Hexane-assisted sol–gel synthesis of Zn and MoS 2 double-doped TiO 2 nanocomposites for lubrication-relevant surface applications
Source abstract
Abstract
Abstract A structurally stable Zn–MoS 2 –TiO 2 nanocomposite was successfully produced by wet-impregnation doping and a hexane-assisted TiCl 4 sol–gel technique. In this present research work, a novel methodology of hexane-assisted sol–gel synthesis with precise control of reaction parameters was adopted, which helped in maintaining the stability of the anatase TiO 2 structure while improving its surface and interfacial characteristics for lubrication applications. XRD analysis confirmed that the anatase phase was maintained after Zn and MoS 2 inclusion, with an average crystallite size of 15–16 nm. The appearance of the characteristic MoS 2 (002) peak at 14.23° verified the successful integration of stacked MoS 2 nanosheets without structural degradation. Consistent element distribution was confirmed by EDS analysis, and a nanoflower-like morphology was revealed by SEM. While the layered structure of MoS 2 introduced controlled heterogeneity, DLS-zeta analysis showed enhanced dispersion stability after Zn doping (PDI < 0.3). UV-DRS analysis revealed that the absorption edges for Zn–TiO 2 and TiO 2 were approximately 380 nm and 390 nm, respectively. This nanocomposite’s dual absorption properties (∼380 nm and ∼600 nm) indicated the existence of strong interfacial electronic interactions. FTIR spectra confirmed the successful surface modification and revealed the presence of Mo–S and Ti–O bonds. All things considered, a clear structure-property relationship is demonstrated by the combination of improved dispersion behaviour, structural stability, and interfacial electronic modulation. These physicochemical improvements suggest the material’s suitability for lubrication-related applications.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Lubricants and Their Additives · Silicone and Siloxane Chemistry · Polymer Nanocomposites and Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
None Indian Maritime University , Chennai , Tamil Nadu , 600119 , India
Funding
Ministry of Ports, Shipping and Waterways
References (44)
Show source-provided references
1. Ahmed, N., Alam, M.A., Sayem, S.M., Hassan, M., and Ghosh, S. (2025). Enhancing tribological properties of MoS2 coatings through doping: a review of mechanisms and applications. Discover Mech. Eng. 4: 20, https://doi.org/10.1007/s44245-025-00105-7.10.1007/s44245-025-00105-7 ↗
2. Aware, D.V. and Jadhav, S.S. (2015). Synthesis, characterization and photocatalytic applications of Zn-doped TiO2 nanoparticles by sol–gel method. Appl. Nanosci. 6: 972, https://doi.org/10.1007/s13204-015-0513-8.10.1007/s13204-015-0513-8 ↗
3. Azam, S. and Park, S.S. (2024). Impact of biosynthesized CeO2 nanoparticle concentration on the tribological, rheological, and thermal performance of lubricating oil. Lubricants 12: 400, https://doi.org/10.3390/lubricants12110400.10.3390/lubricants12110400 ↗
4. Azhari, M.A., Md Sallehan, M.S., and Nazri, M.N. (2017). Oxidation stability comparison between zinc dialkyldithiophosphate and zinc diamyldithiocarbamate induced palm-oil bio-lubricants. J. Mech. Eng. SI: 23–29, https://ir.uitm.edu.my/id/eprint/39030/.
