A review of residual stress effects on fatigue properties of friction stir welds
Source abstract
Abstract
Friction stir welding (FSW) is now widely used in industrial manufacturing fields to join metal materials. Although it avoids solidification cracking, the combination of thermal excursion and plastic deformation introduces significant residual stresses. These residual stresses will combine with the applied stresses in service to cause unexpected failure. Therefore, a detailed knowledge of the residual stress effects on fatigue characteristics of FSWs is required. In this review, the experimental, theoretical and numerical studies of residual stress effects on fatigue characteristics of FSWs are summarized, including fatigue crack initiation, fatigue crack growth, stress-life and residual stress relaxation. The applications of residual stress modification techniques for fatigue improvement in FSWs are also presented.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Advanced Welding Techniques Analysis · Welding Techniques and Residual Stresses · Aluminum Alloys Composites Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Aeronautics, Northwestern Polytechnical University, Xi’an, China
State Key Laboratory of Solidification Processing, Shaanxi Key Laboratory of Friction Welding Technologies, Northwestern Polytechnical University, Xi’an, China
School of Mechanical Engineering, Northwestern Polytechnical University, Xi’an, China
School of Mathematics and Statistics, Northwestern Polytechnical University, Xi’an, China
Funding
National Natural Science Foundation of China
References (100+)
Show source-provided references
1. Thomas W. M.; Nicholas E. D.; Needham J. C.; Murch M. G.; Templesmith P.; Dawes C. J. Friction Stir Welding International Patent Application No. PCT/GB92/02203 and GB Patent Application No. 9125978.8 December 6 1991.
2. 10.1016/S0261-3069(97)00062-910.1016/S0261-3069(97)00062-9 ↗
3. Jones C. S.; Venable R. Friction-Stir Welding of Large Scale Cryogenic Fuel Tanks for Aerospace Applications Proceedings of 5th International Conference on Trends in Welding Research Pine Mountain GA USA 1-5 Jun 1998 p. 553–557.
4. 10.4028/www.scientific.net/MSF.396-402.154310.4028/www.scientific.net/MSF.396-402.1543 ↗
