Crack‐Free Welding of a Co‐Base Superalloy with High γ' Precipitate Fraction
Source abstract
Abstract
Laser cladding of superalloys provides an attractive and cost‐efficient technique for near‐net shape manufacturing, remanufacturing, or individualized repair of components. While the weldability of γ' hardened Ni‐base superalloys is limited, Co‐base superalloys should have a lower susceptibility for cracking during welding due to a lower γ' solvus temperature and less segregation than Ni‐base superalloys. The weldability of the Co‐base superalloy CoWAlloy2Mod and the resulting mechanical properties at 950 °C are investigated. In the as‐welded condition of CoWAlloy2Mod, a fine dendritic microstructure without forming cracks and limited porosity is found. After a three‐step heat treatment, recrystallized, equiaxed grains and a high γ' volume fraction are obtained leading to a very good strength. CoWAlloy2Mod shows a significantly higher strength and creep strength than the conventional weld filler Co‐alloy PWA795.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Additive Manufacturing Materials and Processes · High Entropy Alloys Studies · Welding Techniques and Residual Stresses
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Materials Science & Engineering, Institute I Friedrich-Alexander-Universität Erlangen-Nürnberg (FAU) Martensstr. 5 91058 Erlangen Germany
Gas and Power, Power Generation Operations, Metallic Materials Siemens Energy AG Huttenstr. 12 10553 Berlin Germany
References (64)
Show source-provided references
1. 10.1179/1743280411Y.000000001410.1179/1743280411Y.0000000014 ↗
2. 10.1007/s11665-014-0958-z10.1007/s11665-014-0958-z ↗
3. 10.1016/j.pmatsci.2017.10.00110.1016/j.pmatsci.2017.10.001 ↗
4. 10.1179/imr.1998.43.1.110.1179/imr.1998.43.1.1 ↗
5. 10.1016/S0924-0136(01)01121-910.1016/S0924-0136(01)01121-9 ↗
6. 10.1179/13621710422501709910.1179/136217104225017099 ↗
7. 10.1016/j.jclepro.2014.05.08410.1016/j.jclepro.2014.05.084 ↗
8. 10.1016/j.optlastec.2005.10.00910.1016/j.optlastec.2005.10.009 ↗
9. Arjakine N. · 2008 · 559
10. 10.1016/j.matdes.2019.10810510.1016/j.matdes.2019.108105 ↗
11. 10.1016/j.matchar.2010.02.01610.1016/j.matchar.2010.02.016 ↗
12. 10.1016/j.scriptamat.2004.06.01310.1016/j.scriptamat.2004.06.013 ↗
13. 10.1016/j.scriptamat.2003.11.02510.1016/j.scriptamat.2003.11.025 ↗
14. 10.1016/j.msea.2009.01.00910.1016/j.msea.2009.01.009 ↗
15. 10.1007/s11661-009-9949-310.1007/s11661-009-9949-3 ↗
16. 10.1016/j.ijmachtools.2011.02.00310.1016/j.ijmachtools.2011.02.003 ↗
17. 10.1016/j.matdes.2016.03.00610.1016/j.matdes.2016.03.006 ↗
18. 10.2351/1.475771710.2351/1.4757717 ↗
19. 10.1557/mrs.2016.21110.1557/mrs.2016.211 ↗
20. 10.31399/asm.tb.stg2.978162708267910.31399/asm.tb.stg2.9781627082679 ↗
21. Davis J. R. · 2000
22. 10.1038/s41467-020-18775-010.1038/s41467-020-18775-0 ↗
23. 10.1002/978047050026210.1002/9780470500262 ↗
24. 10.1017/CBO978051154128510.1017/CBO9780511541285 ↗
25. 10.1007/BF0265158910.1007/BF02651589 ↗
26. 10.1016/j.scriptamat.2010.08.03610.1016/j.scriptamat.2010.08.036 ↗
27. 10.1126/science.112173810.1126/science.1121738 ↗
28. 10.1007/BF0264443410.1007/BF02644434 ↗
29. 10.1007/BF0115109110.1007/BF01151091 ↗
30. Bassford T. H. · Handb. Mater. Sel. · 2002 · 235
31. D. N.Frey J. W.Freeman A. E.White 1951https://ntrs.nasa.gov/citations/19930087860.
32. Kelly T. · Weld. J. · 1990 · 69 · S422
33. Gupta C. K. · 1994
34. 10.1016/j.scriptamat.2015.07.03010.1016/j.scriptamat.2015.07.030 ↗
35. 10.1016/j.actamat.2014.08.03310.1016/j.actamat.2014.08.033 ↗
36. 10.1016/j.corsci.2011.02.03310.1016/j.corsci.2011.02.033 ↗
37. 10.1016/j.corsci.2014.03.00210.1016/j.corsci.2014.03.002 ↗
38. 10.1007/s11837-010-0013-y10.1007/s11837-010-0013-y ↗
39. Volz N. · 2020
40. Campbell J. · 2015
41. 10.1016/S1359-6454(02)00042-310.1016/S1359-6454(02)00042-3 ↗
42. 10.1007/s11661-004-0018-710.1007/s11661-004-0018-7 ↗
43. Dupont J. N. · Weld. J. Miami Fla · 1998 · 77 · 417
44. 10.1007/BF0265030010.1007/BF02650300 ↗
45. 10.1007/BF0264500110.1007/BF02645001 ↗
46. 10.1007/BF0259545210.1007/BF02595452 ↗
47. 10.1016/j.matdes.2014.04.02010.1016/j.matdes.2014.04.020 ↗
48. 10.1007/s11661-018-4762-510.1007/s11661-018-4762-5 ↗
49. 10.1007/s11661-021-06568-z10.1007/s11661-021-06568-z ↗
50. 10.1016/j.actamat.2020.09.02310.1016/j.actamat.2020.09.023 ↗
51. 10.1016/j.msea.2016.07.11610.1016/j.msea.2016.07.116 ↗
52. 10.3390/met1003032110.3390/met10030321 ↗
53. 10.15407/tpwj2014.02.0210.15407/tpwj2014.02.02 ↗
54. 10.1016/j.jallcom.2020.15415810.1016/j.jallcom.2020.154158 ↗
55. 10.1016/j.jallcom.2019.07.12110.1016/j.jallcom.2019.07.121 ↗
56. 10.1016/j.msea.2016.10.12410.1016/j.msea.2016.10.124 ↗
57. 10.2320/matertrans.MER200807310.2320/matertrans.MER2008073 ↗
58. 10.1016/j.scriptamat.2015.09.01810.1016/j.scriptamat.2015.09.018 ↗
59. 10.1016/j.intermet.2013.10.02210.1016/j.intermet.2013.10.022 ↗
60. 10.1038/nmeth.201910.1038/nmeth.2019 ↗
61. 10.1093/bioinformatics/btx18010.1093/bioinformatics/btx180 ↗
62. 10.1016/j.actamat.2014.06.02010.1016/j.actamat.2014.06.020 ↗
63. 10.1007/s11837-014-1175-910.1007/s11837-014-1175-9 ↗
64. 10.1016/j.jallcom.2018.04.20410.1016/j.jallcom.2018.04.204 ↗