Sol–Gel Derived Fe‐Rich Matrix Composites Having Precipitated WC
Source abstract
Abstract
SEM image of a sol–gel derived composite presenting WC grains (grey phase) embedded in a Fe binder matrix (dark phase). The crystalline composites are prepared from amorphous sol–gel masses containing W, Fe alkoxides and extra carbon. WC and Fe precipitate in-situ out of the WCFeO masses during a two steps heating process under a flux of H2/Ar up to 600–800 °C and then under vacuum up to 1250 °C.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Advanced materials and composites · Powder Metallurgy Techniques and Materials · Advanced ceramic materials synthesis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Centro Atómico Bariloche – CNEA Av. E. Bustillo 9500 RA‐8400 Bariloche Argentine
AB Sandvik Coromant R&D SE‐12680 Stockholm Sweden
Departamento Metalurgia Centro DEYTEMA Facultad Regional San Nicolás Universidad Tecnológica Nacional Colón 332 B2900LWH San Nicolás Argentine
CONICET, Avenida Rivadavia 1917 RA‐1033 Buenos Aires Argentine
References (34)
Show source-provided references
1. 10.1016/j.ijrmhm.2008.07.01110.1016/j.ijrmhm.2008.07.011 ↗
2. 10.1016/S0921-5093(01)01214-X10.1016/S0921-5093(01)01214-X ↗
3. 10.1016/S0955-2219(00)00038-810.1016/S0955-2219(00)00038-8 ↗
4. 10.1016/0040-6031(79)87099-910.1016/0040-6031(79)87099-9 ↗
5. 10.1016/j.ceramint.2010.09.03610.1016/j.ceramint.2010.09.036 ↗
6. 10.1007/s00604017007210.1007/s006040170072 ↗
7. Sahay S. K. · J. Metall. Mater. Sci. · 2007 · 49 · 143
8. 10.1016/j.ijrmhm.2008.12.00910.1016/j.ijrmhm.2008.12.009 ↗
9. 10.1111/j.1151-2916.1977.tb15543.x10.1111/j.1151-2916.1977.tb15543.x ↗
10. 10.1016/1359-8368(96)00004-210.1016/1359-8368(96)00004-2 ↗
11. 10.1016/j.ceramint.2005.09.01010.1016/j.ceramint.2005.09.010 ↗
12. 10.1016/0025-5416(88)90503-410.1016/0025-5416(88)90503-4 ↗
13. 10.1016/S0263-4368(01)00070-110.1016/S0263-4368(01)00070-1 ↗
14. Prakash L. · 1993 · p. 110
15. 10.1016/j.ijrmhm.2010.12.00710.1016/j.ijrmhm.2010.12.007 ↗
16. 10.1016/j.mspro.2012.06.01310.1016/j.mspro.2012.06.013 ↗
17. 10.1016/j.ultramic.2010.12.02410.1016/j.ultramic.2010.12.024 ↗
18. 10.1016/j.ijrmhm.2011.02.00410.1016/j.ijrmhm.2011.02.004 ↗
19. 10.1007/BF0283368410.1007/BF02833684 ↗
20. 10.1016/S1044-5803(02)00181-X10.1016/S1044-5803(02)00181-X ↗
21. 10.1023/A:100676612760310.1023/A:1006766127603 ↗
22. 10.1016/j.ijrmhm.2007.04.00610.1016/j.ijrmhm.2007.04.006 ↗
23. 10.1016/S1468-6996(00)00006-110.1016/S1468-6996(00)00006-1 ↗
24. 10.1016/S0965-9773(97)00054-810.1016/S0965-9773(97)00054-8 ↗
25. 10.1088/0957-4484/14/9/30310.1088/0957-4484/14/9/303 ↗
26. 10.1021/ie040247v10.1021/ie040247v ↗
27. 10.1016/0022-4596(76)90157-210.1016/0022-4596(76)90157-2 ↗
28. 10.1016/0022-3093(82)90251-410.1016/0022-3093(82)90251-4 ↗
29. 10.1016/0022-3093(86)90139-010.1016/0022-3093(86)90139-0 ↗
30. 10.1016/0022-3093(88)90031-210.1016/0022-3093(88)90031-2 ↗
31. 10.1016/S0254-0584(99)00128-510.1016/S0254-0584(99)00128-5 ↗
32. 10.1016/S0921-5093(00)00773-510.1016/S0921-5093(00)00773-5 ↗
33. 10.1016/S0254-0584(02)00217-110.1016/S0254-0584(02)00217-1 ↗
34. 10.1007/s10853-005-2815-910.1007/s10853-005-2815-9 ↗