Effect of Mo and Cu on stress corrosion cracking of ferritic stainless steel in chloride media
Source abstract
Abstract
Stress corrosion cracking behaviour of ferritic stainless steels with copper and molybdenum additions in 42 wt-% boiling magnesium chloride at 143 ± 1°C has been determined. The nature of the corrosion products was analysed by X-ray photoelectron spectroscopy (XPS). XPS results show that the presence of Fe(0), Cr(0) and Mo(0) unoxidised states on the crack tips of (copper+molybdenum) addition ferritic stainless steel cannot form the stable passive film and causes the further corrosion in the chloride solution. The addition of both copper and molybdenum to 19% Cr ferritic stainless steel causes stress corrosion cracking. The susceptibility to stress corrosion cracking increases with the growth of ε-copper precipitates, and the fracture mode changes from transgranular to intergranular with the increasing aging time. Stress corrosion cracking initiates from pitting of ε-copper phases, then propagates to molybdenum atoms, and finally propagates to the other ε-copper precipitations perpendicular to the direction of maximum strain.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Corrosion Behavior and Inhibition · Hydrogen embrittlement and corrosion behaviors in metals · Non-Destructive Testing Techniques
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (29)
Show source-provided references
1. 10.1016/0010-938X(86)90085-510.1016/0010-938X(86)90085-5 ↗
2. 10.1016/0010-938X(87)90060-610.1016/0010-938X(87)90060-6 ↗
3. 10.1179/00070599179826937810.1179/000705991798269378 ↗
4. 10.1016/0010-938X(92)90049-910.1016/0010-938X(92)90049-9 ↗
5. 10.1002/maco.1994045090410.1002/maco.19940450904 ↗
6. 10.1016/S0010-938X(01)00008-710.1016/S0010-938X(01)00008-7 ↗
7. 10.1016/0013-4686(94)00365-810.1016/0013-4686(94)00365-8 ↗
8. 10.5006/1.329357510.5006/1.3293575 ↗
9. 10.1016/j.corsci.2004.05.02410.1016/j.corsci.2004.05.024 ↗
10. 10.1016/S0921-5093(99)00530-410.1016/S0921-5093(99)00530-4 ↗
11. 10.1016/j.corsci.2007.11.00410.1016/j.corsci.2007.11.004 ↗
12. 10.1016/S0010-938X(97)00118-210.1016/S0010-938X(97)00118-2 ↗
13. 10.1016/S0010-938X(02)00003-310.1016/S0010-938X(02)00003-3 ↗
14. C. D. Wagner, W. N. Riggs, L. E. Davies and J. F. Moulder: ‘Handbook of X-ray photoelectron spectroscopy’, (ed. G. E. Muilenberg), 1978, Eden Prairie, MN, Perkin Elmer Co., Physical Electronic Division.
15. American Society for Metals: ‘Metals handbook, vol. 8: metallography, structures and phase diagrams’; 1973, Metals Park, OH, American Society for Metals.
16. American Society for Metals: ‘ASM specialty handbook: stainless steels’; 1994, Metals Park, OH, American Society for Metals.
17. International Molybdenum Association: ‘Practical guidelines for the fabrication of duplex stainless steels’; 1999, London, UK, International Molybdenum Association.
18. 10.1016/0010-938X(95)00035-I10.1016/0010-938X(95)00035-I ↗
19. 10.1016/0010-938X(86)90022-310.1016/0010-938X(86)90022-3 ↗
20. 10.1016/0010-938X(90)90095-M10.1016/0010-938X(90)90095-M ↗
21. K. Kazior, J. Banas and I. Korozja: ‘Pasywacja spiekanych austenitycznych stali nierdzewnych’, Materialy konferencji KOROZJA 93, 269; 1993, Warszawa, Wydawnictwo ICHF PAN.
22. I. LeMay and L. M. Schetky: ‘Copper in iron and steel’; 1982, New York, John Wiley and Sons Inc.
23. A. Mazurkiewicz: ‘The influence of copper on corrosion behavior of stainless steels’, PhD thesis; 1992, Krakow, Poland, University of Mining and Metallurgy.
24. 10.1016/0010-938X(77)90032-410.1016/0010-938X(77)90032-4 ↗
25. 10.1016/0013-4686(86)80128-110.1016/0013-4686(86)80128-1 ↗
26. 10.1016/0013-4686(93)85031-S10.1016/0013-4686(93)85031-S ↗
27. 10.1016/S0013-4686(96)00321-010.1016/S0013-4686(96)00321-0 ↗
28. 10.1016/j.msea.2003.08.11210.1016/j.msea.2003.08.112 ↗
29. 10.1016/j.corsci.2011.12.03010.1016/j.corsci.2011.12.030 ↗