Microstructure and Mechanical Properties of Al–12.6Si Eutectic Alloy Modified with Al–5Ti Master Alloy
Source abstract
Abstract
The Al–12.6Si eutectic alloy has been modified via the Al–5Ti master alloy to improve both microstructure and mechanical properties. The results show that the fraction of the primary α–Al phase in the Al–12.6Si alloy and the mechanical properties of the resulting alloy vary considerably after modification with the Al–5Ti master alloy at different temperatures. With increasing modification temperature, the fraction of primary α–Al in the Al–12.6Si alloy increases, varying with the amount of added Al–5Ti. For an added amount of 0.2 wt.% Al–5Ti, the fraction of primary α–Al in the Al–12.6Si alloy reaches a maximum. The tensile strength and elongation of an Al–12.6Si alloy modified with 0.2 wt.% Al–5Ti at different temperatures evidently increase compare with unmodified alloys.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Aluminum Alloy Microstructure Properties · Aluminum Alloys Composites Properties · Microstructure and mechanical properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Jiangsu Key Laboratory of Materials Surface Science and Technology School of Materials Science and Engineering Changzhou University Changzhou 213164 Jiangsu China
Jiangsu Collaborative Innovation Center of Photovoltaic Science and Engineering Changzhou University Changzhou 213164 Jiangsu China
Funding
National Natural Science Foundation of China
References (37)
Show source-provided references
1. Murray J. L. · J. Phase Equilib · 1984 · 5 · 74
2. 10.1016/j.matdes.2009.05.04210.1016/j.matdes.2009.05.042 ↗
3. 10.1016/j.jallcom.2016.08.24910.1016/j.jallcom.2016.08.249 ↗
4. 10.1016/j.jallcom.2016.11.06610.1016/j.jallcom.2016.11.066 ↗
5. 10.1016/j.jmapro.2015.01.00510.1016/j.jmapro.2015.01.005 ↗
6. 10.1002/adem.20160062310.1002/adem.201600623 ↗
7. 10.1080/1042691070119034510.1080/10426910701190345 ↗
8. 10.1134/S106378501602019X10.1134/S106378501602019X ↗
9. 10.1016/S1359-6462(97)00277-710.1016/S1359-6462(97)00277-7 ↗
10. 10.1016/j.msea.2011.02.08610.1016/j.msea.2011.02.086 ↗
11. Farahany S. · Mater. Manuf. Processes · 2013 · 28 · 657
12. 10.1080/10426914.2010.50562110.1080/10426914.2010.505621 ↗
13. 10.1016/j.jallcom.2015.11.08310.1016/j.jallcom.2015.11.083 ↗
14. 10.1016/j.msea.2012.05.08810.1016/j.msea.2012.05.088 ↗
15. 10.1016/S1003-6326(11)60878-910.1016/S1003-6326(11)60878-9 ↗
16. 10.1016/j.actamat.2016.08.04510.1016/j.actamat.2016.08.045 ↗
17. 10.1016/j.matdes.2013.10.02910.1016/j.matdes.2013.10.029 ↗
18. 10.1016/j.matchar.2011.11.00510.1016/j.matchar.2011.11.005 ↗
19. 10.1016/j.matdes.2014.07.06810.1016/j.matdes.2014.07.068 ↗
20. 10.1007/s11665-016-2139-810.1007/s11665-016-2139-8 ↗
21. 10.1016/S1003-6326(15)64035-310.1016/S1003-6326(15)64035-3 ↗
22. 10.1557/jmr.2014.11310.1557/jmr.2014.113 ↗
23. 10.1016/j.actamat.2014.10.06410.1016/j.actamat.2014.10.064 ↗
24. 10.1016/j.jallcom.2015.06.26610.1016/j.jallcom.2015.06.266 ↗
25. 10.1016/j.jallcom.2017.03.07610.1016/j.jallcom.2017.03.076 ↗
26. 10.1016/j.jallcom.2010.12.08110.1016/j.jallcom.2010.12.081 ↗
27. 10.1007/s12598-014-0378-010.1007/s12598-014-0378-0 ↗
28. 10.1016/j.scriptamat.2005.10.06710.1016/j.scriptamat.2005.10.067 ↗
29. 10.1002/adem.20050027610.1002/adem.200500276 ↗
30. 10.1179/1743284713Y.000000039210.1179/1743284713Y.0000000392 ↗
31. 10.1007/s10853-017-0923-y10.1007/s10853-017-0923-y ↗
32. 10.1016/j.jallcom.2014.06.20510.1016/j.jallcom.2014.06.205 ↗
33. 10.1016/S1003-6326(14)63340-910.1016/S1003-6326(14)63340-9 ↗
34. 10.1016/j.matdes.2016.10.06110.1016/j.matdes.2016.10.061 ↗
35. Dong G. M. · Mater. Sci. Technol · 2008 · 16 · 34
36. 10.1179/09506600122500104910.1179/095066001225001049 ↗
37. 10.3139/146.11147710.3139/146.111477 ↗