B2-strengthened Fe-Mn-Al-C-Ni steels as a promising environmentally friendly structural material: review and perspectives
Source abstract
Abstract
Inspired by the high entropy alloy design strategy, Fe-Mn-Al-C-Ni steels are classified as high-specific strength steels (HSSSs) or compositionally complex steels (CCSs) with a mainly austenite matrix. Fe-Mn-Al-C-Ni steels strengthened by (Ni,Al)-rich B2 phase have attracted vast attention due to its outstanding mechanical properties (yield strength up to 1600 MPa) combined with ductility (elongation 15–38%), low density (∼6.6–6.8 g/cm3),satisfactory corrosion and oxidation resistance. Thermomechanical processing, recrystallization and aging processes on the morphology of the NiAl-B2 phase, considering also relevant strengthening mechanisms, are analyzed. Future prospects of industrial application and research directions aimed at achieving an environmentally-friendly steel are indicated.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: High Entropy Alloys Studies · Microstructure and Mechanical Properties of Steels · High Temperature Alloys and Creep
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Faculty of Mechanical Engineering, Department of Metal Forming, Welding and Metrology, Wroclaw University of Science and Technology
Centre of Materials Science and Metal Forming, Wrocław University of Science and Technology
Department of Physical Metallurgy, National Center for Metallurgical Research (CENIM-CSIC)
Funding
National Science Centre Poland · Narodowe Centrum Nauki
References (100+)
Show source-provided references
1. 10.1007/s11661-020-05947-210.1007/s11661-020-05947-2 ↗
2. 10.1146/annurev-matsci-070214-02110310.1146/annurev-matsci-070214-021103 ↗
3. 10.1007/s43452-020-00088-010.1007/s43452-020-00088-0 ↗
4. 10.3390/ma1105076110.3390/ma11050761 ↗
5. 10.1016/j.msea.2021.14230010.1016/j.msea.2021.142300 ↗
6. 10.1016/j.jmst.2017.06.01710.1016/j.jmst.2017.06.017 ↗
7. 10.3390/met811092910.3390/met8110929 ↗
8. 10.1016/j.matpr.2020.01.29610.1016/j.matpr.2020.01.296 ↗
9. Grajcar, A.; Borek, W. Thermo-Mechanical Processing of High-Manganese Austenitic TWIP-Type Steels. Arch. Civ. Mech. Eng. 2008, 8, 29–38.10.1016/S1644-9665(12)60119-8 ↗
10. 10.1179/02670830110151034810.1179/026708301101510348 ↗
11. 10.1179/02670830110151035710.1179/026708301101510357 ↗
12. 10.1590/1980-5373-MR-2020-047010.1590/1980-5373-MR-2020-0470 ↗
13. 10.1016/j.actamat.2017.06.04610.1016/j.actamat.2017.06.046 ↗
14. 10.1016/j.msea.2020.14002310.1016/j.msea.2020.140023 ↗
15. 10.1080/09500839.2024.232255210.1080/09500839.2024.2322552 ↗
16. 10.3390/met1202019510.3390/met12020195 ↗
17. 10.1179/1743284713Y.000000042810.1179/1743284713Y.0000000428 ↗
18. 10.1016/j.jmrt.2022.12.17710.1016/j.jmrt.2022.12.177 ↗
19. 10.1038/s41586-019-1702-510.1038/s41586-019-1702-5 ↗
20. 10.1016/j.matdes.2022.11099410.1016/j.matdes.2022.110994 ↗
21. 10.1002/srin.20020002610.1002/srin.200200026 ↗
22. 10.1002/srin.20150013310.1002/srin.201500133 ↗
23. 10.1016/j.pmatsci.2020.10075410.1016/j.pmatsci.2020.100754 ↗
24. 10.1126/science.ado291910.1126/science.ado2919 ↗
25. 10.1016/j.pmatsci.2017.05.00210.1016/j.pmatsci.2017.05.002 ↗
26. 10.1007/s40195-021-01369-010.1007/s40195-021-01369-0 ↗
27. 10.1016/j.jmrt.2023.06.03710.1016/j.jmrt.2023.06.037 ↗
28. 10.1002/srin.20220019110.1002/srin.202200191 ↗
29. 10.2355/isijinternational.ISIJINT-2020-46710.2355/isijinternational.ISIJINT-2020-467 ↗
