Influence of the Loading Rate on the Cyclic Deformation Behaviour and the Damage Accumulation of Cortical Bone Specimens Under Three‐Point Bending
Source abstract
Abstract
Fatigue failure of cortical bone may be observed in vivo after severe cyclic loading. In vitro hysteresis measurements are strongly influenced by time-dependent deformation and microcrack formation. Load increase tests with recovery cycles and/or adapted loading velocity together with microstructural investigations offer a good possibility to discriminate between the influence of loading velocity and microstructural damage on the hysteresis parameters.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Elasticity and Material Modeling · High-Velocity Impact and Material Behavior
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (40)
Show source-provided references
1. Knauf M. · Akt. Traumatol. · 1990 · 20 · 243
2. 10.1097/00003086-197105000-0001610.1097/00003086-197105000-00016 ↗
3. 10.1002/jor.110008041710.1002/jor.1100080417 ↗
4. 10.1111/j.1740-8261.1987.tb01719.x10.1111/j.1740-8261.1987.tb01719.x ↗
5. 10.1016/0268-0033(96)00010-110.1016/0268-0033(96)00010-1 ↗
6. 10.1006/jtbi.2001.231610.1006/jtbi.2001.2316 ↗
7. Freeman M. A. R. · J. Bone Jt. Surg. Br. · 1974 · 56 · 69810.1302/0301-620X.56B4.698 ↗
8. 10.1302/0301-620X.79B2.746110.1302/0301-620X.79B2.7461 ↗
9. Frost H. M. · Henry Ford Hosp. Med. Bull. · 1960 · 8 · 27
10. D. Taylor Proc. 6thInt. Fatigue Cong. Fatigue '96 6–10 May 1996 Berlin Lütjering G. Nowack H. (Eds.) Pergamon 1996 Vol. III 1811 – 1816.
11. 10.1016/S0021-9290(96)00113-310.1016/S0021-9290(96)00113-3 ↗
12. J. D Currey Princeton Univ. Press Princeton New Jersey USA2002
13. J. Wolff Das Gesetz der Transformation der Knochen.A. Hirschwald Berlin Germany 1892.10.1055/s-0028-1144106 ↗
14. C. Fleck Struktur und mechanische Eigenschaften kortikalen Knochens unter quasi‐statischer und zyklischer Beanspruchung PhD thesis Institute of Materials Science University of Kaiserslautern Germany1996.
15. Turner A. S. · Am. J. Vet. Res. · 1975 · 36 · 157310.2460/ajvr.1975.36.11.1573 ↗
16. Schamhardt H. C. · Res. Vet. Sci. · 1985 · 39 · 13910.1016/S0034-5288(18)31736-3 ↗
17. Rubin C. T. · J. Exp. Biol. · 1982 · 101 · 18710.1242/jeb.101.1.187 ↗
18. 10.3109/1745367750898921610.3109/17453677508989216 ↗
19. 10.1152/jappl.1957.10.1.12710.1152/jappl.1957.10.1.127 ↗
20. King A. I. · Digest of the 7th Int. Conf. on Med. and Biol. Eng., Stockholm · 1967 · 514
21. 10.1016/0021-9290(74)90020-710.1016/0021-9290(74)90020-7 ↗
22. 10.1016/0021-9290(76)90136-610.1016/0021-9290(76)90136-6 ↗
23. 10.1115/1.342623110.1115/1.3426231 ↗
24. Nunamaker D. M. · Am. J. Vet. Res. · 1991 · 52 · 9710.2460/ajvr.1991.52.01.97 ↗
25. 10.1016/0021-9290(81)90096-810.1016/0021-9290(81)90096-8 ↗
26. 10.1016/0021-9290(77)90005-710.1016/0021-9290(77)90005-7 ↗
27. 10.1115/1.313840110.1115/1.3138401 ↗
28. C. A. G. Pattin Cyclic Mech. Property Degradation in Bone During Fatigue Loading PhD thesis Stanford University USA 1990.
29. 10.1016/S0021-9290(02)00364-010.1016/S0021-9290(02)00364-0 ↗
30. 10.1115/1.193391610.1115/1.1933916 ↗
31. 10.1016/0021-9290(89)90013-410.1016/0021-9290(89)90013-4 ↗
32. D. Taylor Comprehensive Struct. Integrity: Fracture of Mater. from Nano to Macro vol. 9 Elsevier Inc. Oxford UK2003 35–96.10.1016/B0-08-043749-4/09012-1 ↗
33. 10.1002/jor.110003011010.1002/jor.1100030110 ↗
34. 10.1016/j.biomaterials.2004.05.02410.1016/j.biomaterials.2004.05.024 ↗
35. 10.1016/j.jbiomech.2004.07.01010.1016/j.jbiomech.2004.07.010 ↗
36. 10.1111/j.1460-2695.2005.00878.x10.1111/j.1460-2695.2005.00878.x ↗
37. Harig H. · HTM · 1986 · 41 · 28610.1515/htm-1986-410512 ↗
38. 10.1002/mawe.1995026030510.1002/mawe.19950260305 ↗
39. K. Marchetti Untersuchungen zum Ermüdungsverhalten stranggepreßter kurzfaserverstärkter Glasverbundkörper mit Hilfe von Spannung‐Dehnung‐Hysteresismessungen PhD thesis Institute of Materials Science University of Kaiserslautern Germany1997.
40. 10.1007/BF0035142010.1007/BF00351420 ↗