Analyzing the Phase Evolution, Microstructure and Wear Response of Spark Plasma Sintered Al0.5CoCrFeNi2 High Entropy Superalloy

Abhishek Tikar, Shubhankar Padwal, Shih-Hsun Chen, Sandip P. Harimkar

Advanced Engineering Materials· Volume 25· Issue 9
Publisher page

Abstract

High entropy superalloys (HESA), an extension of high entropy alloys (HEAs), exhibit excellent high‐temperature properties with low density, making them a potential replacement for expensive and heavy superalloys. While multiple processing routes are available for HEAs, spark plasma sintering is becoming increasingly popular due to its ability to fabricate alloy powder in short period of time. Herein, the phase evolution and microstructural development of gas atomized Al0.5CoCrFeNi2 HESA powder fabricated using spark plasma sintering and the wear properties of the sintered specimen are reported. The alloy powder and all the specimen sintered in the range of 800–1050 °C show an extremely stable single‐phase face centered cubic structure. Relative density of 99% is achieved at 1000 °C and above with porosity pinning effect playing an important role in densification behavior and grain growth. In all the sintered specimen, a combination of adhesive, delamination, oxidation, and abrasive wear is observed, with the coefficient of friction lying in the range of 0.6–0.7.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: High Entropy Alloys Studies · High-Temperature Coating Behaviors · Additive Manufacturing Materials and Processes

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Department of Mechanical and Aerospace Engineering Oklahoma State University Stillwater OK 74078 USA

Department of Mechanical Engineering National Taiwan University of Science and Technology Taipei 10607 Taiwan ROC

References (34)

Show source-provided references
1. 10.4028/www.scientific.net/MSF.560.110.4028/www.scientific.net/MSF.560.1 ↗
2. 10.1080/21663831.2014.91269010.1080/21663831.2014.912690 ↗
3. S.Chikumba V. V.Rao in7th Int. Conf. Latest Trends Eng. Technol. Irene Pretoria (South Africa)2015 pp.1–5 https://doi.org/10.15242/IIE.E1115005.10.15242/IIE.E1115005 ↗
4. 10.1557/jmr.2018.15310.1557/jmr.2018.153 ↗
5. 10.1016/j.jallcom.2019.01.38610.1016/j.jallcom.2019.01.386 ↗
6. 10.1088/2053-1591/aabbca10.1088/2053-1591/aabbca ↗
7. 10.1007/s11837-017-2540-210.1007/s11837-017-2540-2 ↗
8. 10.21533/pen.v3i1.4310.21533/pen.v3i1.43 ↗
9. 10.1016/j.matpr.2017.02.26610.1016/j.matpr.2017.02.266 ↗
10. 10.1016/j.scriptamat.2020.06.00210.1016/j.scriptamat.2020.06.002 ↗
11. Yeh A. · Int. J. Metall. Mater. Eng. · 2015 · 1 · 1
12. 10.1016/j.scriptamat.2017.12.00110.1016/j.scriptamat.2017.12.001 ↗
13. 10.1179/00325890222500704110.1179/003258902225007041 ↗
14. 10.1007/s10853-006-6555-210.1007/s10853-006-6555-2 ↗
15. 10.1016/j.matdes.2020.10866210.1016/j.matdes.2020.108662 ↗
16. 10.1016/j.matlet.2016.06.01410.1016/j.matlet.2016.06.014 ↗
17. 10.1016/j.jallcom.2016.12.01010.1016/j.jallcom.2016.12.010 ↗
18. 10.1016/j.matchemphys.2017.09.01310.1016/j.matchemphys.2017.09.013 ↗
19. 10.1063/1.358722810.1063/1.3587228 ↗
20. 10.1016/j.intermet.2012.03.00510.1016/j.intermet.2012.03.005 ↗
21. 10.1016/j.matlet.2006.03.14010.1016/j.matlet.2006.03.140 ↗
22. 10.1016/j.matdes.2015.05.02710.1016/j.matdes.2015.05.027 ↗
23. 10.1016/j.surfcoat.2020.12641110.1016/j.surfcoat.2020.126411 ↗
24. 10.2464/jilm.40.85010.2464/jilm.40.850 ↗
25. 10.1016/S0921-5093(00)01465-910.1016/S0921-5093(00)01465-9 ↗
26. 10.1007/s11837-003-0153-410.1007/s11837-003-0153-4 ↗
27. 10.1051/matecconf/20192690500410.1051/matecconf/201926905004 ↗
28. Al-Shobaki S. D. · Jordan J. Mech. Ind. Eng. · 2007 · 5 · 267
29. 10.1590/S1516-1439200700010001910.1590/S1516-14392007000100019 ↗
30. 10.1557/JMR.1995.100010.1557/JMR.1995.1000 ↗
31. Kang S.-J. L. · 2004
32. 10.1016/0921-5093(89)90403-610.1016/0921-5093(89)90403-6 ↗
33. 10.1016/j.matdes.2013.09.05810.1016/j.matdes.2013.09.058 ↗
34. 10.1016/0043-1648(94)90097-310.1016/0043-1648(94)90097-3 ↗