Effect of Au-ions irradiation on mechanical and LBE corrosion properties of amorphous AlCrFeMoTi HEA coating: Enhanced or deteriorated?
Source abstract
Abstract
Abstract The effect of Au-ions irradiation with different damage doses from 10 to 90 dpa on mechanical properties and LBE corrosion behavior of AlCrFeMoTi HEA coating was investigated. The fracture toughness and the interface bonding strength had been improved after irradiation. The Au-ions irradiation decelerated LBE corrosion rate of coating at low damage dose, which could be attributed to the formation of a more continuous Cr2O3 layer adjacent to the coating surface. However, the element diffusion was intensified and the Cr2O3 layer became more thick and porous at high damage dose, which resulted in the acceleration of LBE corrosion.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Metal and Thin Film Mechanics · Fusion materials and technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (76)
Show source-provided references
1. Generation IV international forum: a decade of progress through international cooperation10.1016/j.pnucene.2014.02.010 ↗
2. Conceptual aspects of melting unit vessel cooling by heavy liquid metal coolant10.1016/j.nucet.2016.07.012 ↗
3. Properties of liquid metal coolants10.1016/B978-0-08-056033-5.00130-0 ↗
4. Fonzo, corrosion and radiation resistant nanoceramic coatings for lead fast reactors10.1016/j.corsci.2017.05.011 ↗
5. Materials challenges in nuclear energy10.1016/j.actamat.2012.11.004 ↗
6. Corrosion of stainless steels in lead–bismuth eutectic up to 600 °C10.1016/j.jnucmat.2004.07.012 ↗
7. Material performance in lead and lead-bismuth alloy10.1016/B978-0-08-056033-5.00096-3 ↗
8. Review of the studies on fundamental issues in LBE corrosion10.1016/j.jnucmat.2007.06.019 ↗
9. A review of steel corrosion by liquid lead and lead–bismuth10.1016/j.corsci.2009.03.013 ↗
10. Oxidation of steels in liquid lead bismuth: oxygen control to achieve efficient corrosion protection10.1016/j.nucengdes.2010.07.039 ↗
11. Oxygen for protective oxide scale formation on pins and structural material surfaces in lead-alloy cooled reactors10.1016/j.nucengdes.2014.03.043 ↗
12. Liquid metal corrosion of T91 and A316L materials in Pb–Bi eutectic at temperatures 400–600°C10.1016/j.corsci.2005.04.001 ↗
13. Oxide layer stability in lead–bismuth at high temperature10.1016/j.jnucmat.2004.07.017 ↗
14. Compatibility of surface-coated steels, refractory metals and ceramics to high temperature lead–bismuth eutectic10.1016/j.pnucene.2007.11.081 ↗
15. Oxidation mechanism of refractory Molybdenum exposed to oxygen-saturated lead-bismuth eutectic at 600 °C10.1016/j.corsci.2020.109132 ↗
16. Exposure of pre-stressed T91 coated with TiN, CrN and DLC to Pb–55.5Bi10.1016/j.jnucmat.2006.05.038 ↗
17. Lead-bismuth eutectic (LBE) corrosion mechanism of nano-amorphous composite TiSiN coatings synthesized by cathodic arc ion plating10.1016/j.corsci.2021.109264 ↗
18. Lead-bismuth eutectic (LBE) corrosion behavior of AlTiN coatings at 550 and 600゜C10.1016/j.jnucmat.2020.152280 ↗
19. Preliminary study on nano- and micro-composite sol–gel based alumina coatings on structural components of lead–bismuth eutectic cooled fast breeder reactors10.1016/j.jnucmat.2010.11.022 ↗
20. Long-term corrosion tests of Ti 3 SiC 2 and Ti 2 AlC in oxygen containing LBE at temperatures up to 700 °C10.1016/j.jnucmat.2016.10.007 ↗
21. Corrosion resistance of alloys F91 and Fe–12Cr–2Si in lead–bismuth eutectic up to 715°C10.1016/j.jnucmat.2012.11.010 ↗
22. Oxide scale formation of modified FeCrAl coatings exposed to liquid lead10.1016/j.corsci.2011.10.019 ↗
