Study of the pitting corrosion of superduplex stainless steel and X-65 carbon steel during erosion–corrosion by cyclic polarisation technique
Source abstract
Abstract
Erosion-enhanced corrosion behaviour of X-65 carbon steel and UNS S32750 superduplex stainless steel was investigated by electrochemical cyclic polarisation. The tests were performed using a jet slurry device coupled with a potentio-galvanostat at various jet velocities of 4, 6.5 and 9 m s−1 and impingement angles of 30 and 90˚ in a 3.5 wt-% NaCl water containing 6 wt-% silica sand particles. The results showed that increasing the jet velocity and impingement angle increased the corrosion rate of both alloys. Negative hysteresis and greater Erp than OCP were observed for superduplex stainless steel in all erosion–corrosion conditions that indicated the pitting resistance of the alloy. However, the low resistance of carbon steel against pitting during erosion–corrosion was demonstrated by positive hysteresis in the cyclic polarisation curves as well as SEM images of the eroded surfaces.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Erosion and Abrasive Machining · Hydrogen embrittlement and corrosion behaviors in metals · High-Temperature Coating Behaviors
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (62)
Show source-provided references
1. 10.1016/j.corsci.2014.07.04310.1016/j.corsci.2014.07.043 ↗
2. 10.1016/j.jngse.2014.10.00110.1016/j.jngse.2014.10.001 ↗
3. 10.3103/S106836661402011110.3103/S1068366614020111 ↗
4. 10.1016/j.wear.2006.03.03310.1016/j.wear.2006.03.033 ↗
5. 10.1016/S0043-1648(99)00233-110.1016/S0043-1648(99)00233-1 ↗
6. 10.1016/j.wear.2010.11.01810.1016/j.wear.2010.11.018 ↗
7. 10.1016/j.corsci.2010.09.05910.1016/j.corsci.2010.09.059 ↗
8. Ghasemi H. M. · Int. J. Mech. Mater. Eng. · 2011 · 6 · 400
9. 10.1016/j.wear.2014.07.00810.1016/j.wear.2014.07.008 ↗
10. 10.1007/s40735-014-0001-910.1007/s40735-014-0001-9 ↗
11. 10.1016/S0010-938X(96)00066-210.1016/S0010-938X(96)00066-2 ↗
12. 10.1016/j.wear.2007.01.05310.1016/j.wear.2007.01.053 ↗
13. 10.1016/j.triboint.2010.12.01310.1016/j.triboint.2010.12.013 ↗
14. 10.1016/j.wear.2005.02.03210.1016/j.wear.2005.02.032 ↗
15. 10.1016/j.wear.2013.01.04110.1016/j.wear.2013.01.041 ↗
16. 10.1016/j.wear.2012.12.00710.1016/j.wear.2012.12.007 ↗
17. 10.1016/j.corsci.2006.08.02310.1016/j.corsci.2006.08.023 ↗
18. 10.1016/j.corsci.2006.05.01210.1016/j.corsci.2006.05.012 ↗
19. 10.1016/j.electacta.2005.04.03210.1016/j.electacta.2005.04.032 ↗
20. 10.1016/S0921-5093(00)00899-610.1016/S0921-5093(00)00899-6 ↗
21. 10.1016/j.wear.2004.09.04310.1016/j.wear.2004.09.043 ↗
22. 10.1016/j.electacta.2006.02.01810.1016/j.electacta.2006.02.018 ↗
23. 10.1361/10599490377034351010.1361/105994903770343510 ↗
24. 10.1016/j.wear.2011.01.03610.1016/j.wear.2011.01.036 ↗
25. 10.1016/S0043-1648(01)00757-810.1016/S0043-1648(01)00757-8 ↗
26. 10.1016/S0043-1648(01)00765-710.1016/S0043-1648(01)00765-7 ↗
27. 10.1016/j.wear.2010.12.06910.1016/j.wear.2010.12.069 ↗
28. 10.1016/j.wear.2013.04.01310.1016/j.wear.2013.04.013 ↗
29. 10.1016/j.wear.2009.07.02310.1016/j.wear.2009.07.023 ↗
30. 10.1016/j.vacuum.2010.10.00910.1016/j.vacuum.2010.10.009 ↗
31. 10.1016/j.wear.2004.09.03810.1016/j.wear.2004.09.038 ↗
32. 10.1016/j.wear.2007.08.00810.1016/j.wear.2007.08.008 ↗
33. 10.1016/j.corsci.2014.04.04510.1016/j.corsci.2014.04.045 ↗
34. 10.1016/j.wear.2009.01.03810.1016/j.wear.2009.01.038 ↗
35. 10.1016/j.wear.2009.06.04110.1016/j.wear.2009.06.041 ↗
36. 10.1016/j.corsci.2011.02.02810.1016/j.corsci.2011.02.028 ↗
37. 10.1016/j.electacta.2013.08.18510.1016/j.electacta.2013.08.185 ↗
38. 10.1016/j.corsci.2010.09.05410.1016/j.corsci.2010.09.054 ↗
39. 10.1016/j.corsci.2011.02.00410.1016/j.corsci.2011.02.004 ↗
40. 10.1016/j.corsci.2008.10.02610.1016/j.corsci.2008.10.026 ↗
41. 10.1007/s11249-013-0265-010.1007/s11249-013-0265-0 ↗
42. 10.1016/j.electacta.2006.07.02610.1016/j.electacta.2006.07.026 ↗
43. 10.1016/S0013-4686(01)00646-610.1016/S0013-4686(01)00646-6 ↗
44. 10.1016/S0043-1648(00)00344-610.1016/S0043-1648(00)00344-6 ↗
45. 10.1016/j.corsci.2010.05.01210.1016/j.corsci.2010.05.012 ↗
46. 10.1016/j.triboint.2010.10.00810.1016/j.triboint.2010.10.008 ↗
47. 10.1016/S0043-1648(99)00226-410.1016/S0043-1648(99)00226-4 ↗
48. 10.1016/j.corsci.2006.05.01210.1016/j.corsci.2006.05.012 ↗
49. 10.1016/S0301-679X(02)00054-310.1016/S0301-679X(02)00054-3 ↗
50. 10.1016/S0010-938X(97)00162-510.1016/S0010-938X(97)00162-5 ↗
51. 10.1016/j.electacta.2008.02.08310.1016/j.electacta.2008.02.083 ↗
52. 10.1016/j.corsci.2010.09.05410.1016/j.corsci.2010.09.054 ↗
53. 10.1016/S0010-938X(99)00100-610.1016/S0010-938X(99)00100-6 ↗
54. 10.1016/j.wear.2004.09.02310.1016/j.wear.2004.09.023 ↗
55. 10.1016/j.wear.2014.08.00610.1016/j.wear.2014.08.006 ↗
56. 10.1016/j.triboint.2009.12.02110.1016/j.triboint.2009.12.021 ↗
57. 10.1115/1.402993910.1115/1.4029939 ↗
58. 10.1007/978-1-4419-0455-310.1007/978-1-4419-0455-3 ↗
59. 10.1201/978020390913310.1201/9780203909133 ↗
60. Tait W. S. · 1994 · 63
61. Fontana M. G. · 66
62. Bardal E. · 124