30. 10.1007/s11661-025-07775-810.1007/s11661-025-07775-8 ↗
31. 10.3390/met1008102110.3390/met10081021 ↗
32. 10.3390/met1210157210.3390/met12101572 ↗
33. Saha M. 2024.
34. 10.1016/j.actamat.2014.04.03110.1016/j.actamat.2014.04.031 ↗
35. 10.1038/nature1414410.1038/nature14144 ↗
36. 10.1016/j.intermet.2015.06.02110.1016/j.intermet.2015.06.021 ↗
37. 10.1002/adem.20030056710.1002/adem.200300567 ↗
38. 10.1016/j.scriptamat.2020.05.03010.1016/j.scriptamat.2020.05.030 ↗
39. 10.1016/j.jmrt.2024.03.01110.1016/j.jmrt.2024.03.011 ↗
40. 10.1126/sciadv.aba954310.1126/sciadv.aba9543 ↗
41. 10.1016/S1359-6454(03)00089-210.1016/S1359-6454(03)00089-2 ↗
42. 10.1016/j.dt.2022.11.01910.1016/j.dt.2022.11.019 ↗
43. 10.1016/j.scriptamat.2012.08.03810.1016/j.scriptamat.2012.08.038 ↗
44. 10.1007/BF0265670510.1007/BF02656705 ↗
45. 10.1016/j.actamat.2016.01.00710.1016/j.actamat.2016.01.007 ↗
46. 10.1007/BF0264322810.1007/BF02643228 ↗
47. 10.1016/j.matlet.2014.09.10410.1016/j.matlet.2014.09.104 ↗
48. 10.1002/srin.20060644010.1002/srin.200606440 ↗
49. 10.1016/j.actamat.2017.08.04910.1016/j.actamat.2017.08.049 ↗
50. 10.1016/j.msea.2022.14433110.1016/j.msea.2022.144331 ↗
51. 10.1016/j.ijhydene.2013.12.17110.1016/j.ijhydene.2013.12.171 ↗
52. 10.3390/ma1711269810.3390/ma17112698 ↗
53. 10.1007/s11661-009-0081-110.1007/s11661-009-0081-1 ↗
54. 10.1007/s11661-012-1149-x10.1007/s11661-012-1149-x ↗
55. 10.1088/1468-6996/14/1/01420510.1088/1468-6996/14/1/014205 ↗
56. Sutou, Y.; Kamiya, N.; Umino, R.; Ohnuma, I.; Ishida, K. High-Strength Fe-20Mn-Al-C-Based Alloys with Low Density. ISIJ Int 2010, 50, 893–899.10.2355/isijinternational.50.893 ↗
57. 10.1016/j.actamat.2012.11.04010.1016/j.actamat.2012.11.040 ↗
58. 10.1016/j.jallcom.2020.15501310.1016/j.jallcom.2020.155013 ↗
59. 10.1016/j.msea.2023.14477610.1016/j.msea.2023.144776 ↗
60. 10.1016/j.jmst.2021.10.01910.1016/j.jmst.2021.10.019 ↗
61. 10.1016/j.msea.2024.14688410.1016/j.msea.2024.146884 ↗
62. 10.1016/j.matdes.2023.11184010.1016/j.matdes.2023.111840 ↗
63. 10.1016/j.msea.2022.14403710.1016/j.msea.2022.144037 ↗
64. 10.1038/nmat95810.1038/nmat958 ↗
65. 10.1016/j.matchar.2009.03.02010.1016/j.matchar.2009.03.020 ↗
66. 10.1016/S0966-9795(97)00045-910.1016/S0966-9795(97)00045-9 ↗
67. 10.1007/s11669-008-9319-710.1007/s11669-008-9319-7 ↗
68. 10.1007/s11663-001-0077-810.1007/s11663-001-0077-8 ↗
69. 10.1179/09506609379032627610.1179/095066093790326276 ↗
70. 10.1016/j.msea.2024.14731710.1016/j.msea.2024.147317 ↗
71. 10.1016/j.actamat.2016.07.02010.1016/j.actamat.2016.07.020 ↗
72. 10.1016/j.ultramic.2008.10.01610.1016/j.ultramic.2008.10.016 ↗
73. 10.1016/j.actamat.2018.02.04410.1016/j.actamat.2018.02.044 ↗
74. 10.1016/j.actamat.2009.10.03010.1016/j.actamat.2009.10.030 ↗
75. 10.1080/02670836.2018.150114510.1080/02670836.2018.1501145 ↗
76. 10.1016/j.msea.2019.13836210.1016/j.msea.2019.138362 ↗
77. 10.1016/j.scriptamat.2024.11615310.1016/j.scriptamat.2024.116153 ↗
78. 10.1016/j.jmrt.2023.10.01610.1016/j.jmrt.2023.10.016 ↗
79. 10.1016/j.nantod.2025.10263710.1016/j.nantod.2025.102637 ↗
80. 10.1016/j.jmrt.2023.10.22910.1016/j.jmrt.2023.10.229 ↗
81. 10.1016/j.msea.2008.05.04210.1016/j.msea.2008.05.042 ↗
82. 10.1016/j.scriptamat.2010.07.03610.1016/j.scriptamat.2010.07.036 ↗
83. 10.1016/j.actamat.2016.02.04410.1016/j.actamat.2016.02.044 ↗
84. 10.1016/j.scriptamat.2019.02.01310.1016/j.scriptamat.2019.02.013 ↗
85. 10.1016/j.mtla.2021.10119810.1016/j.mtla.2021.101198 ↗
86. 10.1016/j.matlet.2023.13395410.1016/j.matlet.2023.133954 ↗
87. 10.1016/j.scriptamat.2018.09.04410.1016/j.scriptamat.2018.09.044 ↗
88. 10.1016/j.actamat.2012.07.01810.1016/j.actamat.2012.07.018 ↗
89. 10.1007/s11661-011-0993-410.1007/s11661-011-0993-4 ↗
90. 10.1016/j.actamat.2016.06.03710.1016/j.actamat.2016.06.037 ↗
91. 10.1016/j.jmrt.2024.05.13710.1016/j.jmrt.2024.05.137 ↗
92. 10.1016/j.msea.2024.14706610.1016/j.msea.2024.147066 ↗
93. 10.1016/j.msea.2022.14433010.1016/j.msea.2022.144330 ↗
94. 10.1016/j.actamat.2017.03.04310.1016/j.actamat.2017.03.043 ↗
95. 10.1016/j.mtla.2024.10204910.1016/j.mtla.2024.102049 ↗
96. 10.1016/j.msea.2022.14348710.1016/j.msea.2022.143487 ↗
97. 10.1016/j.msea.2025.14779810.1016/j.msea.2025.147798 ↗
98. 10.1016/j.jmatprotec.2024.11842310.1016/j.jmatprotec.2024.118423 ↗
99. 10.1007/s11837-022-05349-210.1007/s11837-022-05349-2 ↗
100. 10.1016/0036-9748(86)90208-510.1016/0036-9748(86)90208-5 ↗