5. Batool, A., Azizullah, A., Ullah, K., Ali, I., Khattak, M.N.K., and Hussain, S. (2024). Green synthesis of Zn-doped TiO2 nanoparticles from Zanthoxylum armatum and their biological applications. BMC Plant Biol. 24: 820, https://doi.org/10.1186/s12870-024-05525-3.10.1186/s12870-024-05525-3 ↗
6. Binas, V., Venieri, D., Kotzias, D., and Kiriakidis, G. (2017). Modified TiO2 based photocatalysts for improved air and health quality. Ceram. Int. 43: 1836–1846, https://doi.org/10.1016/j.jmat.2016.11.002.10.1016/j.jmat.2016.11.002 ↗
7. Birleanu, C., Pustan, M., Cioaza, M., Molea, A., Popa, F., and Contiu, G. (2022). Effect of TiO2 nanoparticles on the tribological properties of lubricating oil: an experimental investigation. Sci. Rep. 12: 5201, https://doi.org/10.1038/s41598-022-09245-2.10.1038/s41598-022-09245-2 ↗
8. Bukvić, M., Gajević, S., Skulić, A., Savić, S., Ašonja, A., and Stojanović, B. (2024). Tribological application of nanocomposite additives in industrial oils. Lubricants 12: 6, https://doi.org/10.3390/lubricants12010006.10.3390/lubricants12010006 ↗
9. Chen, X. and Mao, S.S. (2007). Titanium dioxide nanomaterials. Chem. Rev. 107: 2891–2959, https://doi.org/10.1021/cr0500535.10.1021/cr0500535 ↗
10. Chen, L., Ou, S.-F., Nguyen, T.-B., Chuang, Y., Chen, C.-W., and Dong, C.-D. (2025). In-situ hydrothermal synthesis of MoS2/TiO2 nanocomposites for enhanced and stable photocatalytic performance: methylene blue degradation pathway and mechanism. J. Taiwan Inst. Chem. Eng. 166: 105436, https://doi.org/10.1016/j.jtice.2024.105436.10.1016/j.jtice.2024.105436 ↗
11. Daghrir, R., Drogui, P., and Robert, D. (2013). Modified TiO2 for environmental photocatalytic applications: a review. Ind. Eng. Chem. Res. 52: 3599, https://doi.org/10.1021/ie303468t.10.1021/ie303468t ↗
12. Diebold, U. (2003). The surface science of titanium dioxide. Surf. Sci. Rep. 48: 53–229, https://doi.org/10.1016/S0167-5729(02)00100-0.10.1016/S0167-5729(02)00100-0 ↗
13. Fujishima, A., Rao, T.N., and Tryk, D.A. (2000). Titanium dioxide photocatalysis. J. Photochemis. Photobiol. C: Photochemis. Rev. 1: 1–21, https://doi.org/10.1016/S1389-5567(00)00002-2.10.1016/S1389-5567(00)00002-2 ↗
14. Gakuru, S.W., Kiprotich, S., and Waithaka, P. (2024). Effects of different Zn doping concentration on the optical and structural properties of TiO2 nanoparticles. Nanosci. Nanotechno. 13: 1–9, https://doi.org/10.5923/j.nn.20241301.01.10.11648/j.am.20241302.11 ↗
15. Han, J., Wang, X., Wang, H., Yang, C., Zhang, H., Wang, Z., Fan, X., Lu, X., Chen, H., Blawert, C., et al.. (2024). Corrosion and friction behaviours of MoSi2/MoS2 nanoparticles incorporated tinted coating on Ti6Al4V alloy. Surf. Coat. Technol. 477: 130292, https://doi.org/10.1016/j.surfcoat.2023.130292.10.1016/j.surfcoat.2023.130292 ↗
16. Hashimoto, K., Irie, H., and Fujishima, A. (2005). TiO2 photocatalysis. Japanese J. Appl. Phys. 44: 8269–8285, https://doi.org/10.1143/JJAP.44.8269.10.1143/JJAP.44.8269 ↗
17. Holmberg, K. and Erdemir, A. (2017). Influence of tribology on energy consumption. Friction 5: 263–284, https://doi.org/10.1007/s40544-017-0183-5.10.1007/s40544-017-0183-5 ↗
18. Ibrahim, M.N.M., Iqbal, A., Shen, C.C., Bhawani, S.A., and Adam, F. (2019). Lignin–TiO2 composites for sunscreen. BMC Chemist. 13: 17, https://doi.org/10.1186/s13065-019-0537-3.10.1186/s13065-019-0537-3 ↗
