Study on Growth Interface of Large Nd:YAG Crystals

A study was performed on the growth interface of a large-diameter 1 at% neodymium-doped yttrium aluminum garnet (Nd:YAG) single crystal grown using the Czochralski method. Red parallel light and an orthogonal polarizing system were used to observe the distribution of the central and lateral cores of the crystal at different growth interfaces. The solid–liquid interface of large-diameter Nd:YAG crystal growth was mainly determined via the interaction between natural and forced convection. The shape of the solid–liquid interface was mainly controlled via maintaining the crystal rotation rate and the temperature field. Interface inversion generally occurred during the shoulder-expanding stage and late stages of the growth of the cylindrical portion of the crystal. The occurrence of interface inversion is directly related to the temperature field, process parameters, and diameter of the crystal. The growth shape of the crystal interface determined the size and distribution of the central and lateral cores of the crystal. The area of the central and lateral cores was reduced via adjusting the temperature gradient of the solid–liquid interface and crystal rotation speed.