Microstructure and Texture Formation During Near Conventional Forging of an Intermetallic Ti–45Al–5Nb Alloy

Abstract Texture formation was studied in an intermetallic Ti‐45at%Al‐5at%Nb alloy after uniaxial compression and near conventional forging. Depending on the deformation conditions the texture of the γ‐TiAl phase is formed by pure deformation components, components related to dynamic recrystallization, or transformation components. This changing corresponds with microstructural observations. The α₂‐Ti₃Al and the α‐Ti(Al) phase show a similar texture as it is known for Ti and Ti‐base alloys after compressive deformation at elevated temperatures. In contrast to the γ texture, no significant change of the α/α₂ texture was observed in the temperature range between 800 °C and just below the α‐transus temperature (T_α = 1295 °C).