19. Jazaa, Y., Lan, T., Padalkar, S., and Sundararajan, S. (2018). The effect of agglomeration reduction on the tribological behavior of WS2 and MoS2 nanoparticle additives in the boundary lubrication regime. Lubricant 6: 106, https://doi.org/10.3390/lubricants6040106.10.3390/lubricants6040106 ↗
20. Khanna, N., Airao, J., Nirala, C.K., and Krolczyk, G.M. (2022). Novel sustainable cryo-lubrication strategies for reducing tool wear during ultrasonic-assisted turning of inconel 718. Tribol. Int. 174: 107728, https://doi.org/10.1016/j.triboint.2022.107728.10.1016/j.triboint.2022.107728 ↗
21. Kuznetsova, I.N., Blaskov, V., Stambolova, I., Znaidi, L., and Kanaev, A. (2005). TiO2 pure phase brookite with preferred orientation, synthesized as a spin-coated film. Mater. Lett. 59: 3820–3823, https://doi.org/10.1016/j.matlet.2005.07.019.10.1016/j.matlet.2005.07.019 ↗
22. Li, D., Xie, Y., Yong, H., and Sun, D. (2017). Surfactant-assisted preparation of Y2O3-stabilized ZrO2 nanoparticles and their tribological performance in mineral and commercial lubricating oils. RSC Adv. 7: 3727–3735, https://doi.org/10.1039/C6RA26346A.10.1039/C6RA26346A ↗
23. Lindgren, T., Mwabora, J.M., Avenadno, E., Jonsson, J., Hoel, A., Granqvist, C.G., and Lindquist, S.E. (2003). Photoelectrochemical and optical properties of nitrogen doped titanium dioxide films prepared by reactive DC magnetron sputtering. J. Phys. Chemis. B 107: 5709–5716, https://doi.org/10.1021/jp027345j.10.1021/jp027345j ↗
24. Lu, Z., Lin, Q., Cao, Z., Li, W., Gong, J., Wang, Y., Hu, K., and Hu, X. (2023). MoS2 nanomaterials as lubricant additives. Lubricants 11: 527, https://doi.org/10.3390/lubricants11120527.10.3390/lubricants11120527 ↗
25. Maddaleno, A.S., Casellas, C., Teixido, E., Escote, L.G., Vinardell, L.P., and Mitjans, M. (2025). TiO2 toxicity in sunscreens. Nanomaterials 15: 951, https://doi.org/10.3390/nano15120951.10.3390/nano15120951 ↗
26. Nisar, S.S. and Choe, H.-C. (2025). TiO2 coatings doped with MoS2 nanoparticles using plasma electrolytic oxidation on Ti–6Al–4V alloy: application for enhanced and functional bio-implant surface. J. Mater. Res. Technol. 33: 2035–2056, https://doi.org/10.1016/j.jmrt.2024.09.185.10.1016/j.jmrt.2024.09.185 ↗
27. Nugroho, A., Kozin, M., Mamat, R., Bo, Z., Ghazali, M.F., Kamil, M.P., Puranto, P., Fitriani, D.A., Azahra, S.A., Suwondo, K.P., et al.. (2024). Nanoparticle-enriched biolubricants. Heliyon 10: e39742, https://doi.org/10.1016/j.heliyon.2024.e39742.10.1016/j.heliyon.2024.e39742 ↗
28. Pierre, A.C. and Pajonk, G.M. (2002). Chemistry of aerogels and their applications. Chem. Rev. 102: 4243–4266, https://doi.org/10.1021/cr0101306.10.1021/cr0101306 ↗
29. Ratoi, M., Niste, V.B., and Zekonyte, J. (2014). WS2 nanoparticles: potential replacement for ZDDP and friction modifier additives. RSC Adv. 4: 21238–21245, https://doi.org/10.1039/C4RA01795A.10.1039/C4RA01795A ↗
30. Santalucia, R., Vacca, T., Cesano, F., Martra, G., Pellegrino, F., and Scarano, D. (2021). Few-layered MoS2 nanoparticles covering anatase TiO2 nanosheets: comparison between ex situ and in situ synthesis approaches. Appl. Sci. 11: 143, https://doi.org/10.3390/app11010143.10.3390/app11010143 ↗
31. Santhi, K., Ponnusamy, S., Harish, S., and Navaneethan, N. (2022). A facile synthesis of Zn-doped TiO2 nanostructures for enhanced photocatalytic performance. J. Mater. Sci.: Mater. Electron. 33: 9798–9813, https://doi.org/10.1007/s10854-022-07945-z.10.1007/s10854-022-07945-z ↗
