Mesostructured Arrays of Nanometer‐spaced Gold Nanoparticles for Ultrahigh Number Density of SERS Hot Spots

A novel one‐trough synthesis via an air‐water interface is demonstrated to provide hexagonally packed arrays of densely spaced metallic nanoparticles (NPs). In the synthesis, a mesostructured polyoxometalate (POM)‐silicatropic template (PSS) is first self‐assembled at the air‐water interface; upon UV irradiation, anion exchange cycles enable the free‐floating PSS film to continuously uptake gold precursors from the solution subphase for diffusion‐controlled and POM‐site‐directed photoreduction inside the silica channels. NPs ≈ 2 nm can hence be homogeneously formed inside the silica‐surfactant channels until saturation. As revealed via X‐ray diffraction, small‐angle X‐ray scattering (SAXS), grazing incidence SAXS, and transmission electron microscopy, the Au NPs directed by the PSS template are arrayed into a 2D hexagonal lattice with inter‐channel spacing of 3.2 nm and a mean along‐channel NP spacing of 2.8 nm. This corresponds to an ultra‐high number density (≈10¹⁹ NPs cm⁻³) of narrowly spaced Au NPs in the Au‐NP@PSS composite, leading to 3D densely deployed hot‐spots along and across the mesostructured POM‐silica channels for surface‐enhanced Raman scattering (SERS). Consequently, the Au‐NP@PSS composite exhibits prominent SERS with 4‐mercaptobenzoic acid (4‐MBA) adsorbed onto Au NPs. The best 4‐MBA detection limit is 5 nm, with corresponding SERS enhancement factors above 10⁸.