Preparation and Mechanical Properties of Graphene Nanosheet Reinforced Alumina Composites
Source abstract
Abstract
Dense graphene nanosheets (GNSs)/Al2O3 composites have been prepared by spark plasma sintering from ball milled expanded graphite and Al2O3 powder. GNSs have been found to be homogeneously distributed in the alumina matrix. Results show that the introduction of GNSs leads to obvious refinement of Al2O3 grains and improvement of mechanical properties of the as‐prepared composites. Compared with monolithic Al2O3, the flexural strength, fracture toughness, and Vickers hardness of as‐prepared GNSs/Al2O3 samples have been improved by 103, 25, and 26%, respectively, which are attributed to the grain refinement, strong interfacial bonding, and pull‐out of GNSs from the matrix.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Aluminum Alloys Composites Properties · Graphene research and applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
State Key Laboratory for Modification of Chemical Fibers and Polymer Materials Donghua University Shanghai 201620 China
Department of Materials Processing, Graduate School of Engineering Tohoku University Sendai 980‐8579 Japan
School of Materials and Chemical Engineering Hainan University Haikou 570228 China
References (43)
Show source-provided references
1. 10.1126/science.110289610.1126/science.1102896 ↗
2. 10.1016/j.ssc.2008.02.02410.1016/j.ssc.2008.02.024 ↗
3. 10.1021/nl073187210.1021/nl0731872 ↗
4. 10.1126/science.115799610.1126/science.1157996 ↗
5. 10.1116/1.278944610.1116/1.2789446 ↗
6. 10.1016/j.polymer.2011.02.01710.1016/j.polymer.2011.02.017 ↗
7. Kumar N. A. · ACS Nano · 2012 · 6 · 715
8. 10.1021/jp201791h10.1021/jp201791h ↗
9. 10.1021/ma900845w10.1021/ma900845w ↗
10. Uhl F. M. · Polym. Degrad. Stabil. · 2004 · 84 · 21510.1016/j.polymdegradstab.2003.10.014 ↗
11. 10.1002/pc.2219810.1002/pc.22198 ↗
12. 10.1002/app.3622410.1002/app.36224 ↗
13. 10.1016/j.carbon.2010.06.04810.1016/j.carbon.2010.06.048 ↗
14. 10.1002/app.3864510.1002/app.38645 ↗
15. 10.1007/s13726-012-0054-x10.1007/s13726-012-0054-x ↗
16. 10.1016/j.carbon.2010.01.01710.1016/j.carbon.2010.01.017 ↗
17. 10.1021/nn200319d10.1021/nn200319d ↗
18. 10.1016/j.jeurceramsoc.2012.04.02210.1016/j.jeurceramsoc.2012.04.022 ↗
19. 10.1016/j.materresbull.2010.11.00510.1016/j.materresbull.2010.11.005 ↗
20. 10.1016/j.ceramint.2013.01.04110.1016/j.ceramint.2013.01.041 ↗
21. 10.1016/j.jeurceramsoc.2013.07.00710.1016/j.jeurceramsoc.2013.07.007 ↗
22. 10.1016/j.carbon.2010.05.00310.1016/j.carbon.2010.05.003 ↗
23. 10.1021/nl803279t10.1021/nl803279t ↗
24. 10.1038/nmat216610.1038/nmat2166 ↗
25. 10.1039/C0JM02704A10.1039/C0JM02704A ↗
26. 10.1111/j.1151-2916.1972.tb11224.x10.1111/j.1151-2916.1972.tb11224.x ↗
27. 10.1007/978-3-662-04350-910.1007/978-3-662-04350-9 ↗
28. 10.1111/j.1151-2916.1976.tb10991.x10.1111/j.1151-2916.1976.tb10991.x ↗
29. 10.1016/j.carbon.2005.04.01710.1016/j.carbon.2005.04.017 ↗
30. 10.1016/S0008-6223(03)00200-810.1016/S0008-6223(03)00200-8 ↗
31. 10.1016/j.jeurceramsoc.2012.07.00310.1016/j.jeurceramsoc.2012.07.003 ↗
32. 10.1016/j.actamat.2005.03.03110.1016/j.actamat.2005.03.031 ↗
33. 10.1016/j.jeurceramsoc.2009.03.02310.1016/j.jeurceramsoc.2009.03.023 ↗
34. 10.1038/nmat116110.1038/nmat1161 ↗
35. 10.1016/j.jeurceramsoc.2009.09.03210.1016/j.jeurceramsoc.2009.09.032 ↗
36. 10.1016/j.jeurceramsoc.2009.09.03210.1016/j.jeurceramsoc.2009.09.032 ↗
37. 10.1016/S0955-2219(01)00304-110.1016/S0955-2219(01)00304-1 ↗
38. 10.1002/adem.20100001210.1002/adem.201000012 ↗
39. 10.1007/BF0123315410.1007/BF01233154 ↗
40. 10.1021/nn901047210.1021/nn9010472 ↗
41. 10.1007/BF0003708510.1007/BF00037085 ↗
42. 10.1016/j.jeurceramsoc.2010.11.00910.1016/j.jeurceramsoc.2010.11.009 ↗
43. 10.1016/j.jeurceramsoc.2013.08.03510.1016/j.jeurceramsoc.2013.08.035 ↗