Effect of Microalloyed Al on Microstructure and Corrosion Behaviors of As‐Cast Mg–Zn–Y–Mn Alloys
Source abstract
Abstract
The effect of Al microalloying on microstructure and corrosion behaviors of as‐cast Mg–6Zn–8.16Y–2.02Mn is investigated. Microstructural characterization reveals that Al addition can refine grain and lead to the formation of Al(Y, Zn) phase. When a 0.3 wt% Al is added, the alloy exhibits the lowest weight loss rate of 0.99 mm/Y and displays relatively uniform corrosion morphology. However, alloys with more Al addition present localized corrosion on the surface. It results from more W phase (Mg3Zn3Y2) and a little long‐period stacking order (LPSO) phase along the grain boundary. Electrochemical tests are also used to rationalize the corrosion behaviors observed in weight loss. In conclusion, the decrease in corrosion rate is due to grain refinement, optimal quantification of Al(Y, Zn) with short‐rod shape and LPSO phase.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Magnesium Alloys: Properties and Applications · Hydrogen Storage and Materials · Metal and Thin Film Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
College of Materials Science and Engineering Taiyuan University of Technology Taiyuan 030024 P. R. China
College of Materials Science and Engineering Shanxi Key Laboratory of Advanced Magnesium-based Materials Taiyuan 030024 P. R. China
Funding
National Natural Science Foundation of China
References (44)
Show source-provided references
1. 10.1007/s00170-007-1279-210.1007/s00170-007-1279-2 ↗
2. 10.1002/adem.20190090810.1002/adem.201900908 ↗
3. 10.1016/j.ijplas.2019.03.00110.1016/j.ijplas.2019.03.001 ↗
4. 10.1016/j.corsci.2018.12.03710.1016/j.corsci.2018.12.037 ↗
5. 10.1016/j.calphad.2020.10174210.1016/j.calphad.2020.101742 ↗
6. 10.1016/j.jmst.2019.05.01610.1016/j.jmst.2019.05.016 ↗
7. 10.1016/j.jallcom.2019.15229710.1016/j.jallcom.2019.152297 ↗
8. 10.1016/j.jmst.2013.03.00210.1016/j.jmst.2013.03.002 ↗
9. 10.1016/j.jallcom.2019.04.08010.1016/j.jallcom.2019.04.080 ↗
10. 10.1016/j.jmst.2020.01.02210.1016/j.jmst.2020.01.022 ↗
11. 10.1016/j.msea.2019.01.09810.1016/j.msea.2019.01.098 ↗
12. 10.1016/j.jallcom.2017.02.10710.1016/j.jallcom.2017.02.107 ↗
13. 10.1016/j.matdes.2017.02.07810.1016/j.matdes.2017.02.078 ↗
14. 10.1016/j.jallcom.2018.03.25410.1016/j.jallcom.2018.03.254 ↗
15. 10.1016/j.scriptamat.2019.12.01610.1016/j.scriptamat.2019.12.016 ↗
16. 10.1016/j.jmst.2018.06.01510.1016/j.jmst.2018.06.015 ↗
17. 10.1016/j.corsci.2015.03.01810.1016/j.corsci.2015.03.018 ↗
18. 10.1016/j.jmst.2018.05.01410.1016/j.jmst.2018.05.014 ↗
19. 10.1002/adem.20160060610.1002/adem.201600606 ↗
20. 10.1016/j.jmst.2019.09.03810.1016/j.jmst.2019.09.038 ↗
21. 10.1016/j.apsusc.2011.01.04610.1016/j.apsusc.2011.01.046 ↗
22. 10.1002/adem.20050001310.1002/adem.200500013 ↗
23. 10.3139/146.11015710.3139/146.110157 ↗
24. 10.1016/j.actamat.2009.03.01110.1016/j.actamat.2009.03.011 ↗
25. S.Izumi M.Yamasaki Y.Kawamura inMaterials Science Forum Trans Tech Publications Ltd.2010 Vol.654 p.767.10.4028/www.scientific.net/MSF.654-656.767 ↗
26. 10.1016/j.matdes.2015.06.04110.1016/j.matdes.2015.06.041 ↗
27. 10.1016/j.jma.2014.01.00810.1016/j.jma.2014.01.008 ↗
28. 10.1002/adem.20180001710.1002/adem.201800017 ↗
29. 10.1016/j.actamat.2012.05.03510.1016/j.actamat.2012.05.035 ↗
30. 10.1016/j.jallcom.2013.10.04210.1016/j.jallcom.2013.10.042 ↗
31. 10.1016/j.msea.2018.12.06710.1016/j.msea.2018.12.067 ↗
32. 10.1016/j.actbio.2014.07.00510.1016/j.actbio.2014.07.005 ↗
33. 10.1016/j.electacta.2014.03.13310.1016/j.electacta.2014.03.133 ↗
34. 10.1016/j.apsusc.2018.09.20310.1016/j.apsusc.2018.09.203 ↗
35. 10.1016/j.jallcom.2018.06.05610.1016/j.jallcom.2018.06.056 ↗
36. 10.1002/adem.20190114010.1002/adem.201901140 ↗
37. 10.1016/j.surfcoat.2008.10.00410.1016/j.surfcoat.2008.10.004 ↗
38. 10.1002/adem.20031040510.1002/adem.200310405 ↗
39. 10.1016/j.corsci.2019.10841910.1016/j.corsci.2019.108419 ↗
40. 10.1016/j.corsci.2009.03.01110.1016/j.corsci.2009.03.011 ↗
41. 10.1016/j.corsci.2019.10813310.1016/j.corsci.2019.108133 ↗
42. 10.1016/j.intermet.2004.05.00710.1016/j.intermet.2004.05.007 ↗
43. 10.1515/corrrev-2015-000710.1515/corrrev-2015-0007 ↗
44. 10.1007/s40195-018-0709-510.1007/s40195-018-0709-5 ↗