On the Influence of Antioxidants and Recycled MgO–C Source Material on the Mechanical Properties of Carbon‐Bonded Magnesia Refractories
Source abstract
Abstract
In the present study, the role of recycled source material and the addition of antioxidants to refractory MgO–C material commonly used in the steel industry were addressed from the perspective of fracture mechanics. Initially, the fracture behaviour of the fine grained MgO–C‐matrix was assessed by sequential bending experiments (particle sizes <150 μm). Based on this, coarse grained parts with particle sizes up to 7 mm were prepared and characterised in regard to their high‐temperature properties, i.e. the refractoriness under load, the thermal expansion behaviour and the Young's modulus as function of the temperature. Four differently designed batches were tested. One batch, consisting of all fresh source materials (MgO and C), served as reference. Furthermore, the additives Al, SiO 2 and TiO 2 were systematically added, and 50% of the source material was replaced by recycled MgO–C from the industry. During the batch production, environmentally friendly fructose, collagen and lignin served as temporary binding agents. It was found that while the addition of recycled MgO–C had a reducing effect on the mechanical properties, the opposite was observed for the addition of antioxidants.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Magnesium Oxide Properties and Applications · Magnesium Alloys: Properties and Applications · Advanced ceramic materials synthesis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Institute of Ceramics, Refractories and Composite Materials Technical University Bergakademie Freiberg Freiberg Germany
Institute of Advanced Ceramics Hamburg University of Technology Hamburg Germany
Funding
German Research Foundation
References (41)
Show source-provided references
1. 10.1016/j.resconrec.2010.03.00310.1016/j.resconrec.2010.03.003 ↗
2. World Steel Association: World Steel in Figures 2025 · 2025
3. 10.1016/j.resconrec.2018.09.02510.1016/j.resconrec.2018.09.025 ↗
4. 10.1016/j.ceramint.2024.07.37210.1016/j.ceramint.2024.07.372 ↗
5. 10.1016/j.oceram.2023.10042610.1016/j.oceram.2023.100426 ↗
6. 10.1007/s00128990096610.1007/s001289900966 ↗
7. MgO–C Refractories Based on Refractory Recyclates and Environmentally Friendly Binders
8. 10.1016/0008-6223(95)00133-610.1016/0008-6223(95)00133-6 ↗
9. 10.1016/S0955-2219(00)00308-310.1016/S0955-2219(00)00308-3 ↗
10. 10.1016/j.jeurceramsoc.2006.03.00110.1016/j.jeurceramsoc.2006.03.001 ↗
11. 10.1016/j.ceramint.2006.10.00410.1016/j.ceramint.2006.10.004 ↗
12. 10.1016/j.ceramint.2012.01.06210.1016/j.ceramint.2012.01.062 ↗
13. 10.2355/isijinternational.54.222110.2355/isijinternational.54.2221 ↗
14. 10.1016/j.ceramint.2014.09.09110.1016/j.ceramint.2014.09.091 ↗
15. 10.1016/j.ceramint.2016.06.18010.1016/j.ceramint.2016.06.180 ↗
16. 10.1016/j.jallcom.2018.12.31010.1016/j.jallcom.2018.12.310 ↗
17. 10.1016/j.conbuildmat.2020.12191210.1016/j.conbuildmat.2020.121912 ↗
18. 10.1002/adem.20250271510.1002/adem.202502715 ↗
19. C. G.Aneziris D. K.Gunarsekar P.Gehre D.Veres S.Dudczig andJ.Hubálková German Patent Application no. 10 2025 120 670.8(2025).
20. 10.1080/17436753.2018.147144310.1080/17436753.2018.1471443 ↗
21. 10.1016/j.ceramint.2019.01.20010.1016/j.ceramint.2019.01.200 ↗
22. 10.1016/j.jeurceramsoc.2023.12.01310.1016/j.jeurceramsoc.2023.12.013 ↗
23. R Core Team · 2024
24. 10.1016/j.ceramint.2016.03.08010.1016/j.ceramint.2016.03.080 ↗
25. 10.1007/s10853-006-6770-x10.1007/s10853-006-6770-x ↗
26. 10.1016/j.actamat.2011.03.02310.1016/j.actamat.2011.03.023 ↗
27. 10.1111/j.1151-2916.1990.tb05260.x10.1111/j.1151-2916.1990.tb05260.x ↗
28. 10.1111/j.1151-2916.1994.tb07253.x10.1111/j.1151-2916.1994.tb07253.x ↗
29. Cyclic Fatigue in Monolithic Alumina: Mechanisms for Crack Advance Promoted by Frictional Wear of Grain Bridges
30. 10.2109/jcersj.102.2310.2109/jcersj.102.23 ↗
31. 10.2355/isijinternational.53.139210.2355/isijinternational.53.1392 ↗
32. 10.1016/j.ceramint.2018.04.24810.1016/j.ceramint.2018.04.248 ↗
33. 10.1016/j.ceramint.2023.08.08110.1016/j.ceramint.2023.08.081 ↗
34. 10.1016/j.actamat.2018.03.01810.1016/j.actamat.2018.03.018 ↗
35. 10.1016/j.mtla.2020.10076110.1016/j.mtla.2020.100761 ↗
36. Munz D. · 2001 · 25
37. 10.1111/j.1551-2916.2004.00037.x10.1111/j.1551-2916.2004.00037.x ↗
38. 10.1111/jace.1557510.1111/jace.15575 ↗
39. 10.1520/JTE11625J10.1520/JTE11625J ↗
40. Puttock M. · 1969
41. 10.1016/j.jmbbm.2020.10425310.1016/j.jmbbm.2020.104253 ↗