/S2053273314026370 ↗
46. Crystal structure refinement with SHELXL10.1107/S2053229614024218 ↗
47. ShelXle: A Qt graphical user interface for SHELXL10.1107/S0021889811043202 ↗
48. (2021, December 21). Joint CCDC/FIZ Karlsruhe Online Deposition Service. Available online: https://www.ccdc.cam.ac.uk/structures/.
49. Velikanov, D.A. (2021, December 21). Vibration Magnetic Meter. RF Patent for the Invention RU2341810 (C1). Publ. 20.12.2008, Bulletin No. 35. Available online: https://worldwide.espacenet.com/patent/search?q=RU2341810.
50. Electromagnet for physico-chemical studies
51. High-sensitivity measurements of the magnetic properties of materials at cryogenic temperatures10.1134/S2075113320040413 ↗
52. Velikanov, D.A. (2021, December 21). Magnetometer with a Superconducting Quantum Interferometric Sensor. RF Patent for the Invention RU2481591 (C1). Publ. 10.05.2013, Bulletin No. 13. Available online: https://worldwide.espacenet.com/patent/search?q=RU2481591.
53. NETZSCH Proteus 6 (2012). Thermic Analyses—User’s and Software Manuals, Netzsch-Gerätebau.
54. Revised Effective Ionic Radii and Systematic Studies of Interatomic Distances in Halides and Chalcogenides10.1107/S0567739476001551 ↗
55. Temperatures and enthalpies of melting of Ln2S3 (Ln = Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu) compounds10.1007/s10973-017-6620-x ↗
56. Persistent luminescence in Eu2+-doped compounds: A review10.3390/ma3042536 ↗
57. Trends in thermodynamic parameters of phase transitions of lanthanide sulfides SrLnCuS3 (Ln = La − Lu)10.1007/s10973-016-6010-9 ↗
58. Synthsis, structural and spectroscopic properties of orthorhombic compounds BaLnCuS3 (Ln = Pr, Sm)10.1016/j.jallcom.2019.153134 ↗
59. Synthesis, structure, melting and optical properties of three complex orthorhombic sulfides BaDyCuS3, BaHoCuS3 and BaYbCuS310.1016/j.materresbull.2021.111314 ↗
60. Experimental and DFT study of BaLaCuS3: Direct band gap semiconductor10.1016/j.jpcs.2020.109670 ↗