Carbon Segregation in CoCrFeMnNi High‐Entropy Alloy Driven by High‐Pressure Torsion at Room and Cryogenic Temperatures
Source abstract
Abstract
Herein, a CoCrFeMnNi high‐entropy alloy with reduced Cr content and with the addition of 2 at% C interstitial is processed via high‐pressure torsion (HPT) under 6.5 GPa by three turns at room and cryogenic temperatures. The microstructure is investigated by transmission electron microscopy (TEM) and atom probe tomography (APT). The results indicate that C atoms segregate at the boundaries of the nanograins in the sample processed at room temperature, while the sample processed at cryogenic temperature does not show any notable segregations of carbon.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: High Entropy Alloys Studies · High-Temperature Coating Behaviors · Advanced materials and composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Institute of Nanotechnology Karlsruhe Institute of Technology Hermann-von-Helmholtz-Platz 1 76344 Eggenstein-Leopoldshafen Germany
Karlsruhe Nano-Micro Facility Karlsruhe Institute of Technology Hermann-von-Helmholtz-Platz 1 76344 Eggenstein-Leopoldshafen Germany
Funding
China Scholarship Council
References (31)
Show source-provided references
1. 10.1016/j.msea.2003.10.25710.1016/j.msea.2003.10.257 ↗
2. 10.1016/j.actamat.2016.07.03810.1016/j.actamat.2016.07.038 ↗
3. 10.1016/j.intermet.2014.05.01410.1016/j.intermet.2014.05.014 ↗
4. 10.1016/j.jallcom.2019.03.37310.1016/j.jallcom.2019.03.373 ↗
5. 10.1016/j.actamat.2013.06.01810.1016/j.actamat.2013.06.018 ↗
6. 10.1016/j.jallcom.2015.05.22410.1016/j.jallcom.2015.05.224 ↗
7. 10.1016/j.jallcom.2019.15200010.1016/j.jallcom.2019.152000 ↗
8. 10.1016/j.actamat.2018.10.05010.1016/j.actamat.2018.10.050 ↗
9. 10.1016/j.pmatsci.2008.03.00210.1016/j.pmatsci.2008.03.002 ↗
10. 10.1016/S0079-6425(99)00007-910.1016/S0079-6425(99)00007-9 ↗
11. 10.1016/j.mtla.2021.10105910.1016/j.mtla.2021.101059 ↗
12. 10.1016/j.actamat.2011.08.02310.1016/j.actamat.2011.08.023 ↗
13. 10.1007/s10853-006-0750-z10.1007/s10853-006-0750-z ↗
14. 10.1002/adem.20180044310.1002/adem.201800443 ↗
15. 10.1016/j.jallcom.2017.03.35210.1016/j.jallcom.2017.03.352 ↗
16. 10.1016/j.actamat.2015.06.02510.1016/j.actamat.2015.06.025 ↗
17. 10.1016/j.msea.2016.08.11810.1016/j.msea.2016.08.118 ↗
18. 10.3390/cryst1004033610.3390/cryst10040336 ↗
19. 10.1002/adem.20190075210.1002/adem.201900752 ↗
20. 10.1016/j.jallcom.2021.16145210.1016/j.jallcom.2021.161452 ↗
21. 10.1016/j.actamat.2018.12.02810.1016/j.actamat.2018.12.028 ↗
22. 10.1016/0956-7151(94)90444-810.1016/0956-7151(94)90444-8 ↗
23. 10.1016/0001-6160(64)90220-210.1016/0001-6160(64)90220-2 ↗
24. 10.1016/j.actamat.2008.07.02910.1016/j.actamat.2008.07.029 ↗
25. 10.1016/j.msea.2007.06.09310.1016/j.msea.2007.06.093 ↗
26. 10.1021/acs.jpcc.8b0765010.1021/acs.jpcc.8b07650 ↗
27. 10.1016/j.msea.2020.13931510.1016/j.msea.2020.139315 ↗
28. 10.1016/j.intermet.2014.12.00410.1016/j.intermet.2014.12.004 ↗
29. 10.1016/j.matchar.2017.05.01410.1016/j.matchar.2017.05.014 ↗
30. 10.1016/j.mtnano.2021.10011010.1016/j.mtnano.2021.100110 ↗
31. 10.1016/j.scriptamat.2015.05.04110.1016/j.scriptamat.2015.05.041 ↗