Localised corrosion assessment of friction-stir welded AA7050-T76511 alloy: galvanic interactions and microstructural effects
Source abstract
Abstract
In this work, the localised corrosion behaviour of friction stir welded (FSW) AA7050-T76511 alloy was studied using micro-electrochemical scanning methods combined with surface characterisation. The study focused on macro galvanic interactions between the stir zone (SZ) and thermo-mechanically/heat-affected zones (TMAZ/HAZ), considering distinct initial micro-structures created by an L-bent pre-welding configuration at advancing and retreating sides. Agar-visualisation, local electrochemical impedance spectroscopy and scanning vibrating electrode technique revealed significant galvanic coupling. The TMAZ/HAZ regions behaved anodically relative to the SZ, with notably higher electrochemical activity observed at the AS. These findings demonstrate the critical influence of initial microstructural differences on corrosion susceptibility in FSW AA7050 alloys.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Advanced Welding Techniques Analysis · Welding Techniques and Residual Stresses · Aluminum Alloy Microstructure Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Departamento de Engenharia Metalúrgica e de Materiais – Escola Politécnica da Universidade de São Paulo, São Paulo, Brazil
Centro de Ciências e Tecnologia de Materiais – Instituto de Pesquisas Energéticas e Nucleares, São Paulo, Brazil
Distrito Tecnológico SENAI – SP, São Paulo, Brazil
Campus of São João da Boa Vista, São Paulo State University (UNESP), São Paulo, Brazil
Centro Nacional de Pesquisa em Energia e Materiais, Diretoria Adjunta de Tecnologia, Campinas, Brazil
Funding
Fundação de Amparo à Pesquisa do Estado de São Paulo · Coordenação de Aperfeiçoamento de Pessoal de Nível Superior · Conselho Nacional de Desenvolvimento Científico e Tecnológico
References (83)
Show source-provided references
1. 10.1016/j.mtcomm.2020.10159110.1016/j.mtcomm.2020.101591 ↗
2. ABAL. Associação Brasileira do Alumínio [Internet]. 2019 [cited 2021 Mar 9]. Available from: http://abal.org.br.
3. 10.1016/j.surfcoat.2024.13068210.1016/j.surfcoat.2024.130682 ↗
4. 10.1016/j.surfcoat.2024.13068310.1016/j.surfcoat.2024.130683 ↗
5. Birbilis N, Buchheit RG. Electrochemical characteristics of intermetallic phases in aluminum alloys an experimental survey and discussion. J Electrochem Soc [Internet] 2005; 152: B140–B151.
6. 10.3390/met903027010.3390/met9030270 ↗
7. 10.1016/j.jmst.2017.11.04110.1016/j.jmst.2017.11.041 ↗
8. 10.1179/174327806X10790510.1179/174327806X107905 ↗
9. 10.1149/2.0391713jes10.1149/2.0391713jes ↗
10. 10.1007/s10853-020-05072-w10.1007/s10853-020-05072-w ↗
11. 10.1016/j.jallcom.2016.11.38910.1016/j.jallcom.2016.11.389 ↗
12. Edermariam A. Wings of desire [Internet]. The Guardian. 2006 [cited 2021 Mar 24]. Available from: https://www.theguardian.com/business/2006/feb/23/theairlineindustry.travelnews.
13. Aeronewstv.com. A Boeing 747-8 has how many rivets? [Internet]. 2015 [cited 2021 Mar 24]. Available from: https://www.aeronewstv.com/en/lifestyle/in-your-opinion/2782-a-boeing-747-8-has-how-many-rivets.html.
14. 10.1016/j.corsci.2014.05.00110.1016/j.corsci.2014.05.001 ↗
15. 10.1016/j.engfracmech.2006.07.01010.1016/j.engfracmech.2006.07.010 ↗
16. 10.1016/j.electacta.2019.04.13710.1016/j.electacta.2019.04.137 ↗
17. 10.1016/j.pmatsci.2014.03.00310.1016/j.pmatsci.2014.03.003 ↗
18. Prabhuraj P, Rajakumar S. Experimental investigation on corrosion behavior of friction stir welded AA7075-T651 aluminium alloy under 3.5% wt NaCl environment. Mater Today Proc [Internet] 2020; 45: 3–10.
19. 10.5006/1.327755310.5006/1.3277553 ↗
20. 10.4028/www.scientific.net/MSF.396-402.167710.4028/www.scientific.net/MSF.396-402.1677 ↗
21. 10.1016/j.mser.2005.07.00110.1016/j.mser.2005.07.001 ↗
22. 10.1016/j.corsci.2005.02.02010.1016/j.corsci.2005.02.020 ↗
23. 10.1016/j.corsci.2011.07.04310.1016/j.corsci.2011.07.043 ↗
24. 10.1080/09507116.2012.70849710.1080/09507116.2012.708497 ↗
25. Paglia CS Ungaro LM Pitts BC et al. The corrosion and environmentally assisted cracking behavior of high strength aluminum alloys friction stir welds: 7075-T651 vs65–75.
26. 10.1016/j.matchar.2021.11102510.1016/j.matchar.2021.111025 ↗
27. 10.1016/j.corsci.2021.10925310.1016/j.corsci.2021.109253 ↗
28. 10.1016/j.matchar.2018.07.00410.1016/j.matchar.2018.07.004 ↗
29. 10.1016/j.jnucmat.2020.15244010.1016/j.jnucmat.2020.152440 ↗
30. 10.1016/j.electacta.2021.13791010.1016/j.electacta.2021.137910 ↗
31. 10.1016/j.jelechem.2014.06.02510.1016/j.jelechem.2014.06.025 ↗
32. The Aluminium Association. International alloy designations and chemical composition limits for wrought aluminum and wrought aluminum alloys with support for on-line access from: aluminum extruders council use of the information. Aluminum Assoc Arlington Virg 2015; 31.
