Hot corrosion behaviour of yttrium and aluminium modified wear resistance coating alloy in mixed sulphate at 900 °C
Source abstract
Abstract
Abstract The wear resistance coating alloy Tribaloy T-900 modified by aluminium and yttrium was prepared by mechanical alloying. The hot corrosion behaviour of modified and unmodified alloys was investigated at 900 °C. Results revealed that T-900AlY with aluminium plus yttrium showed the superior hot corrosion resistance. The Yttrium addition promoted the selective oxidation of Al and Cr and accelerated a continuous oxide layer of Al2O3 and Cr2O3. The oxides layer acted as a barrier against the molten salt attack. The early formation of chromia and alumina layer obstructed the formation of outer NiO and MoO3, which were more susceptible to the liquid salt attack.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Metal and Thin Film Mechanics · High Entropy Alloys Studies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (52)
Show source-provided references
1. Manufacturing and mechanical evaluation of cooled cooling air (CCA) heat exchanger for aero engine10.1007/s12541-016-0143-4 ↗
2. Microstructure and sliding wear behaviour of Tribaloy T-800 coatings deposited by laser cladding10.1016/j.wear.2005.04.020 ↗
3. Microstructure and properties of tribaloy T-800 coatings deposited by laser cladding10.3989/cyv.2004.v43.i2.530 ↗
4. Influence of the F.C.C. phase retained at room temperature on the mechanical properties of cobalt10.1016/0036-9748(78)90078-9 ↗
5. Heat treatment effects on the tribological performance of HVOF sprayed Co-Mo-Cr-Si coatings10.1361/105996306X146721 ↗
6. Characteristics of Tribaloy T-800 and T-900 coatings on steel substrates by laser cladding10.1016/j.surfcoat.2007.11.025 ↗
7. Hot corrosion of metals and alloys10.1007/s11085-011-9254-6 ↗
8. Hot corrosion in gas turbine components10.1016/S1350-6307(00)00035-2 ↗
9. Vapour aluminide coating of internal cooling channels in turbine blades and vanes
10. Microstructure and hot corrosion behavior of Co–Si modified aluminide coating on nickel based superalloys10.1016/j.corsci.2015.08.011 ↗
11. Hot corrosion behavior of Co modified NiAl coating on nickel base superalloys10.1016/j.corsci.2012.06.027 ↗
12. Preparation and corrosion resistance of ZnO/CeO2 composite films10.1179/1743294414Y.0000000337 ↗
13. Microstructure and hot corrosion behaviors of two Co modified aluminide coatings on a Ni-based superalloy at 700°C10.1016/j.apsusc.2014.05.043 ↗
14. Effect of Ce and La additions in low temperature aluminization process by CVD–FBR on 12%Cr ferritic/martensitic steel and behaviour in steam oxidation10.1016/j.corsci.2008.05.008 ↗
15. The reactive element effect in high-temperature corrosion10.1016/0921-5093(89)90730-2 ↗
16. Effect of trivalent rare earth dopants in nanocrystalline ceria coatings for high-temperature oxidation resistance10.1016/j.actamat.2007.01.043 ↗
17. The development of Cr2O3 scales on iron-chromium alloys containing reactive elements10.1016/0010-938X(89)90057-7 ↗
18. Effect of Cr and Y2O3 on the oxidation behavior of Co-based oxide dispersion strengthened superalloys at 900°C10.1016/j.corsci.2017.08.013 ↗
19. Role of y in the oxidation resistance of CrAlYN coatings10.1016/j.apsusc.2015.06.099 ↗
20. Adherence of oxide scale formed on Ni 20Cr 1Si alloys with small additions of rare earth elements10.1016/0025-5416(87)90389-2 ↗
