Coaxial Nanorods of MgO Core with Si Shell Layers
Source abstract
Abstract
This article demonstrates an approach to the synthesis of MgO/Si core-shell nanorods. The Si shell was close to amorphous, whereas the MgO core was crystalline with a cubic structure. The PL of the Si-coated products under excitation at 325 nm exhibited a visible light emission, which was almost identical to that of the uncoated ones.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: ZnO doping and properties · Ga2O3 and related materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (46)
Show source-provided references
1. Wu Y. · Chem. Eur. J. · 2002 · 8 · 1261
2. 10.1126/science.281.5379.97310.1126/science.281.5379.973 ↗
3. Yu Y. · Nature · 2004 · 450 · 61
4. 10.1038/nature0114110.1038/nature01141 ↗
5. 10.1021/jp034734k10.1021/jp034734k ↗
6. 10.1126/science.281.5379.97310.1126/science.281.5379.973 ↗
7. 10.1021/nl049467o10.1021/nl049467o ↗
8. 10.1038/nature0114110.1038/nature01141 ↗
9. 10.1016/S0022-0248(03)00967-910.1016/S0022-0248(03)00967-9 ↗
10. 10.1021/ja035787i10.1021/ja035787i ↗
11. 10.1038/nature0114110.1038/nature01141 ↗
12. 10.1063/1.160965310.1063/1.1609653 ↗
13. 10.1063/1.12687110.1063/1.126871 ↗
14. 10.1021/jp034184q10.1021/jp034184q ↗
15. 10.1021/nl015613410.1021/nl0156134 ↗
16. 10.1021/nl02550810.1021/nl025508 ↗
17. 10.1063/1.163201710.1063/1.1632017 ↗
18. 10.1002/adma.20030520910.1002/adma.200305209 ↗
19. 10.1007/s00339-003-2427-710.1007/s00339-003-2427-7 ↗
20. 10.1557/JMR.1998.035310.1557/JMR.1998.0353 ↗
21. 10.1002/1521-4095(20020805)14:15<1046::AID-ADMA1046>3.0.CO;2-H10.1002/1521-4095(20020805)14:15<1046::AID-ADMA1046>3.0.CO;2-H ↗
22. 10.1021/jp046501e10.1021/jp046501e ↗
23. 10.1021/nl034012510.1021/nl0340125 ↗
24. 10.1002/1521-4095(20021104)14:21<1560::AID-ADMA1560>3.0.CO;2-P10.1002/1521-4095(20021104)14:21<1560::AID-ADMA1560>3.0.CO;2-P ↗
25. 10.1021/cm03417310.1021/cm034173 ↗
26. 10.1063/1.162625910.1063/1.1626259 ↗
27. 10.1021/nl034950510.1021/nl0349505 ↗
28. 10.1002/smll.20050016910.1002/smll.200500169 ↗
29. 10.1103/PhysRevB.27.128310.1103/PhysRevB.27.1283 ↗
30. 10.1103/PhysRevB.39.1030910.1103/PhysRevB.39.10309 ↗
31. 10.1063/1.45610510.1063/1.456105 ↗
32. 10.1126/science.279.5348.20810.1126/science.279.5348.208 ↗
33. 10.1126/science.271.5251.93310.1126/science.271.5251.933 ↗
34. 10.1016/S0022-0248(01)01360-410.1016/S0022-0248(01)01360-4 ↗
35. 10.1021/jp034184q10.1021/jp034184q ↗
36. 10.1038/nature0114110.1038/nature01141 ↗
37. 10.1016/j.carbon.2006.01.02810.1016/j.carbon.2006.01.028 ↗
38. 10.1016/S0169-4332(01)00877-710.1016/S0169-4332(01)00877-7 ↗
39. 10.1016/j.tsf.2005.11.11410.1016/j.tsf.2005.11.114 ↗
40. 10.1002/1616-3028(20020418)12:4<293::AID-ADFM293>3.0.CO;2-U10.1002/1616-3028(20020418)12:4<293::AID-ADFM293>3.0.CO;2-U ↗
41. 10.1021/jp050545l10.1021/jp050545l ↗
42. 10.1016/j.cplett.2005.10.05210.1016/j.cplett.2005.10.052 ↗
43. 10.1016/j.materresbull.2005.01.01310.1016/j.materresbull.2005.01.013 ↗
44. 10.1016/S0009-2614(02)01229-010.1016/S0009-2614(02)01229-0 ↗
45. 10.1103/PhysRevB.39.1030910.1103/PhysRevB.39.10309 ↗
46. 10.1002/pssa.20052003110.1002/pssa.200520031 ↗