Sandwiched polydopamine (PDA) layer for titanium dioxide (TiO2) coating on magnesium to enhance corrosion protection
Source abstract
Abstract
Abstract A polydopamine (PDA) layer was sandwiched between a TiO 2 coating and Mg substrate to enhance the corrosion protection. The PDA layer was covalently immobilized on Mg, and the TiO 2 was coated by liquid phase deposition subsequently on it. The hybrid TiO 2 /PDA coated Mg exhibited significantly smaller free corrosion current density as well as a remarkably lower degradation rate in vitro (up to 21 days) in phosphate buffered saline compared to direct TiO 2 coated and untreated Mg. The efficacy is ascribed to the organic PDA layer which suppresses the electric pathway of galvanic corrosion cell and therefore corrosion rate of magnesium.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Magnesium Alloys: Properties and Applications · Corrosion Behavior and Inhibition · Polymer Surface Interaction Studies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (40)
Show source-provided references
1. Biodegradable metals10.1016/j.mser.2014.01.001 ↗
2. Strategies to improve the corrosion resistance of microarc oxidation (MAO) coated magnesium alloys for degradable implants: prospects and challenges10.1016/j.pmatsci.2013.08.002 ↗
3. Magnesium and its alloys as orthopedic biomaterials: a review10.1016/j.biomaterials.2005.10.003 ↗
4. The history of biodegradable magnesium implants: a review10.1016/j.actbio.2010.02.028 ↗
5. A survey of bio-corrosion rates of magnesium alloys10.1016/j.corsci.2009.09.033 ↗
6. Control of biodegradation of biocompatible magnesium alloys10.1016/j.corsci.2007.01.001 ↗
7. The possibility of forming a sacrificial anode coating for Mg10.1016/j.corsci.2014.07.007 ↗
8. A novel biodegradable Mg–Nd–Zn–Zr alloy with uniform corrosion behavior in artificial plasma10.1016/j.matlet.2012.08.012 ↗
9. Effects of extrusion and heat treatment on the mechanical properties and biocorrosion behaviors of a Mg–Nd–Zn–Zr alloy10.1016/j.jmbbm.2011.05.026 ↗
10. MgZnCa glasses without clinically observable hydrogen evolution for biodegradable implants10.1038/nmat2542 ↗
11. Corrosion of, and cellular responses to Mg–Zn–Ca bulk metallic glasses10.1016/j.biomaterials.2009.11.015 ↗
12. Protective coatings on magnesium and its alloys – a critical review10.1016/S0925-8388(01)01899-0 ↗
13. Surface design of biodegradable magnesium alloys – a review10.1016/j.surfcoat.2012.10.009 ↗
14. Anodizing treatment for magnesium alloys and their effect on corrosion resistance in various environments10.1002/adem.200500257 ↗
15. Electrochemical corrosion behavior of plasma electrolytic oxidation coatings on AM50 magnesium alloy formed in silicate and phosphate based electrolytes10.1016/j.electacta.2009.02.004 ↗
16. Corrosion properties of oxygen plasma immersion ion implantation treated magnesium10.1016/j.surfcoat.2006.02.088 ↗
17. Covalent immobilization of phytic acid on Mg by alkaline pre-treatment: corrosion and degradation behavior in phosphate buffered saline10.1016/j.corsci.2013.06.011 ↗
18. Effects of pretreatment and process temperature of a conversion coating produced by an aprotic ammonium-phosphate ionic liquid on magnesium corrosion protection10.1016/j.electacta.2013.12.167 ↗
19. Surface modification of a biodegradable magnesium alloy with phosphorylcholine (PC) and sulfobetaine (SB) functional macromolecules for reduced thrombogenicity and acute corrosion resistance10.1021/la401341y ↗
20. A surface-eroding poly(1,3-trimethylene carbonate) coating for fully biodegradable magnesium-based stent application: toward better biofunction, biodegradation and biocompatibility10.1016/j.actbio.2013.02.041 ↗
21. Hemocompatibility of titanium oxide films10.1016/S0142-9612(03)00046-2 ↗
22. In vitro degradation of AZ31 magnesium alloy coated with nano TiO2 film by sol–gel method10.1016/j.apsusc.2011.03.148 ↗
23. Preparation and characterization of oxide films containing crystalline TiO2 on magnesium alloy by plasma electrolytic oxidation10.1016/j.electacta.2007.01.059 ↗
24. Templated site-selective deposition of titanium dioxide on self-assembled monolayers10.1021/cm0107528 ↗
25. Dopamine/TiO2 hybrid thin films prepared by the liquid phase deposition method10.1016/j.tsf.2007.06.165 ↗
26. Conversion coating treatment for AZ91 magnesium alloys by a permanganate-REMS bath10.1002/maco.200604000 ↗
27. In vitro investigation of enhanced hemocompatibility and endothelial cell proliferation associated with Quinone-rich polydopamine coating10.1021/am3027635 ↗
28. Deposition mechanism of anatase TiO2 on self-assembled monolayers from an aqueous solution10.1021/cm030255m ↗
29. The in vitro degradation process and biocompatibility of a ZK60 magnesium alloy with a forsterite-containing micro-arc oxidation coating10.1016/j.actbio.2012.12.016 ↗
30. Measurement of the corrosion rate of magnesium alloys using Tafel extrapolation10.1016/j.corsci.2009.10.016 ↗
31. Biomedical coatings on magnesium alloys – a review10.1016/j.actbio.2012.04.012 ↗
32. Polydopamine and its derivative materials: synthesis and promising applications in energy, environmental, and biomedical fields10.1021/cr400407a ↗
33. Effects of substrate surface functionality on solution-deposited titania films10.1021/cm010776e ↗
34. Nanoscale magnesium hydroxide and magnesium oxide powders: control over size, shape, and structure via hydrothermal synthesis10.1021/cm000607e ↗
35. Assessing the corrosion of biodegradable magnesium implant: a critical review of current methodologies and their limitations10.1016/j.actbio.2011.11.014 ↗
36. Enhanced antimicrobial properties, cytocompatibility, and corrosion resistance of plasma-modified biodegradable magnesium alloys10.1016/j.actbio.2013.10.012 ↗
37. Accurate electrochemical measurement of magnesium corrosion rates; a combined impedance, mass-loss and hydrogen collection study10.1016/j.electacta.2013.12.124 ↗
38. Corrosion-controlling and osteo-compatible Mg ion-integrated phytic acid (Mg-PA) coating on magnesium substrate for biodegradable implants application10.1021/am506741d ↗
39. Recent progress in corrosion and protection of magnesium alloys10.1002/adem.200500013 ↗
40. A electro-deposition process for fabrication of biomimetic super-hydrophobic surface and its corrosion resistance on magnesium alloy10.1016/j.electacta.2014.01.135 ↗