23. Surface modification/alloying using intense pulsed electron beam as a tool for improving the corrosion resistance of steels exposed to heavy liquid metals10.1016/j.jnucmat.2011.04.030 ↗
24. Enhancing radiation tolerance by controlling defect mobility and migration pathways in multicomponent single-phase alloys10.1038/ncomms13564 ↗
25. Microstructural stability and mechanical behavior of FeNiMnCr high entropy alloy under ion irradiation10.1016/j.actamat.2016.05.007 ↗
26. Enhanced damage resistance and novel defect structure of CrFeCoNi under in situ electron irradiation10.1016/j.scriptamat.2016.07.023 ↗
27. Microstructure and properties of coating of FeAlCuCrCoMn high entropy alloy deposited by direct current magnetron sputtering10.1590/1980-5373-MR-2015-0536 ↗
28. A review on fundamental of high entropy alloys with promising high–temperature properties10.1016/j.jallcom.2018.05.067 ↗
29. Microstructures and properties of high-entropy alloy films and coatings: a review10.1080/21663831.2018.1434248 ↗
30. Thermally stable laser cladded CoCrCuFeNi high-entropy alloy coating with low stacking fault energy10.1016/j.jallcom.2014.02.121 ↗
31. Novel corrosion behaviours of the annealing and cryogenic thermal cycling treated Ti-based metallic glasses10.1016/j.intermet.2019.04.010 ↗
32. FeCrMoWCBY metallic glass with high corrosion resistance in molten lead–bismuth eutectic alloy10.1016/j.corsci.2021.109688 ↗
33. Effect of annealing on microstructure evolution and corrosion resistance of an amorphous Cr-Al-C coating10.1016/j.corsci.2020.109062 ↗
34. A novel AlCrFeMoTi high-entropy alloy coating with a high corrosion-resistance in lead-bismuth eutectic alloy10.1016/j.corsci.2021.109524 ↗
35. Early corrosion behaviour of irradiated FeCrAl alloy in a simulated pressurized water reactor environment10.1016/j.corsci.2020.108824 ↗
36. Degradation of HT9 under simultaneous ion beam irradiation and liquid metal corrosion10.1016/j.jnucmat.2016.06.039 ↗
37. The effects of neutron and ionizing irradiation on the aqueous corrosion of SiC10.1016/j.jnucmat.2020.152190 ↗
38. Role of radiation-induced grain boundary segregation in irradiation assisted stress corrosion cracking10.1080/18811248.2004.9715522 ↗
39. Microstructural evolution and hardening effect of 12Cr2W2Mn ferritic/martensitic steel under Au-ions irradiation10.1016/j.jallcom.2020.155360 ↗
40. Irradiation accelerated fluoride molten salt corrosion of nickel-based UNS N10003 alloy revealed by X-ray absorption fine structure10.1016/j.corsci.2019.108408 ↗
41. Role of helium ion irradiation in the corrosion of CVD−SiC in molten LiF−NaF−KF salt10.1016/j.corsci.2021.109287 ↗
42. Proton irradiation assisted localized corrosion and stress corrosion cracking in 304 nuclear grade stainless steel in simulated primary PWR water10.1016/j.jmst.2020.04.068 ↗
43. Corrosion behavior of ion-irradiated 12Cr2W2Mn F/M steel in liquid LBE
44. HLMIF, a facility for investigating the synergistic effect of ion-irradiation and LBE corrosion10.1016/j.jnucmat.2019.05.049 ↗
45. The design, setup and operational testing of the irradiation and corrosion experiment (ICE)10.1016/j.jnucmat.2008.02.021 ↗
46. Materials for future nuclear energy systems10.1016/j.jnucmat.2019.151837 ↗
47. An ion beam facility based on a 3 MV tandetron accelerator in Sichuan University, China10.1016/j.nimb.2018.01.002 ↗
48. The effects of cold working on the corrosion behavior of an austenitic stainless steel in liquid lead-bismuth eutectic under vacuum at 873 K10.1016/j.jnucmat.2018.07.034 ↗
49. Corrosion behavior of 410 stainless steel in flowing lead-bismuth eutectic alloy at 550 °C10.1016/j.jnucmat.2019.05.029 ↗
