Corrosion‐Induced Strengthening: Development of High‐Strength Nanoporous Metals
Source abstract
Abstract
Replacing parts of a solid with voids usually weakens a material. Here, we report that a material (Au–Pt–Ag alloy) becomes stronger by 7 times, its strength increases from 50 to 345 MPa, when ≈40% of solids (Ag) is dissolved and replaced by pores during dealloying. The corrosion‐induced strengthening originates from the formation of nanoporous structure, and the high strength of nanoscale ligaments due to size effect. The results also suggest that the connectivity of nanoporous structure decreases during coarsening, leading to additional decreases in strength and stiffness, which may explain the unexpected low strength and stiffness of previously reported nanoporous gold.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Nanoporous metals and alloys · Anodic Oxide Films and Nanostructures · Corrosion Behavior and Inhibition
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Shenyang National Laboratory for Materials Science, Institute of Metal Research Chinese Academy of Sciences Shenyang 110016 P.R. China
References (64)
Show source-provided references
1. 10.1038/3506852910.1038/35068529 ↗
2. 10.1557/mrs2009.15710.1557/mrs2009.157 ↗
3. 10.1126/science.118359110.1126/science.1183591 ↗
4. 10.1021/ja032011910.1021/ja0320119 ↗
5. 10.1016/j.jpowsour.2006.12.00710.1016/j.jpowsour.2006.12.007 ↗
6. 10.1038/nnano.2011.1310.1038/nnano.2011.13 ↗
7. 10.1039/b910282e10.1039/b910282e ↗
8. 10.1021/nl049927d10.1021/nl049927d ↗
9. 10.1038/nmat233510.1038/nmat2335 ↗
10. 10.1021/nl903262b10.1021/nl903262b ↗
11. 10.1002/adem.20090032910.1002/adem.200900329 ↗
12. 10.1063/1.362592610.1063/1.3625926 ↗
13. 10.1126/science.120219010.1126/science.1202190 ↗
14. 10.1016/j.actamat.2014.04.06710.1016/j.actamat.2014.04.067 ↗
15. Steyskal E. M. · J. Appl. Lett · 2012 · 112 · 073703
16. 10.1126/science.109899310.1126/science.1098993 ↗
17. 10.1016/j.pmatsci.2011.01.00510.1016/j.pmatsci.2011.01.005 ↗
18. 10.1017/CBO978113987832610.1017/CBO9781139878326 ↗
19. 10.1038/nmat140310.1038/nmat1403 ↗
20. 10.1021/nl048456s10.1021/nl048456s ↗
21. 10.1016/j.actamat.2006.11.02410.1016/j.actamat.2006.11.024 ↗
22. 10.1007/BF0265853510.1007/BF02658535 ↗
23. 10.1016/S0924-0136(01)00619-710.1016/S0924-0136(01)00619-7 ↗
24. 10.1103/PhysRevLett.97.03550410.1103/PhysRevLett.97.035504 ↗
25. 10.1016/j.actamat.2009.02.01710.1016/j.actamat.2009.02.017 ↗
26. 10.1063/1.224010910.1063/1.2240109 ↗
27. 10.1021/nl061978i10.1021/nl061978i ↗
28. 10.1063/1.183274210.1063/1.1832742 ↗
29. 10.1016/j.actamat.2006.09.03810.1016/j.actamat.2006.09.038 ↗
30. 10.1088/0957-4484/17/9/04010.1088/0957-4484/17/9/040 ↗
31. 10.1016/j.scriptamat.2007.12.00810.1016/j.scriptamat.2007.12.008 ↗
32. 10.1103/PhysRevLett.68.116810.1103/PhysRevLett.68.1168 ↗
33. 10.1007/s11837-009-0176-610.1007/s11837-009-0176-6 ↗
34. 10.1016/j.actamat.2013.12.00310.1016/j.actamat.2013.12.003 ↗
35. 10.1080/14786435.2013.86894410.1080/14786435.2013.868944 ↗
36. 10.1016/j.actamat.2015.04.02110.1016/j.actamat.2015.04.021 ↗
37. 10.1063/1.277375710.1063/1.2773757 ↗
38. Corcoran S. G. · Mater. Res. Soc. Symp. Proc · 1997 · 451 · 9310.1557/PROC-451-93 ↗
39. 10.1149/2.003401jes10.1149/2.003401jes ↗
40. 10.1149/2.0131412jes10.1149/2.0131412jes ↗
41. 10.1002/adma.20070276010.1002/adma.200702760 ↗
42. 10.1021/nl803799q10.1021/nl803799q ↗
43. 10.1007/s10853-009-3731-110.1007/s10853-009-3731-1 ↗
44. 10.1016/j.scriptamat.2008.02.04610.1016/j.scriptamat.2008.02.046 ↗
45. 10.1080/1478643060056773910.1080/14786430600567739 ↗
46. 10.1016/j.actamat.2013.02.01310.1016/j.actamat.2013.02.013 ↗
47. 10.1016/j.actamat.2014.11.04010.1016/j.actamat.2014.11.040 ↗
48. 10.1016/j.actamat.2015.07.07410.1016/j.actamat.2015.07.074 ↗
49. Mameka N. · Mater. Res. Lett · 2015
50. 10.1103/PhysRevLett.106.22550410.1103/PhysRevLett.106.225504 ↗
51. 10.1063/1.328517510.1063/1.3285175 ↗
52. 10.1016/j.actamat.2012.05.01210.1016/j.actamat.2012.05.012 ↗
53. 10.1002/adem.20070017710.1002/adem.200700177 ↗
54. 10.1080/0141861850824527210.1080/01418618508245272 ↗
55. 10.1007/BF0265682110.1007/BF02656821 ↗
56. 10.5006/1.329212010.5006/1.3292120 ↗
57. 10.1007/s11661-008-9714-z10.1007/s11661-008-9714-z ↗
58. 10.1038/nmat433510.1038/nmat4335 ↗
59. 10.1016/0022-3697(87)90120-X10.1016/0022-3697(87)90120-X ↗
60. 10.1016/j.susc.2008.09.03810.1016/j.susc.2008.09.038 ↗
61. 10.1002/adma.20120374010.1002/adma.201203740 ↗
62. 10.1126/science.121164910.1126/science.1211649 ↗
63. 10.1126/science.125229110.1126/science.1252291 ↗
64. 10.1073/pnas.131514711110.1073/pnas.1315147111 ↗