Dramatic Increase of Strength and Ductility in Fe–22Mn–1.0C Twinning‐Induced Plasticity Steel at Elevated Temperature
Source abstract
Abstract
Tensile properties and microstructural evolutions of Fe–22Mn–1.0C (wt%) twinning‐induced plasticity steel are investigated in the temperature range from 293 to 443 K. An unexpected enhancement of strength and ductility is observed at the elevated temperature of 443 K (≈400 MPa ultimate tensile strength and ≈10% true strain improvements). The twinning capability is still kept stable with the increasing temperature, and the premature fracture is postponed by suppressing dynamic strain aging effect. As a result, the synchronous improvement of strength and plasticity is achieved at high deformation temperature.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Microstructure and Mechanical Properties of Steels · Microstructure and mechanical properties · Metal Alloys Wear and Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Materials Fatigue and Fracture Division Shenyang National Laboratory for Materials Science Institute of Metal Research Chinese Academy of Sciences 72 Wenhua Road Shenyang 110016 P. R. China
Funding
National Natural Science Foundation of China
References (51)
Show source-provided references
1. 10.1126/science.118586610.1126/science.1185866 ↗
2. 10.1038/nature0113310.1038/nature01133 ↗
3. 10.1016/j.pmatsci.2006.02.00310.1016/j.pmatsci.2006.02.003 ↗
4. 10.1016/S0079-6425(99)00007-910.1016/S0079-6425(99)00007-9 ↗
5. 10.1126/science.116764110.1126/science.1167641 ↗
6. 10.1007/BF0339898610.1007/BF03398986 ↗
7. 10.1007/s11661-001-0109-710.1007/s11661-001-0109-7 ↗
8. 10.1080/1478643620821217110.1080/14786436208212171 ↗
9. 10.1016/j.actamat.2011.11.00910.1016/j.actamat.2011.11.009 ↗
10. 10.1016/S1359-6454(03)00117-410.1016/S1359-6454(03)00117-4 ↗
11. 10.1016/S0921-5093(00)02019-010.1016/S0921-5093(00)02019-0 ↗
12. 10.1016/j.actamat.2011.07.00910.1016/j.actamat.2011.07.009 ↗
13. 10.1016/j.msea.2018.02.00310.1016/j.msea.2018.02.003 ↗
14. 10.1016/j.msea.2009.04.06710.1016/j.msea.2009.04.067 ↗
15. 10.1016/j.actamat.2017.06.04210.1016/j.actamat.2017.06.042 ↗
16. 10.1016/j.scriptamat.2017.07.01710.1016/j.scriptamat.2017.07.017 ↗
17. 10.1016/j.cossms.2011.04.00210.1016/j.cossms.2011.04.002 ↗
18. 10.1016/j.ijplas.2018.02.00110.1016/j.ijplas.2018.02.001 ↗
19. 10.2355/isijinternational.47.180410.2355/isijinternational.47.1804 ↗
20. 10.1016/j.msea.2010.01.03710.1016/j.msea.2010.01.037 ↗
21. 10.1016/j.actamat.2017.04.01110.1016/j.actamat.2017.04.011 ↗
22. 10.1016/j.actamat.2011.12.00410.1016/j.actamat.2011.12.004 ↗
23. 10.1016/j.actamat.2013.02.03110.1016/j.actamat.2013.02.031 ↗
24. 10.1016/j.actamat.2017.11.02310.1016/j.actamat.2017.11.023 ↗
25. 10.1016/j.actamat.2013.07.03610.1016/j.actamat.2013.07.036 ↗
26. 10.1016/j.msea.2018.01.01910.1016/j.msea.2018.01.019 ↗
27. De Cooman B. C. · 2011
28. 10.1016/j.actamat.2011.07.04010.1016/j.actamat.2011.07.040 ↗
29. 10.1016/j.actamat.2013.07.04210.1016/j.actamat.2013.07.042 ↗
30. 10.1016/j.scriptamat.2013.02.06010.1016/j.scriptamat.2013.02.060 ↗
31. 10.1016/j.msea.2009.08.04810.1016/j.msea.2009.08.048 ↗
32. 10.1017/CBO978051181094710.1017/CBO9780511810947 ↗
33. 10.1080/1478643720822102910.1080/14786437208221029 ↗
34. 10.1016/j.scriptamat.2009.06.01810.1016/j.scriptamat.2009.06.018 ↗
35. 10.1016/j.msea.2010.02.04110.1016/j.msea.2010.02.041 ↗
36. 10.1016/j.calphad.2010.02.00110.1016/j.calphad.2010.02.001 ↗
37. 10.1016/j.msea.2004.01.05910.1016/j.msea.2004.01.059 ↗
38. 10.1007/s11661-009-0050-810.1007/s11661-009-0050-8 ↗
39. 10.2355/isijinternational.ISIJINT-2015-07010.2355/isijinternational.ISIJINT-2015-070 ↗
40. 10.2355/isijinternational.ISIJINT-2015-06910.2355/isijinternational.ISIJINT-2015-069 ↗
41. 10.1016/j.msea.2015.01.08010.1016/j.msea.2015.01.080 ↗
42. 10.1007/s11661-018-4562-y10.1007/s11661-018-4562-y ↗
43. 10.2355/isijinternational.53.32310.2355/isijinternational.53.323 ↗
44. 10.1016/S0749-6419(00)00015-210.1016/S0749-6419(00)00015-2 ↗
45. 10.1016/j.msea.2017.02.01410.1016/j.msea.2017.02.014 ↗
46. 10.1016/j.msea.2012.10.08710.1016/j.msea.2012.10.087 ↗
47. 10.1016/j.actamat.2006.10.02910.1016/j.actamat.2006.10.029 ↗
48. 10.1016/j.scriptamat.2012.02.01910.1016/j.scriptamat.2012.02.019 ↗
49. 10.1016/j.actamat.2017.06.04610.1016/j.actamat.2017.06.046 ↗
50. 10.1016/j.msea.2016.10.04310.1016/j.msea.2016.10.043 ↗
51. 10.1016/j.actamat.2009.12.03210.1016/j.actamat.2009.12.032 ↗