5. 10.1016/j.pmatsci.2020.10070610.1016/j.pmatsci.2020.100706 ↗
6. 10.1016/j.surfcoat.2020.12583810.1016/j.surfcoat.2020.125838 ↗
7. 10.1016/S0142-1123(03)00059-810.1016/S0142-1123(03)00059-8 ↗
8. 10.1016/j.mser.2005.07.00110.1016/j.mser.2005.07.001 ↗
9. 10.1007/s11663-012-9716-510.1007/s11663-012-9716-5 ↗
10. 10.1007/s11661-014-2651-010.1007/s11661-014-2651-0 ↗
11. 10.1007/s11665-022-06832-210.1007/s11665-022-06832-2 ↗
12. 10.1007/s11665-022-06822-410.1007/s11665-022-06822-4 ↗
13. 10.1007/s11661-006-0159-y10.1007/s11661-006-0159-y ↗
14. 10.1179/174328009X41113610.1179/174328009X411136 ↗
15. 10.1007/s11340-014-9939-210.1007/s11340-014-9939-2 ↗
16. 10.1016/S0142-1123(02)00038-510.1016/S0142-1123(02)00038-5 ↗
17. 10.1016/j.actamat.2006.04.03410.1016/j.actamat.2006.04.034 ↗
18. 10.1016/j.tws.2017.09.00910.1016/j.tws.2017.09.009 ↗
19. 10.1088/0034-4885/70/12/R0410.1088/0034-4885/70/12/R04 ↗
20. 10.1016/j.jmapro.2021.06.04610.1016/j.jmapro.2021.06.046 ↗
21. 10.1016/j.engfracmech.2009.03.00610.1016/j.engfracmech.2009.03.006 ↗
22. 10.1016/j.pmatsci.2008.05.00110.1016/j.pmatsci.2008.05.001 ↗
23. 10.1016/j.pmatsci.2011.05.00310.1016/j.pmatsci.2011.05.003 ↗
24. 10.1016/j.pmatsci.2014.03.00310.1016/j.pmatsci.2014.03.003 ↗
25. 10.1016/j.engfracmech.2015.09.00710.1016/j.engfracmech.2015.09.007 ↗
26. 10.1016/j.matchar.2016.07.01010.1016/j.matchar.2016.07.010 ↗
27. 10.1016/j.pmatsci.2020.10075210.1016/j.pmatsci.2020.100752 ↗
28. 10.1016/j.intermet.2021.10712210.1016/j.intermet.2021.107122 ↗
29. 10.1080/10408436.2018.149025110.1080/10408436.2018.1490251 ↗
30. 10.1016/j.jmst.2017.10.01810.1016/j.jmst.2017.10.018 ↗
31. 10.1016/j.jmst.2017.10.02410.1016/j.jmst.2017.10.024 ↗
32. 10.1016/j.matdes.2017.12.03310.1016/j.matdes.2017.12.033 ↗
33. 10.1007/s11665-014-0968-x10.1007/s11665-014-0968-x ↗
34. Sergeeva, E. V. Friction Stir Welding in Aerospace Industry (Review). Paton Weld. J. 2013, May, p. 56–60.
35. 10.1016/j.jmapro.2018.10.00510.1016/j.jmapro.2018.10.005 ↗
36. 10.1016/j.jmst.2017.11.02910.1016/j.jmst.2017.11.029 ↗
37. 10.1007/s00170-016-9861-010.1007/s00170-016-9861-0 ↗
38. 10.1016/j.matdes.2015.07.07110.1016/j.matdes.2015.07.071 ↗
39. 10.1179/02670830110151008710.1179/026708301101510087 ↗
40. 10.1002/9781118402832.ch110.1002/9781118402832.ch1 ↗
41. 10.1002/9781118402832.ch210.1002/9781118402832.ch2 ↗
42. 10.1002/9781118402832.ch310.1002/9781118402832.ch3 ↗
43. 10.1002/9781118402832.ch410.1002/9781118402832.ch4 ↗
44. 10.1002/9781118402832.ch510.1002/9781118402832.ch5 ↗
45. 10.1002/9781118402832.ch610.1002/9781118402832.ch6 ↗
46. 10.1002/9781118402832.ch710.1002/9781118402832.ch7 ↗
47. 10.1002/9781118402832.ch810.1002/9781118402832.ch8 ↗
48. 10.1002/9781118402832.ch910.1002/9781118402832.ch9 ↗
49. 10.1002/9781118402832.ch1010.1002/9781118402832.ch10 ↗
50. 10.1002/9781118402832.ch1110.1002/9781118402832.ch11 ↗
51. 10.1016/j.matlet.2020.12834710.1016/j.matlet.2020.128347 ↗
52. 10.1016/j.acme.2018.02.00710.1016/j.acme.2018.02.007 ↗
53. 10.1007/s12666-022-02625-210.1007/s12666-022-02625-2 ↗
54. 10.1007/s12540-020-00921-410.1007/s12540-020-00921-4 ↗
55. 10.1016/j.ijpvp.2022.10478210.1016/j.ijpvp.2022.104782 ↗
56. 10.1007/s43452-022-00468-810.1007/s43452-022-00468-8 ↗
57. 10.1016/j.ijmachtools.2005.07.01310.1016/j.ijmachtools.2005.07.013 ↗
58. 10.1016/j.ijfatigue.2007.04.01610.1016/j.ijfatigue.2007.04.016 ↗
59. 10.1179/136217112X1343916018419610.1179/136217112X13439160184196 ↗
60. 10.1016/j.engfailanal.2020.10491110.1016/j.engfailanal.2020.104911 ↗
61. 10.1007/s00339020183010.1007/s003390201830 ↗
62. 10.1016/j.msea.2012.01.07110.1016/j.msea.2012.01.071 ↗
63. 10.1016/j.msea.2006.04.06610.1016/j.msea.2006.04.066 ↗
64. 10.1016/j.matdes.2012.10.03010.1016/j.matdes.2012.10.030 ↗
65. 10.1016/j.msea.2006.08.01210.1016/j.msea.2006.08.012 ↗
66. 10.1016/j.msea.2008.09.07810.1016/j.msea.2008.09.078 ↗
67. Mishra, R.; De, P.; Kumar, N. Friction Stir Welding and Processing; Springer Cham Heidelberg New York Dordrecht London, 2014; p. 13–58.