50. Characterization of corrosion phenomena and kinetics on T91 ferritic/martensitic steel exposed at 450 and 550 °C to flowing Pb-Bi eutectic with 10−7 mass% dissolved oxygen10.1016/j.jnucmat.2017.07.031 ↗
51. Effect of Au-ion irradiation on the surface morphology, microstructure and mechanical properties of amorphous AlCrFeMoTi HEA coating10.1016/j.surfcoat.2021.127252 ↗
52. Microstructural characterization, mechanical property and corrosion behavior of VNbMoTaWAl refractory high entropy alloy coatings: effect of Al content10.1016/j.surfcoat.2020.126351 ↗
53. Structural characterization of the Ta-rich part of the Ta–Al system10.1016/j.jssc.2006.07.001 ↗
54. Liquid metal embrittlement of a dual-phase Al0.7CoCrFeNi high-entropy alloy exposed to oxygen-saturated lead-bismuth eutectic10.1016/j.scriptamat.2020.113652 ↗
55. Aloe polysaccharides ameliorate acute colitis in mice via Nrf2/HO-1 signaling pathway and short-chain fatty acids metabolism10.1016/j.ijbiomac.2021.07.007 ↗
56. Influence of irradiation on the oxide film formed on 316 L stainless steel in PWR primary water10.1007/s11085-013-9401-3 ↗
57. Effect of irradiation on corrosion of 304 nuclear grade stainless steel in simulated PWR primary water10.1016/j.corsci.2017.08.010 ↗
58. Radiation endurance in Al2O3 nanoceramics10.1038/srep33478 ↗
59. Roles of ion irradiation and thermal annealing in inducing crystallization in metallic glass10.1016/j.intermet.2019.106608 ↗
60. Effects of annealing on the hardness and elastic modulus of a Cu36Zr48Al8Ag8 bulk metallic glass10.1016/j.matdes.2012.12.071 ↗
61. Hardening behaviour in the irradiated high entropy alloy10.1016/j.mechmat.2021.103744 ↗
62. Investigation of the relationship between elastic modulus and hardness based on depth-sensing indentation measurements10.1016/j.actamat.2004.08.002 ↗
63. On the significance of the H/E ratio in wear control: a nanocomposite coating approach to optimised tribological behaviour10.1016/S0043-1648(00)00488-9 ↗
64. Fabrication of AlTiN coatings deposited on the ultrasonic rolling textured substrates for improving coatings adhesion strength10.1016/j.apsusc.2021.149394 ↗
65. Corrosion behavior of stainless steels in simulated PWR primary water—effect of chromium content in alloys and dissolved hydrogen—10.1080/18811248.2008.9711883 ↗
66. Oxide growth and dissolution on 316L stainless steel during irradiation in high temperature water10.1016/j.corsci.2019.06.006 ↗
67. The role of diffusion in the oxidation of mild steel in high temperature aqueous solutions10.1016/S0010-938X(66)80001-X ↗
68. Accelerated corrosion and oxide dissolution in 316L stainless steel irradiated in situ in high temperature water10.1016/j.jnucmat.2017.05.043 ↗
69. Oxidation kinetics and mechanisms of Ni-base alloys in pressurised water reactor primary conditions: influence of subsurface defects10.1016/j.corsci.2011.07.024 ↗
70. Characterization of the oxide films formed at the surface of Ni-Base alloys in pressurized water reactors primary coolant by transmission electron microscopy10.4028/www.scientific.net/MSF.595-598.539 ↗
71. Thermochemical data of pure substances
72. High temperature oxidation behavior of Al0.6CrFeCoNi and Al0.6CrFeCoNiSi0.3 high entropy alloys10.1016/j.jallcom.2018.06.036 ↗
73. Sluggish diffusion in Co–Cr–Fe–Mn–Ni high-entropy alloys10.1016/j.actamat.2013.04.058 ↗
74. Proton irradiation-decelerated intergranular corrosion of Ni-Cr alloys in molten salt10.1038/s41467-020-17244-y ↗
75. Simulation of neutron-induced damage in tungsten by irradiation with energetic self-ions10.1016/j.jnucmat.2015.02.004 ↗
76. Emulation of reactor irradiation damage using ion beams10.1016/j.scriptamat.2014.06.003 ↗