High Strength Nanocrystalline Ni‐Co Alloy with Enhanced Tensile Ductility
Source abstract
Abstract
Nanocrystalline Ni‐1.7%Co alloy exhibited high ultimate tensile strength of about 1600 MPa and enhanced ductility of 8‐9.6% over a wide strain rate range of 1.04 × 10–6–1.04 s–1 revealed by tensile tests at room temperature. The typical tradeoff characteristic between yield stress and elongation to failure would make this Ni‐1.7%Co alloy for potential use in different applications.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Microstructure and mechanical properties · Surface Treatment and Residual Stress · Metal and Thin Film Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (37)
Show source-provided references
1. 10.1016/S1359-6454(99)00285-210.1016/S1359-6454(99)00285-2 ↗
2. 10.1016/j.mser.2004.07.00110.1016/j.mser.2004.07.001 ↗
3. 10.1126/science.109705810.1126/science.1097058 ↗
4. 10.1016/S0921-5107(97)00015-910.1016/S0921-5107(97)00015-9 ↗
5. 10.1016/S1359-6454(02)00421-410.1016/S1359-6454(02)00421-4 ↗
6. 10.1063/1.175619810.1063/1.1756198 ↗
7. 10.1016/j.actamat.2003.08.03210.1016/j.actamat.2003.08.032 ↗
8. 10.1016/S1359-6454(02)00198-210.1016/S1359-6454(02)00198-2 ↗
9. 10.1016/S1359-6454(03)00365-310.1016/S1359-6454(03)00365-3 ↗
10. 10.1016/j.scriptamat.2004.08.01510.1016/j.scriptamat.2004.08.015 ↗
11. 10.1038/nmat114110.1038/nmat1141 ↗
12. 10.1016/j.actamat.2003.12.02210.1016/j.actamat.2003.12.022 ↗
13. 10.1002/adem.20050009410.1002/adem.200500094 ↗
14. 10.1016/S1359-6462(03)00297-510.1016/S1359-6462(03)00297-5 ↗
15. 10.1038/nature0113310.1038/nature01133 ↗
16. 10.1016/j.scriptamat.2005.10.04110.1016/j.scriptamat.2005.10.041 ↗
17. 10.1016/S1359-6462(03)00397-X10.1016/S1359-6462(03)00397-X ↗
18. 10.1063/1.203412210.1063/1.2034122 ↗
19. 10.1016/j.apsusc.2004.08.03310.1016/j.apsusc.2004.08.033 ↗
20. 10.1016/S0040-6090(99)00315-610.1016/S0040-6090(99)00315-6 ↗
21. 10.1016/S0013-4686(99)00405-310.1016/S0013-4686(99)00405-3 ↗
22. Rosner H. · Philos Mag Lett. · 2004 · 84 · 32110.1080/09500830410001675687 ↗
23. 10.1016/j.scriptamat.2004.05.00810.1016/j.scriptamat.2004.05.008 ↗
24. 10.1016/S1359-6454(03)00237-410.1016/S1359-6454(03)00237-4 ↗
25. 10.1063/1.179923810.1063/1.1799238 ↗
26. 10.1016/j.actamat.2005.03.04710.1016/j.actamat.2005.03.047 ↗
27. 10.1016/j.actamat.2005.01.03110.1016/j.actamat.2005.01.031 ↗
28. 10.1016/j.msea.2004.03.06410.1016/j.msea.2004.03.064 ↗
29. 10.1016/j.actamat.2004.08.04510.1016/j.actamat.2004.08.045 ↗
30. 10.1179/imr.1994.39.3.11310.1179/imr.1994.39.3.113 ↗
31. 10.1016/S0921-5093(02)00729-310.1016/S0921-5093(02)00729-3 ↗
32. 10.1038/nmat103510.1038/nmat1035 ↗
33. 10.1063/1.181062910.1063/1.1810629 ↗
34. 10.1016/0038-1098(95)00506-410.1016/0038-1098(95)00506-4 ↗
35. 10.1126/science.108428410.1126/science.1084284 ↗
36. 10.1002/adem.20031008010.1002/adem.200310080 ↗
37. 10.1016/j.surfcoat.2005.07.00110.1016/j.surfcoat.2005.07.001 ↗