68. 10.1016/S1359-6454(03)00319-710.1016/S1359-6454(03)00319-7 ↗
69. 10.1177/030932471878976810.1177/0309324718789768 ↗
70. 10.2514/1.C00021210.2514/1.C000212 ↗
71. 10.1115/1.142963910.1115/1.1429639 ↗
72. 10.1016/j.corsci.2008.09.03110.1016/j.corsci.2008.09.031 ↗
73. Wang X.; Feng Z.; David S.; Spooner S.; Hubbard C. Diffraction Study of Residual Stresses in Friction Stir Welds The 6th International Conference on Residual Stresses (ICRS-6) London UK 2000 p. 1408–1415.
74. 10.4028/www.scientific.net/MSF.347-349.67810.4028/www.scientific.net/MSF.347-349.678 ↗
75. 10.1007/s11661-000-0136-910.1007/s11661-000-0136-9 ↗
76. Dalle Donne, C.; Lima, E.; Wegener, J.; Kaysser-Pyzalla, A.; Buslaps, T. 2001 Investigations on Residual Stresses in Friction Stir Welds. 3rd International Symposium on Friction Stir Welding, Kobe, Japan, Sept 27–28.
77. 10.1111/j.1460-2695.2008.01234.x10.1111/j.1460-2695.2008.01234.x ↗
78. 10.1111/j.1460-2695.2008.01258.x10.1111/j.1460-2695.2008.01258.x ↗
79. 10.1007/s00170-011-3210-010.1007/s00170-011-3210-0 ↗
80. 10.1007/s11661-011-0643-x10.1007/s11661-011-0643-x ↗
81. 10.1016/S1359-6462(03)00024-110.1016/S1359-6462(03)00024-1 ↗
82. 10.1007/s10853-014-8638-910.1007/s10853-014-8638-9 ↗
83. 10.1016/j.msea.2007.10.05510.1016/j.msea.2007.10.055 ↗
84. 10.1016/j.ijfatigue.2010.06.00110.1016/j.ijfatigue.2010.06.001 ↗
85. 10.1007/BF0258613910.1007/BF02586139 ↗
86. 10.1016/j.msea.2012.01.12910.1016/j.msea.2012.01.129 ↗
87. 10.1016/j.matchar.2017.02.01110.1016/j.matchar.2017.02.011 ↗
88. 10.1016/j.ijfatigue.2019.02.02310.1016/j.ijfatigue.2019.02.023 ↗
89. 10.1007/978-3-319-26324-3_3410.1007/978-3-319-26324-3_34 ↗
90. 10.1016/j.ijfatigue.2016.11.01110.1016/j.ijfatigue.2016.11.011 ↗
91. 10.1111/ffe.1229110.1111/ffe.12291 ↗
92. 10.1016/S0142-1123(01)00171-210.1016/S0142-1123(01)00171-2 ↗
93. 10.1520/STP1058-EB10.1520/STP1058-EB ↗
94. 10.1016/S0142-1123(98)00024-310.1016/S0142-1123(98)00024-3 ↗
95. 10.1016/j.ijfatigue.2003.08.00210.1016/j.ijfatigue.2003.08.002 ↗
96. 10.1016/0378-3804(84)90064-010.1016/0378-3804(84)90064-0 ↗
97. 10.1016/j.ijfatigue.2011.05.00810.1016/j.ijfatigue.2011.05.008 ↗
98. 10.1016/0013-7944(89)90089-110.1016/0013-7944(89)90089-1 ↗
99. 10.1520/STP26673S10.1520/STP26673S ↗
100. Swift T. Damage Tolerance in Pressurized Fuselages. In Proceedings of the 14th ICAF Symposium (Ottawa June 1987) New Materials and Fatigue Resistant Aircraft Design (ed.D. L. Simpson). EMAS London 1987 p. 1–78.