A Mechanism for the Evolution of Hot Compression Cracking in Inconel 625 Alloy Ingot With Respect to Grain Growth
Source abstract
Abstract
Hot compression cracking of as‐cast Inconel 625 alloy is investigated utilizing high temperature and high strain rate compression tests. The formation mechanism of the hot crack is systematically investigated based on grain growth and crystal slipping. Scanning electron microscopy (SEM) and electron backscattered diffraction (EBSD) analysis are used to characterize the crack morphology and microstructure. SEM results showed that the hot cracking during hot compression of Inconel 625 alloy is determined to be quasi‐cleavage fracture. The formation of carbide (NbC) plays a key role in the formation and propagation of the hot crack. The various slip systems activation strongly contributes to the overall growth of the dynamic recrystallization (DRX) grains. In addition, subgranular boundary formation within the grown grains is attribution to various slip systems activation in different local regions. The initiation and propagation of the hot compression cracks in Inconel 625 alloy depend on the development of the subgranular boundary within the grown grain.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Metallurgy and Material Forming · High Temperature Alloys and Creep · Microstructure and mechanical properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Material Science and Engineering Lanzhou University of Technology No. 287 Langongping Road Qilihe District Lanzhou 730050 P. R. China
State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals Lanzhou University of Technology Lanzhou 730050 P. R. China
School of Materials Engineering Lanzhou Institute of Technology Lanzhou 730050 P. R. China
Funding
National Natural Science Foundation of China
References (59)
Show source-provided references
1. 10.1016/j.matdes.2016.02.05210.1016/j.matdes.2016.02.052 ↗
2. 10.1016/j.jallcom.2015.07.14910.1016/j.jallcom.2015.07.149 ↗
3. 10.1016/j.jallcom.2015.04.00810.1016/j.jallcom.2015.04.008 ↗
4. 10.1016/j.msea.2016.11.06910.1016/j.msea.2016.11.069 ↗
5. 10.3390/ma1203051010.3390/ma12030510 ↗
6. 10.1016/j.msea.2015.06.04310.1016/j.msea.2015.06.043 ↗
7. 10.1016/j.msea.2016.03.04410.1016/j.msea.2016.03.044 ↗
8. 10.1016/j.msea.2015.10.00410.1016/j.msea.2015.10.004 ↗
9. 10.1016/j.jallcom.2014.11.05610.1016/j.jallcom.2014.11.056 ↗
10. 10.1002/adem.20190042610.1002/adem.201900426 ↗
11. 10.1016/j.msea.2019.13816510.1016/j.msea.2019.138165 ↗
12. 10.1016/j.jallcom.2019.01.33410.1016/j.jallcom.2019.01.334 ↗
13. 10.1016/j.jallcom.2019.06.20210.1016/j.jallcom.2019.06.202 ↗
14. 10.1016/j.proeng.2017.10.110810.1016/j.proeng.2017.10.1108 ↗
15. 10.1016/j.matdes.2013.12.07210.1016/j.matdes.2013.12.072 ↗
16. 10.1016/j.jallcom.2018.08.14410.1016/j.jallcom.2018.08.144 ↗
17. Wan Z. P. · Acta Metall. Sin. · 2019 · 55 · 213
18. 10.1016/j.jallcom.2017.05.23310.1016/j.jallcom.2017.05.233 ↗
19. 10.1016/j.msea.2018.07.10410.1016/j.msea.2018.07.104 ↗
20. 10.1016/j.matdes.2016.09.00710.1016/j.matdes.2016.09.007 ↗
21. 10.1016/j.matchar.2018.10.00810.1016/j.matchar.2018.10.008 ↗
22. 10.1016/j.msea.2007.09.00810.1016/j.msea.2007.09.008 ↗
23. 10.1016/j.actamat.2015.03.06010.1016/j.actamat.2015.03.060 ↗
24. 10.1016/j.msea.2014.11.02610.1016/j.msea.2014.11.026 ↗
25. 10.2320/matertrans.M201532310.2320/matertrans.M2015323 ↗
26. 10.1016/j.msea.2013.10.05510.1016/j.msea.2013.10.055 ↗
27. 10.1016/j.actamat.2013.12.01110.1016/j.actamat.2013.12.011 ↗
28. 10.1016/j.msea.2011.04.08310.1016/j.msea.2011.04.083 ↗
29. 10.1016/j.actamat.2008.02.03510.1016/j.actamat.2008.02.035 ↗
30. 10.1016/j.ijfatigue.2019.02.02210.1016/j.ijfatigue.2019.02.022 ↗
31. 10.1016/j.ijfatigue.2019.01.01410.1016/j.ijfatigue.2019.01.014 ↗
32. 10.1007/s11661-002-0302-310.1007/s11661-002-0302-3 ↗
33. 10.1007/s00170-015-6990-910.1007/s00170-015-6990-9 ↗
34. 10.1016/j.pnsc.2016.03.00710.1016/j.pnsc.2016.03.007 ↗
35. 10.1016/j.ijfatigue.2010.11.00310.1016/j.ijfatigue.2010.11.003 ↗
36. 10.1016/j.tafmec.2018.07.00210.1016/j.tafmec.2018.07.002 ↗
37. 10.1007/s11665-015-1678-810.1007/s11665-015-1678-8 ↗
38. 10.1016/S0921-5093(03)00156-410.1016/S0921-5093(03)00156-4 ↗
39. 10.1016/j.ijfatigue.2019.04.02410.1016/j.ijfatigue.2019.04.024 ↗
40. 10.1016/j.matdes.2018.10.04210.1016/j.matdes.2018.10.042 ↗
41. 10.1016/j.ijfatigue.2018.09.00110.1016/j.ijfatigue.2018.09.001 ↗
42. 10.1016/j.matdes.2019.10779310.1016/j.matdes.2019.107793 ↗
43. 10.1016/j.matchar.2017.08.01210.1016/j.matchar.2017.08.012 ↗
44. 10.1016/j.msea.2019.03.11210.1016/j.msea.2019.03.112 ↗
45. 10.1016/j.ijfatigue.2018.08.03310.1016/j.ijfatigue.2018.08.033 ↗
46. 10.1016/j.jallcom.2016.03.16410.1016/j.jallcom.2016.03.164 ↗
47. 10.1016/j.actamat.2017.09.04710.1016/j.actamat.2017.09.047 ↗
48. 10.1016/j.matdes.2015.12.14510.1016/j.matdes.2015.12.145 ↗
49. 10.1016/j.jallcom.2017.12.26510.1016/j.jallcom.2017.12.265 ↗
50. 10.1016/S1003-6326(16)64161-410.1016/S1003-6326(16)64161-4 ↗
51. Wang Y. · J. Mater. Process. Tech. · 2018 · 34 · 2439
52. 10.1016/S1359-6454(96)00193-010.1016/S1359-6454(96)00193-0 ↗
53. 10.1361/10599490177034459310.1361/105994901770344593 ↗
54. 10.1007/BF0264922610.1007/BF02649226 ↗
55. 10.1016/j.ijfatigue.2015.11.01010.1016/j.ijfatigue.2015.11.010 ↗
56. 10.1016/j.jmatprotec.2019.01.01310.1016/j.jmatprotec.2019.01.013 ↗
57. 10.1016/j.matchar.2015.12.01710.1016/j.matchar.2015.12.017 ↗
58. 10.1016/S1359-6454(02)00471-810.1016/S1359-6454(02)00471-8 ↗
59. 10.1007/s00170-017-1197-x10.1007/s00170-017-1197-x ↗