21. Lou · Oxid. Met. · 1992 · 38 · 29910.1007/BF00666917 ↗
22. Reactive element-sulfur interaction and oxide scale adherence10.1007/BF02811687 ↗
23. First principles assessment of metal/oxide interface adhesion10.1063/1.2907339 ↗
24. Effect of sulfur removal on Al2O3 scale adhesion10.1007/BF02670297 ↗
25. Segregation phenomena at thermally grown Al2O3/alloy interfaces10.1146/annurev.matsci.38.060407.130323 ↗
26. The effect of reactive element additions on the selective oxidation, growth and adhesion of chromia scales10.1016/0921-5093(95)09798-8 ↗
27. The formation of aluminum oxide scales on high-temperature alloys10.1007/BF00666913 ↗
28. Thermal properties of MoSi2 with minor aluminum substitutions10.1016/j.intermet.2006.03.013 ↗
29. Effect of Al additions on the oxidation behavior of Laves phase NbCr2 alloys at 1373K and 1473K10.1016/j.ijrmhm.2008.09.007 ↗
30. Effect of Y2O3 content in the pack on microstructure and hot corrosion resistance of Y–Co-modified aluminide coating10.1016/j.corsci.2014.05.018 ↗
31. Effect of rare earth cerium on the microstructure and corrosion resistance of laser cladded nickel-base alloy coatings10.1016/S0924-0136(96)02684-2 ↗
32. Hot corrosion behavior of a Cr-Modified aluminide coating on a Ni-based superalloy10.1007/s40195-014-0108-5 ↗
33. Comparative cyclic oxidation behaviour and effect of oxides on hardness of wear resistance coating alloys T-401 and T-90010.1007/s42243-019-00258-2 ↗
34. Preparation and hot corrosion behaviour of two Co modified NiAl coatings on a Ni-based superalloy10.1016/j.corsci.2013.07.008 ↗
35. On the hot corrosion of nickel at 700 °C10.1007/s11085-015-9588-6 ↗
36. Lingfengdong - the first lower Paleolithic site found in Fujiang Province
37. Improved Cr2O3 adhesion by Ce ion implantation in the presence of interfacial sulfur segregation10.1016/j.actamat.2006.07.047 ↗
38. Improvement of the oxidation resistance of Tribaloy T-800 alloy by the additions of yttrium and aluminium10.1016/j.corsci.2010.11.038 ↗
39. Hot Corrosion of a single crystal Ni-base superalloy by Na-salts at 900°C10.1007/s11085-006-9004-3 ↗
40. Studies on the hot corrosion of a nickel-base superalloy, Udimet 70010.1007/BF00655894 ↗
41. Chemical reactions involved in the initiation of hot Corrosion of B‐1900 and NASA‐TRW VIA10.1149/1.2123928 ↗
42. Mechanism of Na2 SO 4 – induced corrosion of molybdenum containing nickel‐base superalloys at high temperatures: I. Corrosion in atmospheres containing only10.1149/1.2108700 ↗
43. Hou · Mater. Sci. Eng., A · 1995 · 202 · 110.1016/0921-5093(95)09798-8 ↗
44. On the formation of interfacial and internal voids inα-Al2O3 scales10.1007/BF01670505 ↗
45. Pint · Oxid. Met. · 1997 · 48 · 30310.1007/BF01670505 ↗
46. The influence of alloying elements on the development and maintenance of protective scales10.1007/BF01046725 ↗
47. Na2SO4-induced accelerated oxidation (hot corrosion) of nickel10.1007/BF02642794 ↗
48. Whitney award lecture—1986: chemistry and electrochemistry of the hot corrosion of metals10.5006/1.3583026 ↗
49. Influence of Cr content on hot corrosion and a special tube sealing test of single crystal nickel base superalloy10.1016/j.corsci.2019.05.001 ↗
50. The solubility of SiO2 in fused Na2 SO 4 at 900°C10.1149/1.2108692 ↗
51. Hot corrosion of materials: a fluxing mechanism?10.1016/S0010-938X(01)00057-9 ↗
52. The role of silicon in corrosion-resistant high temperature coatings10.1016/0040-6090(82)90578-8 ↗