High‐Cycle Fatigue Properties of Ultrafine‐Scale Cu/Ni Laminated Composites
Source abstract
Abstract
Cu/Ni laminated composites with a thickness ratio of the Cu layer to the nanocrystalline Ni layer of 1:20 are prepared by the dual‐bath electrodeposition technique. Tensile and fatigue tests are performed at room temperature. The results show that the laminated composites not only have a better synergy of the tensile strength and ductility, but also the higher fatigue strength than the pure Ni counterpart sheets. The introduction of the ultrathin Cu layer into the composite may play a key role in enhancing the ductility and the fatigue cracking resistance. The basic mechanisms for the blunting at the crack tip in the laminated composites are discussed.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Microstructure and mechanical properties · Aluminum Alloys Composites Properties · Metal Forming Simulation Techniques
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education), School of Materials Science and Engineering Northeastern University 3‐11 Wenhua Road Shenyang 110819 P. R. China
Shenyang National Laboratory for Materials Science, Institute of Metal Research Chinese Academy of Sciences 72 Wenhua Road Shenyang 110016 P. R. China
References (41)
Show source-provided references
1. 10.1016/S1359-6462(03)00393-210.1016/S1359-6462(03)00393-2 ↗
2. 10.1016/j.scriptamat.2007.04.01310.1016/j.scriptamat.2007.04.013 ↗
3. 10.1016/j.scriptamat.2005.11.05410.1016/j.scriptamat.2005.11.054 ↗
4. 10.1016/j.ijfatigue.2005.06.03510.1016/j.ijfatigue.2005.06.035 ↗
5. 10.1103/PhysRevLett.94.16550210.1103/PhysRevLett.94.165502 ↗
6. 10.1016/j.ijfatigue.2009.05.00410.1016/j.ijfatigue.2009.05.004 ↗
7. D.‐C.Baek S.‐B.Lee in11th International Conference on the Mechanical Behavior of Materials Vol.10(Eds:M.Guagliano L.Vergani) Curran Associates Inc. Red Hook NY2011. p.3006.
8. 10.1016/j.actamat.2003.12.03210.1016/j.actamat.2003.12.032 ↗
9. K.Tanaka M.Sakakibara H.Kimachi In11th International Conference on the Mechanical Behavior of Materials Vol.10(Eds:M.Guagliano L.Vergani) Curran Associates Inc. Red Hook NY2011.
10. 10.1016/j.msea.2003.12.02010.1016/j.msea.2003.12.020 ↗
11. 10.1016/j.scriptamat.2008.01.00510.1016/j.scriptamat.2008.01.005 ↗
12. 10.1016/j.actamat.2011.02.03610.1016/j.actamat.2011.02.036 ↗
13. 10.1063/1.293892110.1063/1.2938921 ↗
14. 10.1016/S1359-6462(98)00196-110.1016/S1359-6462(98)00196-1 ↗
15. 10.1016/j.tsf.2015.01.06710.1016/j.tsf.2015.01.067 ↗
16. 10.1016/j.msea.2012.09.02110.1016/j.msea.2012.09.021 ↗
17. 10.1016/j.scriptamat.2008.07.02010.1016/j.scriptamat.2008.07.020 ↗
18. 10.1016/j.surfcoat.2015.04.03910.1016/j.surfcoat.2015.04.039 ↗
19. 10.1016/j.surfcoat.2010.12.03210.1016/j.surfcoat.2010.12.032 ↗
20. 10.1016/j.matdes.2015.10.14610.1016/j.matdes.2015.10.146 ↗
21. 10.1016/S1359-6462(00)00449-810.1016/S1359-6462(00)00449-8 ↗
22. Stoudt M. R. · 2000 · 15
23. 10.1111/ffe.1232710.1111/ffe.12327 ↗
24. 10.1016/j.scriptamat.2011.08.00110.1016/j.scriptamat.2011.08.001 ↗
25. 10.1088/0022-3727/42/5/05541110.1088/0022-3727/42/5/055411 ↗
26. 10.1016/j.scriptamat.2006.01.02710.1016/j.scriptamat.2006.01.027 ↗
27. 10.1016/j.msea.2014.04.11110.1016/j.msea.2014.04.111 ↗
28. 10.1016/j.msea.2015.03.07510.1016/j.msea.2015.03.075 ↗
29. 10.1016/j.surfcoat.2007.08.06210.1016/j.surfcoat.2007.08.062 ↗
30. 10.1016/S1359-6454(97)00365-010.1016/S1359-6454(97)00365-0 ↗
31. 10.1016/S1359-6462(02)00329-910.1016/S1359-6462(02)00329-9 ↗
32. 10.1016/S1359-6462(02)00358-510.1016/S1359-6462(02)00358-5 ↗
33. 10.1073/pnas.132406911110.1073/pnas.1324069111 ↗
34. Subra S. · 1998
35. 10.1016/j.actamat.2006.03.01310.1016/j.actamat.2006.03.013 ↗
36. 10.1080/14786435.2010.53801710.1080/14786435.2010.538017 ↗
37. 10.1002/adem.20120026410.1002/adem.201200264 ↗
38. 10.1016/j.msea.2007.06.09210.1016/j.msea.2007.06.092 ↗
39. 10.1016/S1359-6454(02)00391-910.1016/S1359-6454(02)00391-9 ↗
40. 10.1016/j.materresbull.2013.10.01910.1016/j.materresbull.2013.10.019 ↗
41. 10.1016/j.jmps.2005.09.00210.1016/j.jmps.2005.09.002 ↗