A MoS₂ and Graphene Alternately Stacking van der Waals Heterostructure for Li⁺/Mg²⁺ Co‐Intercalation

Abstract Owing to the low‐cost, dendrite‐free formation, and high volumetric capacity, rechargeable Li⁺/Mg²⁺ hybrid‐ion batteries (LMIBs) have attracted great attention and are regarded as promising energy storage devices. However, due to the strong Coulombic interaction of Mg²⁺ with host materials, the traditional “Daniell Type” LMIBs with only Li⁺ intercalation usually cannot ensure a satisfactory energy density. Herein, graphene monolayers are arranged intercalating into MoS₂ interlamination to construct van der Waals heterostructures (MoS₂/G VH). This operation transforms the construction of ion channels from pristine interlamination of two MoS₂ monolayers to the interlamination of MoS₂ monolayer with graphene monolayer, thereby greatly reducing ion diffusion energy barriers. Compared with pristine MoS₂, the MoS₂/G VH can obviously reduce the migration energy barriers of Li⁺ (from 0.67 to 0.09 eV) and Mg²⁺ (from 1.01 to 0.21 eV). Moreover, it is also demonstrated that MoS₂/G VHs realize Li⁺/Mg²⁺ co‐intercalation even at a rate current of 1000 mA g⁻¹. As expected, the MoS₂/G VH exhibits superior electrochemical performance with a reversible capacity of 145.8 mAh g⁻¹ at 1000 mA g⁻¹ after 2200 cycles, suggesting the feasibility of potential applications for high‐performance energy storage devices.