32. Sheit, H.M.K., Mohan, K.S., Geetha, N., Lavanya, R., Kannan, K., Esakki Muthu, S., Ayyar, M., Paramasivam, P., Rajesndran, S., Santhamoorthy, M., et al.. (2026). Nanoengineered t-ZrO2 coatings for superior corrosion resistance on steel surfaces. Sci. Rep. 16: 439, https://doi.org/10.1038/s41598-025-30044-y.10.1038/s41598-025-30044-y ↗
33. Sugimoto, T. (1987). Preparation of monodispersed colloidal particles. Adv. Colloid Interface Sci. 28: 65–108, https://doi.org/10.1016/0001-8686(87)80009-X.10.1016/0001-8686(87)80009-X ↗
34. Sugimoto, T., Zhou, X., and Muramatsu, A. (2002). Synthesis of uniform anatase TiO2 nanoparticles by gel–sol method: 1. solution chemistry of Ti(OH)n(4−n)+ complexes. J. Colloid Interface Sci. 252: 339–346, https://doi.org/10.1006/jcis.2002.8454.10.1006/jcis.2002.8454 ↗
35. Sultana, M., Mondal, A., Islam, S., Khatun, M.A., Rahaman, M.H., Chakraborty, A.K., Rahman, M.S., Rahman, M.M., and Nur, A.S. (2023). Strategic development of metal doped TiO2 photocatalysts for enhanced dye degradation activity under UV–vis irradiation: a review. Curren. Res. Green and Sustaina. Chemist. 7: 100383, https://doi.org/10.1016/j.crgsc.2023.100383.10.1016/j.crgsc.2023.100383 ↗
36. Tasbihi, M., Lavrenčič Štangar, U., Cernigoj, U., and Kogej, K. (2009). Low-temperature synthesis and characterization of anatase TiO2 powders from inorganic precursors. Photochem. Photobiol. Sci. 8: 719–725, https://doi.org/10.1039/b817472e.10.1039/b817472e ↗
37. Tian, Y., Guo, K., Bian, X., Wang, T., Chen, S., and Sun, J. (2017). Durable and room-temperature curable superhydrophobic composite coating on nitrocellulose lacquer. Surf. Coat. Technol. 328: 444–450, https://doi.org/10.1016/j.surfcoat.2017.08.056.10.1016/j.surfcoat.2017.08.056 ↗
38. Vazirisereshk, M.R., Martini, A., Strubbe, D.A., and Baykara, M.Z. (2019). Solid lubrication with MoS2: a review. Lubricants 7: 57, https://doi.org/10.3390/lubricants7070057.10.3390/lubricants7070057 ↗
39. Vorkapic, D. and Matsoukas, T. (1998). Effect of temperature and alcohols in the preparation of titania nanoparticles from alkoxides. J. Am. Ceram. Soc. 81: 2815–2820, https://doi.org/10.1111/j.1151-2916.1998.tb02701.x.10.1111/j.1151-2916.1998.tb02701.x ↗
40. Wattanawikkam, C. and Pecharapa, W. (2015). Synthesis and characterization of Zn-doped TiO2 nanoparticles via sonochemical method. Integra. Ferroelec. 165: 167–175, https://doi.org/10.1080/10584587.2015.1063928.10.1080/10584587.2015.1063928 ↗
41. Wight, A.P. and Davis, M.E. (2002). Design and preparation of organic–inorganic hybrid catalysts. Chem. Rev. 102: 3589–3614, https://doi.org/10.1021/cr010334m.10.1021/cr010334m ↗
42. Zeng, K., Cheng, L., Hu, W., and Li, J. (2025). Synthesis, stability, and tribological performance of TiO2 nanomaterials for advanced applications. Lubricants 13: 56, https://doi.org/10.3390/lubricants13020056.10.3390/lubricants13020056 ↗
43. Zhang, S., Zhang, M., Jiang, H., Chen, L., Han, D., Hu, X., and Qiu, L. (2025). Tribological behavior and wear mechanism of TiO2/MoS2 nanocomposite coatings fabricated on TC6 alloys by micro-arc oxidation and duplex surface technologies. Surf. Coating. Technol. 510: 132227, https://doi.org/10.1016/j.surfcoat.2025.132227.10.1016/j.surfcoat.2025.132227 ↗
44. Zhao, X., An, Y., Hou, G., Zhou, H., and Chen, J. (2016). Preparation and tribological properties of plasma sprayed nano- and micro-structure alumina-reinforced CuAl composite coatings. Tribol. Int. 101: 255–263, https://doi.org/10.1016/j.triboint.2016.04.034.10.1016/j.triboint.2016.04.034 ↗