Room‐Temperature Superformability in Novel As‐Cast High‐Entropy Alloy During Compressive Loading
Source abstract
Abstract
Conventional alloys show low compressive strength and strain accommodation due to their propensity for limited strengthening mechanisms and rapid compressive instability. High‐entropy alloys (HEA) may overcome this limitation by metastability engineering. Inspired by this, herein, a dual‐phase Fe44Mn20Cr15Ni7.5Co6Si7.5 HEA (M‐HEA) which shows maximum engineering strength of ≈4.4 GPa at true compressive strain of ≈2.2 (engineering strain of 90%) in as‐cast condition due to controlled hardening and sustained softening response during deformation is presented. The controlled hardening phenomenon (up to 60% strain) is attributed to transformation‐induced plasticity in γ‐phase and nanotwinning in untransformed γ‐phase. The sustained softening is a result of extensive strain accommodation by both γ‐ and β‐phases via dynamic recovery in γ‐phase and shearing of β‐phase during deformation. Hence, this superformability in M‐HEA makes it an excellent material for structural applications in comparison with other conventional alloys and HEAs.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: High Entropy Alloys Studies · High-Temperature Coating Behaviors · Advanced materials and composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Advanced Materials Design and Processing Group Department of Metallurgical and Materials Engineering Indian Institute of Technology Jodhpur 342037 Karwar, Jodhpur Rajasthan India
Department of Material Science and Engineering National Chung Hsing University 402 Taichung City Taiwan
Laboratory for Texture and Related Studies Department of Materials Engineering Indian Institute of Science 560012 Bangalore Karnataka India
Funding
Ministry of Education · Ministry of Science and Technology, Taiwan
References (58)
Show source-provided references
1. Bhadeshia H. K. D. H. · Prog. Mater. Sci. · 2012 · 572 · 68
2. Li Z. · J. Mater. Eng. · 2013 · 22 · 1208
3. 10.1007/s11837-014-1032-x10.1007/s11837-014-1032-x ↗
4. 10.1016/j.scriptamat.2022.11475710.1016/j.scriptamat.2022.114757 ↗
5. 10.1016/j.msea.2003.10.25710.1016/j.msea.2003.10.257 ↗
6. 10.1002/adem.20030056710.1002/adem.200300567 ↗
7. 10.1016/j.jallcom.2021.15958710.1016/j.jallcom.2021.159587 ↗
8. 10.1016/j.msea.2013.01.00610.1016/j.msea.2013.01.006 ↗
9. 10.1016/j.jallcom.2009.08.09010.1016/j.jallcom.2009.08.090 ↗
10. 10.1016/j.msea.2018.05.00110.1016/j.msea.2018.05.001 ↗
11. 10.1016/j.jallcom.2009.12.18310.1016/j.jallcom.2009.12.183 ↗
12. 10.1016/j.matdes.2017.01.08210.1016/j.matdes.2017.01.082 ↗
13. 10.1038/srep0620010.1038/srep06200 ↗
14. 10.1016/j.scriptamat.2021.11413210.1016/j.scriptamat.2021.114132 ↗
15. 10.1038/nature1798110.1038/nature17981 ↗
16. 10.1016/j.msea.2020.13958010.1016/j.msea.2020.139580 ↗
17. 10.1016/j.actamat.2017.02.00410.1016/j.actamat.2017.02.004 ↗
18. 10.1016/j.jallcom.2019.04.03510.1016/j.jallcom.2019.04.035 ↗
19. 10.1007/s11837-017-2540-210.1007/s11837-017-2540-2 ↗
20. 10.1038/s41598-017-18230-z10.1038/s41598-017-18230-z ↗
21. 10.1016/j.matdes.2020.10896810.1016/j.matdes.2020.108968 ↗
22. 10.1007/s12540-017-6701-110.1007/s12540-017-6701-1 ↗
23. ASTM E9-19 · 2019
24. R.Chait C. H.Curll Evaluating Engineering Alloys in Compression ASTM STP27852S 1976.10.1520/STP27852S ↗
25. 10.1016/j.scriptamat.2021.11407010.1016/j.scriptamat.2021.114070 ↗
26. 10.1038/s41598-018-28383-010.1038/s41598-018-28383-0 ↗
27. 10.1016/j.istruc.2021.07.06310.1016/j.istruc.2021.07.063 ↗
28. 10.1016/j.mechmat.2017.08.00710.1016/j.mechmat.2017.08.007 ↗
29. 10.1016/j.actamat.2019.12.04010.1016/j.actamat.2019.12.040 ↗
30. 10.1016/j.matdes.2016.12.02010.1016/j.matdes.2016.12.020 ↗
31. 10.1016/j.ijplas.2018.10.01410.1016/j.ijplas.2018.10.014 ↗
32. Li J. · J. Mater. Sci. Technol. · 2022 · 120 · 107
33. 10.1016/0001-6160(85)90080-X10.1016/0001-6160(85)90080-X ↗
34. 10.1016/0079-6425(85)90009-X10.1016/0079-6425(85)90009-X ↗
35. Mecking H. · 1980 · 197
36. 10.4028/www.scientific.net/SSP.35-36.110.4028/www.scientific.net/SSP.35-36.1 ↗
37. 10.1007/BF0266156210.1007/BF02661562 ↗
38. 10.1016/S0079-6425(97)00032-710.1016/S0079-6425(97)00032-7 ↗
39. 10.1016/B978-0-08-098235-9.00005-710.1016/B978-0-08-098235-9.00005-7 ↗
40. 10.1016/j.matdes.2012.04.01910.1016/j.matdes.2012.04.019 ↗
41. Verlinden B. · 2007
42. 10.1016/j.scriptamat.2018.05.04310.1016/j.scriptamat.2018.05.043 ↗
43. 10.1111/j.1151-2916.1981.tb10244.x10.1111/j.1151-2916.1981.tb10244.x ↗
44. 10.1016/j.actamat.2018.11.03310.1016/j.actamat.2018.11.033 ↗
45. Lee K. · J. Alloys Compd. · 2017 · 723 · 156
46. 10.1016/j.matdes.2015.11.01310.1016/j.matdes.2015.11.013 ↗
47. Chang X. · 2017 · 293
48. 10.1016/j.msea.2018.07.06910.1016/j.msea.2018.07.069 ↗
49. 10.1016/j.jallcom.2022.16504310.1016/j.jallcom.2022.165043 ↗
50. 10.1007/s00339-014-8964-410.1007/s00339-014-8964-4 ↗
51. 10.1016/j.jallcom.2015.09.15310.1016/j.jallcom.2015.09.153 ↗
52. 10.1007/s11661-018-4871-110.1007/s11661-018-4871-1 ↗
53. 10.1016/j.jallcom.2021.16180010.1016/j.jallcom.2021.161800 ↗
54. 10.1016/j.matchar.2020.11083610.1016/j.matchar.2020.110836 ↗
55. 10.1016/j.proeng.2012.03.04310.1016/j.proeng.2012.03.043 ↗
56. 10.3390/ma1102020810.3390/ma11020208 ↗
57. 10.1016/j.matlet.2018.01.12410.1016/j.matlet.2018.01.124 ↗
58. 10.1016/j.msea.2021.14229010.1016/j.msea.2021.142290 ↗