Laser‐Based Closed‐Loop Controlled Heat Treatment for Residual Stress Relief of Additively Manufactured AlSi10Mg Components
Source abstract
Abstract
In laser powder bed fusion of metals small melt pools with extremely short solidification times and steep temperature gradients to the surrounding material exist due to the layer‐wise and selective melting process with small areas of energy input compared to the cooler, solid ambient material. This causes high thermally induced residual stresses (RS), which can lead to the immediate rejection of the component due to critical part deformation and inhomogeneous mechanical properties under load. To prevent this, furnace‐based stress relief heat treatments are commonly applied before cutting‐off the part from the built platform. In this study a novel closed‐loop controlled laser‐based heat treatment using temperature feedback through inline pyrometer measurement is investigated, enabling a fast and highly efficient postprocess stress relief. Therefore, a laser beam is guided by a scanner optics in a meandering pattern over the top surface of AlSi10Mg cantilever specimens. It enables a decrease of near‐surface RS from 158 to 5 N mm−2, resulting in a reduction of displacement by over 90% at material affecting depths up to 3 mm and area rates of 8 to 163 mm2 s−1.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Additive Manufacturing Materials and Processes · Welding Techniques and Residual Stresses · High Entropy Alloys Studies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
LaserApplicationCenter (LAZ) Aalen University of Applied Sciences Aalen 73430 Germany
Chair of Materials Science School of Engineering and Design Technical University of Munich Garching 85748 Germany
Funding
Bundesministerium für Bildung und Forschung
References (33)
Show source-provided references
1. 10.1177/095440541243708510.1177/0954405412437085 ↗
2. 10.1007/978-3-642-54989-210.1007/978-3-642-54989-2 ↗
3. J.‐P.Kruth M.Badrossamay E.Yasa J.Deckers L.Thijs J.Van Humbeeck inProc. of the 16th Inter. Symp. on Electromachining (ISEM XVI) Shanghai China April2010.
4. 10.1007/s11661-014-2549-x10.1007/s11661-014-2549-x ↗
5. 10.1016/j.addma.2017.08.01410.1016/j.addma.2017.08.014 ↗
6. 10.1108/1355254061070701310.1108/13552540610707013 ↗
7. 10.1007/s40192-019-00144-510.1007/s40192-019-00144-5 ↗
8. 10.1007/s40192-019-00149-010.1007/s40192-019-00149-0 ↗
9. 10.1016/j.addma.2017.05.00110.1016/j.addma.2017.05.001 ↗
10. 10.3390/app1010341410.3390/app10103414 ↗
11. 10.1016/j.pmatsci.2017.10.00110.1016/j.pmatsci.2017.10.001 ↗
12. 10.1016/S0007-8506(07)60677-510.1016/S0007-8506(07)60677-5 ↗
13. 10.2351/1.482875510.2351/1.4828755 ↗
14. 10.1016/j.scriptamat.2016.02.02210.1016/j.scriptamat.2016.02.022 ↗
15. 10.1115/1.402851310.1115/1.4028513 ↗
16. 10.1016/j.msea.2017.04.03310.1016/j.msea.2017.04.033 ↗
17. Smith W. L. · Addit. Manuf. · 2021 · 47 · 102252
18. 10.1016/S0921-5093(01)01179-010.1016/S0921-5093(01)01179-0 ↗
19. 10.1007/s11740-009-0192-y10.1007/s11740-009-0192-y ↗
20. 10.1016/j.optlastec.2015.07.00910.1016/j.optlastec.2015.07.009 ↗
21. 10.1007/s40516-023-00217-610.1007/s40516-023-00217-6 ↗
22. 10.3390/ma1303072010.3390/ma13030720 ↗
23. 10.1016/j.vacuum.2018.05.03010.1016/j.vacuum.2018.05.030 ↗
24. 10.1016/j.ijfatigue.2018.07.01610.1016/j.ijfatigue.2018.07.016 ↗
25. 10.3390/met1205075010.3390/met12050750 ↗
26. Pereira R. · Int. J. Lightweight Mater. Manuf. · 2024 · 7 · 248
27. 10.1016/j.surfcoat.2020.12539910.1016/j.surfcoat.2020.125399 ↗
28. 10.1016/j.phpro.2015.11.04010.1016/j.phpro.2015.11.040 ↗
29. 10.1016/j.actamat.2012.11.05210.1016/j.actamat.2012.11.052 ↗
30. 10.1007/s40964-020-00131-910.1007/s40964-020-00131-9 ↗
31. 10.1524/zkri.2008.121310.1524/zkri.2008.1213 ↗
32. 10.1002/srin.20210062710.1002/srin.202100627 ↗
33. 10.1007/s11837-015-1763-310.1007/s11837-015-1763-3 ↗