Phase Decomposition of a Single‐Phase AlTiVNb High‐Entropy Alloy after Severe Plastic Deformation and Annealing
Source abstract
Abstract
An equiatomic AlTiVNb high‐entropy alloy is deformed by high pressure torsion inducing a nanocrystalline microstructure. The samples then are subjected to isochronal heat treatments between 300 °C and 1000 °C. The hardness increase from ≈7.4 GPa for the as‐ processed state to 10.4 GPa for an annealing temperature of 700 °C, while for higher temperatures the hardness starts to decrease. Furthermore, the reduced modulus increases after annealing treatments as well. It will be shown that the unusual annealing response can be related to the formation of intermetallic phases creating a multi‐phase nanocomposite material during annealing. The results give new insights into the thermodynamic stability of this alloy, which are also relevant for coarser‐grained microstructures.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: High Entropy Alloys Studies · High-Temperature Coating Behaviors · Additive Manufacturing Materials and Processes
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Materials Physics Montanuniversität Leoben and Erich Schmid Institute of Materials Science Austrian Academy of Sciences A‐8700 Leoben Austria
Department of Physical Metallurgy and Materials Testing Montanuniversität Leoben A‐8700 Leoben Austria
Institute of Casting Research Montanuniversität Leoben A‐8700 Leoben Austria
References (56)
Show source-provided references
1. 10.1016/j.pmatsci.2013.10.00110.1016/j.pmatsci.2013.10.001 ↗
2. 10.3166/acsm.31.633-64810.3166/acsm.31.633-648 ↗
3. 10.1007/s11837-015-1583-510.1007/s11837-015-1583-5 ↗
4. 10.3390/e1512533810.3390/e15125338 ↗
5. 10.1080/21663831.2014.91269010.1080/21663831.2014.912690 ↗
6. 10.1016/j.msea.2003.10.25710.1016/j.msea.2003.10.257 ↗
7. 10.1016/j.intermet.2012.03.00510.1016/j.intermet.2012.03.005 ↗
8. 10.1016/j.intermet.2010.05.01410.1016/j.intermet.2010.05.014 ↗
9. 10.1016/j.intermet.2011.01.00410.1016/j.intermet.2011.01.004 ↗
10. 10.1016/j.scriptamat.2015.10.02510.1016/j.scriptamat.2015.10.025 ↗
11. 10.1016/j.actamat.2016.04.00510.1016/j.actamat.2016.04.005 ↗
12. 10.1016/j.matdes.2016.11.05510.1016/j.matdes.2016.11.055 ↗
13. 10.1016/j.msea.2012.12.01810.1016/j.msea.2012.12.018 ↗
14. 10.1007/s10853-012-6260-210.1007/s10853-012-6260-2 ↗
15. 10.3390/e1803010210.3390/e18030102 ↗
16. 10.1016/j.matlet.2014.04.06210.1016/j.matlet.2014.04.062 ↗
17. 10.1016/j.actamat.2014.01.02910.1016/j.actamat.2014.01.029 ↗
18. 10.1007/s11837-014-1066-010.1007/s11837-014-1066-0 ↗
19. 10.1016/j.matlet.2015.08.09910.1016/j.matlet.2015.08.099 ↗
20. 10.1007/s11837-013-0761-610.1007/s11837-013-0761-6 ↗
21. 10.1016/j.matlet.2014.11.16210.1016/j.matlet.2014.11.162 ↗
22. 10.1016/j.jallcom.2015.08.22410.1016/j.jallcom.2015.08.224 ↗
23. 10.1016/j.actamat.2015.06.02510.1016/j.actamat.2015.06.025 ↗
24. 10.1016/j.msea.2007.06.09310.1016/j.msea.2007.06.093 ↗
25. 10.4028/www.scientific.net/MSF.584-586.1610.4028/www.scientific.net/MSF.584-586.16 ↗
26. 10.1080/0895795960820140810.1080/08957959608201408 ↗
27. CrystalImpact http://www.crystalimpact.com/ 2016.
28. 10.1557/JMR.1992.156410.1557/JMR.1992.1564 ↗
29. 10.1557/jmr.2004.19.1.310.1557/jmr.2004.19.1.3 ↗
30. 10.1080/14786435.2014.98274110.1080/14786435.2014.982741 ↗
31. 10.1016/j.cossms.2015.02.00110.1016/j.cossms.2015.02.001 ↗
32. 10.1016/j.msea.2004.03.06410.1016/j.msea.2004.03.064 ↗
33. 10.1016/S0079-6425(99)00007-910.1016/S0079-6425(99)00007-9 ↗
34. 10.1002/3527607595.ch110.1002/3527607595.ch1 ↗
35. 10.1103/PhysRevB.86.14430210.1103/PhysRevB.86.144302 ↗
36. 10.1080/1478643090331368210.1080/14786430903313682 ↗
37. 10.3139/146.10107110.3139/146.101071 ↗
38. 10.4028/www.scientific.net/MSF.503-504.78110.4028/www.scientific.net/MSF.503-504.781 ↗
39. 10.1016/j.scriptamat.2015.05.00110.1016/j.scriptamat.2015.05.001 ↗
40. Seeger A. · Zeitschrift Fuer Met. Res. Adv. Tech · 1981 · 72 · 369
41. 10.1016/j.msea.2010.10.07310.1016/j.msea.2010.10.073 ↗
42. 10.1038/nmat167110.1038/nmat1671 ↗
43. 10.1126/science.112426810.1126/science.1124268 ↗
44. 10.1016/j.scriptamat.2014.09.02310.1016/j.scriptamat.2014.09.023 ↗
45. 10.1016/j.scriptamat.2010.07.01410.1016/j.scriptamat.2010.07.014 ↗
46. 10.1016/S0965-9773(99)00052-510.1016/S0965-9773(99)00052-5 ↗
47. 10.1016/S1359-6454(97)00092-X10.1016/S1359-6454(97)00092-X ↗
48. 10.1016/0921-5093(95)09927-110.1016/0921-5093(95)09927-1 ↗
49. 10.1016/j.actamat.2012.02.04910.1016/j.actamat.2012.02.049 ↗
50. 10.1007/s10853-006-0628-010.1007/s10853-006-0628-0 ↗
51. 10.1016/j.intermet.2012.07.00110.1016/j.intermet.2012.07.001 ↗
52. 10.1016/j.jallcom.2012.11.07410.1016/j.jallcom.2012.11.074 ↗
53. 10.1080/09506608.2016.118002010.1080/09506608.2016.1180020 ↗
54. 10.1016/j.calphad.2013.10.00610.1016/j.calphad.2013.10.006 ↗
55. 10.1016/j.matlet.2016.08.08810.1016/j.matlet.2016.08.088 ↗
56. 10.1179/1743284714Y.000000074910.1179/1743284714Y.0000000749 ↗