Cellular Ceramics in Metal Filtration
Source abstract
Abstract
Abstract In most molten metal processing operations, the acts of melting, transporting and alloying the metal in preparation for casting into desired shapes introduces undesirable non‐metallic inclusions to the melt. Molten metals are highly reactive and tend to interact with gases and refractories during processing steps; undesirable phases are absorbed either as liquid or solid. Such examples of inclusion introduction are molten aluminum reacting with oxygen in air to form solid aluminum oxide, or molten cast iron reacting with oxygen in air to form liquid slag phases.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Advanced Manufacturing and Logistics Optimization · Innovations in Concrete and Construction Materials · Recycling and utilization of industrial and municipal waste in materials production
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (16)
Show source-provided references
1. J. E.Dore J. C.Yarwood R. K.Preuss US Patent 3 962 081 1976.
2. Cramb A. W. · Iron & Steelmaker · 1989 · 43
3. J. R. Schmahl L. S Aubrey L. C. B Martins Proc. of 4thInt. Conf. on Molten Aluminum Processing AFS Orlando FL1995.
4. D. D. Smith L. S Aubrey W. C Miller Light Metals TMS San Antonio TX1998 893–915.
5. R. Mutharasan D. Apelian C. Romanowski Light Metals TMS Chicago IL1981 735–750.
6. L. J. Gauckler M. M. Waeber C. Conti M. Jacob‐Duliere Light Metals TMS New York NY1985 1261–1283.
7. P. Netter C. Conti Light MetalsTMS New Orleans LA1986 847–860.
8. J. F. Grandfield D. W. Irwin S. Brumale C. J. Simensen C. J.Light Metals TMS Warrendale PA1990 737–746.
9. L. S. Aubrey D. D. Smith Aluminium Cast House Technology 6thAustralian Asian Pacific Conference P. R. Whiteley and J. F. Grandfield (Eds.) TMS Sydney Australia1999 133–157.
10. P. Waite Light MetalsTMS Seattle WA2002 841–848.
11. L. A.Aubrey C. L.Oliver B. T.MacPhail US Patent 5 673 902 1997.
12. W. R. Maddocks Iron Steel Inst. (London) Carnegie Schol. Mem.1935 24 64 Figure 690 inPhase Diagrams for Ceramists Volume I.
13. W. I.Hoffman R. A.OlsonIII US Patent 6 663 776 2003.10.1001/archinte.163.6.663 ↗
14. Schmahl J. R. · AFS Transactions · 1993 · 101 · 1
15. FosecoFoundry Practice2003 238 (3) 18–26.
16. Aubrey L. S. · AFS Transactions · 1993 · 101 · 59