Boosting the H₂–D₂ Exchange Activity of Dilute Nanoporous Ti–Cu Catalysts through Oxidation–Reduction Cycle–Induced Restructuring

The use of nanoporous metals as catalysts has attracted significant interest in recent years. Their high‐curvature, nanoscale ligaments provide not only high surface area but also a high density of undercoordinated step edge and kink sites. However, their long‐term stability, especially at higher temperatures, is often limited by thermal coarsening and the associated loss of surface area. Herein, it is demonstrated that the nanoscale morphology of nanoporous Cu can be regenerated by applying oxidation/reduction cycles at 250 °C. Specifically, the morphological evolution and H₂ dissociation activity of hierarchical nanoporous Cu catalysts doped with Ti during structural rearrangement triggered by oxidative and reductive atmospheres at elevated temperatures are studied. In addition to coarsening of the structure at elevated temperatures, oxidation at 400 °C causes an expansion of the ligaments. Subsequent reduction at 400 °C leads to the formation of particles and a drop in the H₂ dissociation activity compared the fresh catalyst. However, performing the redox cycle at 250 °C reverses coarsening and boosts the H₂ dissociation activity for the hydrogen–deuterium (H₂–D₂) reaction. Herein, the possibility to reverse coarsening is demonstrated, thereby mitigating the loss of activity frequently observed in nanoporous catalysts.