Microstructure and Corrosion Behavior of the Friction Stir Welded Joints Made from Ultrafine Grained Aluminum
Source abstract
Abstract
Joints made from ultrafine grained aluminium alloy 1050 are investigated in order to examine the corrosion behavior and microstructural changes between base materials and stir zones. Samples in the initial state, after four and eight passes of Incremental ECAP (I‐ECAP) process were joined with similar plates using Friction Stir Welding. Initially refined microstructure after I‐ECAP transformed to homogenous few micron sized grains structure in stir zones. AlFeSi particles present in the microstructure became fragmented during plastic deformation and welding process. The observed minor differences in corrosion resistance include slightly higher values of corrosion potentials but more complex pits’ morphology for I‐ECAP processed samples comparing to the stir zones.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Advanced Welding Techniques Analysis · Metal Forming Simulation Techniques · Aluminum Alloys Composites Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Faculty of Materials Science and Engineering Warsaw University of Technology Woloska 141 02‐507 Warsaw Poland
Institute of Manufacturing Processes Warsaw University of Technology Narbutta 85 02‐524 Warsaw Poland
Design, Manufacture and Engineering Management University of Strathclyde 75 Montrose Street Glasgow G1 1XJ United Kingdom
References (40)
Show source-provided references
1. 10.1016/j.actamat.2013.08.01810.1016/j.actamat.2013.08.018 ↗
2. 10.1016/j.pmatsci.2006.02.00310.1016/j.pmatsci.2006.02.003 ↗
3. 10.1016/0921-5093(95)09705-810.1016/0921-5093(95)09705-8 ↗
4. 10.1016/S0921-5093(98)00750-310.1016/S0921-5093(98)00750-3 ↗
5. 10.1016/j.actamat.2010.01.03810.1016/j.actamat.2010.01.038 ↗
6. 10.1016/j.scriptamat.2004.11.01410.1016/j.scriptamat.2004.11.014 ↗
7. 10.1016/S0921-5093(97)00467-X10.1016/S0921-5093(97)00467-X ↗
8. 10.1016/j.msea.2012.09.07910.1016/j.msea.2012.09.079 ↗
9. 10.1088/1757-899X/63/1/01200410.1088/1757-899X/63/1/012004 ↗
10. 10.4028/www.scientific.net/MSF.584-586.10810.4028/www.scientific.net/MSF.584-586.108 ↗
11. 10.4028/www.scientific.net/MSF.584-586.13910.4028/www.scientific.net/MSF.584-586.139 ↗
12. 10.1016/j.jmapro.2013.04.00210.1016/j.jmapro.2013.04.002 ↗
13. 10.1016/j.scriptamat.2007.09.06410.1016/j.scriptamat.2007.09.064 ↗
14. 10.1016/j.matdes.2015.08.12910.1016/j.matdes.2015.08.129 ↗
15. 10.1007/s10008-007-0496-910.1007/s10008-007-0496-9 ↗
16. 10.1016/j.matdes.2014.01.00510.1016/j.matdes.2014.01.005 ↗
17. 10.1016/j.msea.2003.08.05610.1016/j.msea.2003.08.056 ↗
18. 10.4028/www.scientific.net/KEM.710.5910.4028/www.scientific.net/KEM.710.59 ↗
19. 10.1002/srin.20130002610.1002/srin.201300026 ↗
20. 10.1016/j.corsci.2006.01.00510.1016/j.corsci.2006.01.005 ↗
21. 10.1088/1757-899X/63/1/01201010.1088/1757-899X/63/1/012010 ↗
22. 10.1016/S1359-6454(97)00494-110.1016/S1359-6454(97)00494-1 ↗
23. 10.1016/j.msea.2006.02.47310.1016/j.msea.2006.02.473 ↗
24. 10.1016/j.msea.2015.03.09810.1016/j.msea.2015.03.098 ↗
25. 10.1016/j.matdes.2010.08.00110.1016/j.matdes.2010.08.001 ↗
26. 10.1016/j.msea.2009.07.07110.1016/j.msea.2009.07.071 ↗
27. 10.1016/j.matdes.2012.04.01610.1016/j.matdes.2012.04.016 ↗
28. 10.1016/j.msea.2011.03.02410.1016/j.msea.2011.03.024 ↗
29. 10.1016/j.matchar.2005.08.00510.1016/j.matchar.2005.08.005 ↗
30. 10.1016/j.actamat.2006.09.03710.1016/j.actamat.2006.09.037 ↗
31. 10.1016/j.msea.2013.09.00610.1016/j.msea.2013.09.006 ↗
32. 10.1016/j.msea.2013.10.03110.1016/j.msea.2013.10.031 ↗
33. 10.1016/j.corsci.2006.05.03810.1016/j.corsci.2006.05.038 ↗
34. 10.1016/j.matdes.2015.06.01810.1016/j.matdes.2015.06.018 ↗
35. 10.1016/j.electacta.2009.11.01610.1016/j.electacta.2009.11.016 ↗
36. 10.1016/j.corsci.2011.12.01610.1016/j.corsci.2011.12.016 ↗
37. 10.1016/j.jmatprotec.2007.06.03410.1016/j.jmatprotec.2007.06.034 ↗
38. 10.1016/j.matchemphys.2016.02.00410.1016/j.matchemphys.2016.02.004 ↗
39. 10.1016/j.dt.2015.04.00410.1016/j.dt.2015.04.004 ↗
40. 10.1016/j.jmrt.2015.01.00710.1016/j.jmrt.2015.01.007 ↗