33. 10.1016/j.corsci.2025.11270110.1016/j.corsci.2025.112701 ↗
34. 10.1016/j.corsci.2024.11201210.1016/j.corsci.2024.112012 ↗
35. 10.1016/j.corsci.2024.11264010.1016/j.corsci.2024.112640 ↗
36. 10.1016/j.corsci.2015.02.02910.1016/j.corsci.2015.02.029 ↗
37. Warmuzek M. Metallographic techniques for aluminum and its alloys. Metallograph Microstruct 2018; 9: 711–751.
38. Vander VG. Metallographic etching of aluminium and its alloy 1–49. [accessed 2025 Feb 7]. Available from: https://www.researchgate.net/file.PostFileLoader.html?id=56b494b57c1920b66d8b4587&assetKey=AS:325745235775488@1454675124664.
39. 10.1149/1.216837710.1149/1.2168377 ↗
40. 10.1016/j.corsci.2018.01.02810.1016/j.corsci.2018.01.028 ↗
41. 10.1016/j.corsci.2016.10.01510.1016/j.corsci.2016.10.015 ↗
42. 10.1016/j.msea.2004.09.01310.1016/j.msea.2004.09.013 ↗
43. 10.1017/S143192760488336310.1017/S1431927604883363 ↗
44. 10.1016/j.electacta.2019.04.13710.1016/j.electacta.2019.04.137 ↗
45. 10.1149/1.216837710.1149/1.2168377 ↗
46. 10.1016/j.corsci.2018.01.02810.1016/j.corsci.2018.01.028 ↗
47. 10.1016/j.corsci.2016.10.01510.1016/j.corsci.2016.10.015 ↗
48. 10.1016/j.msea.2004.09.01310.1016/j.msea.2004.09.013 ↗
49. 10.1016/S1003-6326(09)60041-810.1016/S1003-6326(09)60041-8 ↗
50. 10.1007/s11661-000-0136-910.1007/s11661-000-0136-9 ↗
51. 10.1016/S1359-6454(02)00449-410.1016/S1359-6454(02)00449-4 ↗
52. 10.1179/174328009X41113610.1179/174328009X411136 ↗
53. 10.30765/er.153310.30765/er.1533 ↗
54. 10.1016/j.jmapro.2020.11.01610.1016/j.jmapro.2020.11.016 ↗
55. 10.1016/j.scriptamat.2004.06.00210.1016/j.scriptamat.2004.06.002 ↗
56. 10.1016/0956-716X(93)90006-E10.1016/0956-716X(93)90006-E ↗
57. 10.1016/j.msea.2009.11.05710.1016/j.msea.2009.11.057 ↗
58. 10.1007/s11661-009-0152-310.1007/s11661-009-0152-3 ↗
59. 10.1016/j.actamat.2006.06.01510.1016/j.actamat.2006.06.015 ↗
60. 10.1016/j.matchar.2011.12.00510.1016/j.matchar.2011.12.005 ↗
61. 10.1023/A:102268890888510.1023/A:1022688908885 ↗
62. 10.24425/amm.2020.13173110.24425/amm.2020.131731 ↗
63. 10.1016/j.matchar.2016.11.01110.1016/j.matchar.2016.11.011 ↗
64. 10.1016/j.matchemphys.2018.08.05310.1016/j.matchemphys.2018.08.053 ↗
65. Pérez H, Tufaro L, Berardo L, et al. Corrosion behavior of friction stir welds on aa7075-T651:Galvanic evaluation. Revista Materia 2018; 23.
66. 10.1590/1980-5373-mr-2020-016110.1590/1980-5373-mr-2020-0161 ↗
67. 10.5006/1.329438610.5006/1.3294386 ↗
68. 10.1016/j.corsci.2010.09.00910.1016/j.corsci.2010.09.009 ↗
69. 10.1016/j.corsci.2010.09.03010.1016/j.corsci.2010.09.030 ↗
70. 10.1016/j.corsci.2010.09.03510.1016/j.corsci.2010.09.035 ↗
71. 10.1016/j.mtcomm.2020.10159110.1016/j.mtcomm.2020.101591 ↗
72. 10.1016/S1003-6326(15)63782-710.1016/S1003-6326(15)63782-7 ↗
73. 10.5006/1.328395010.5006/1.3283950 ↗
74. 10.1016/j.corsci.2024.11234510.1016/j.corsci.2024.112345 ↗
75. 10.1002/maco.20070406310.1002/maco.200704063 ↗
76. 10.1016/j.jmrt.2023.05.05310.1016/j.jmrt.2023.05.053 ↗
77. 10.1007/BF0266740410.1007/BF02667404 ↗
78. 10.1007/BF0266740310.1007/BF02667403 ↗
79. 10.1016/j.matchar.2016.11.01110.1016/j.matchar.2016.11.011 ↗
80. 10.1179/174328009X41113610.1179/174328009X411136 ↗
81. 10.1016/j.jmst.2019.11.01610.1016/j.jmst.2019.11.016 ↗
82. da Silva R, Milagre M, Araujo JV, et al. Investigação da atividade eletroquímica de liga Al-Cu-Li após processo de soldagem por fricção e mistura. Quim Nova [Internet] 2023; X: 1–12.
83. 10.1016/j.mtla.2025.10236310.1016/j.mtla.2025.102363 ↗