Mechanical Properties of Nanocrystalline and Ultrafine‐Grained Nickel with Bimodal Microstructure
Source abstract
Abstract
The aim of this work was to use bimodal microstructures to improve ductility and fatigue resistance of nanocrystalline (NC) and ultrafine‐grained (UFG) materials while keeping the materials’ high strength. Nickel plates produced by pulsed electrodeposition were used as NC base material while as UFG base material high‐purity nickel was processed by equal channel angular pressing. After different heat treatments, bimodal microstructures could be realized in the size ranges of NC/UFG and UFG/coarse grained (CG). While the UFG/CG nickel revealed an improved ductility but little influence on the fatigue resistance, the NC/UFG nickel shows an extraordinary fatigue resistance.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Microstructure and mechanical properties · Metal and Thin Film Mechanics · Aluminum Alloys Composites Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Materials Science and Engineering Saarland University 66123 Saarbrücken Germany
Department of Materials Science and Engineering Texas A&M University College Station TX 77843 USA
References (48)
Show source-provided references
1. 10.1016/j.pmatsci.2005.08.00310.1016/j.pmatsci.2005.08.003 ↗
2. 10.1016/j.pmatsci.2006.02.00310.1016/j.pmatsci.2006.02.003 ↗
3. 10.1016/j.actamat.2003.12.02210.1016/j.actamat.2003.12.022 ↗
4. 10.1016/j.actamat.2009.11.05310.1016/j.actamat.2009.11.053 ↗
5. 10.1016/S1359-6462(03)00394-410.1016/S1359-6462(03)00394-4 ↗
6. 10.4028/www.scientific.net/JMNM.18.910.4028/www.scientific.net/JMNM.18.9 ↗
7. 10.1016/S1359-6462(03)00396-810.1016/S1359-6462(03)00396-8 ↗
8. 10.1016/S0079-6425(99)00007-910.1016/S0079-6425(99)00007-9 ↗
9. 10.1063/1.177934210.1063/1.1779342 ↗
10. 10.1002/adem.20050009410.1002/adem.200500094 ↗
11. 10.1038/nature0113310.1038/nature01133 ↗
12. 10.1002/adma.20080021410.1002/adma.200800214 ↗
13. 10.1002/adem.20110001910.1002/adem.201100019 ↗
14. 10.1007/s11661-001-0207-610.1007/s11661-001-0207-6 ↗
15. 10.1016/j.msea.2005.08.10410.1016/j.msea.2005.08.104 ↗
16. 10.1179/174328408X36151710.1179/174328408X361517 ↗
17. 10.1016/j.scriptamat.2012.07.00310.1016/j.scriptamat.2012.07.003 ↗
18. 10.1016/j.scriptamat.2010.08.00510.1016/j.scriptamat.2010.08.005 ↗
19. 10.1016/j.actamat.2012.11.00910.1016/j.actamat.2012.11.009 ↗
20. 10.1016/j.scriptamat.2009.11.02210.1016/j.scriptamat.2009.11.022 ↗
21. 10.2320/matertrans.M201027910.2320/matertrans.M2010279 ↗
22. 10.1016/j.matlet.2011.05.00210.1016/j.matlet.2011.05.002 ↗
23. 10.1016/j.msea.2010.10.10910.1016/j.msea.2010.10.109 ↗
24. 10.1179/1743284712Y.000000001610.1179/1743284712Y.0000000016 ↗
25. 10.1080/14786435.2012.70734110.1080/14786435.2012.707341 ↗
26. 10.1016/j.actamat.2011.02.02910.1016/j.actamat.2011.02.029 ↗
27. 10.1007/s11661-011-0708-x10.1007/s11661-011-0708-x ↗
28. 10.1002/adem.20100005910.1002/adem.201000059 ↗
29. 10.1557/mrc.2013.4010.1557/mrc.2013.40 ↗
30. 10.1023/A:101793241704310.1023/A:1017932417043 ↗
31. 10.1016/j.actamat.2013.03.00810.1016/j.actamat.2013.03.008 ↗
32. 10.1016/j.actamat.2010.11.05110.1016/j.actamat.2010.11.051 ↗
33. 10.1016/j.actamat.2012.01.01310.1016/j.actamat.2012.01.013 ↗
34. 10.1080/1478643100377680210.1080/14786431003776802 ↗
35. 10.1016/j.msea.2008.02.01510.1016/j.msea.2008.02.015 ↗
36. 10.1016/S0965-9773(99)00050-110.1016/S0965-9773(99)00050-1 ↗
37. 10.1016/S1359-6454(02)00198-210.1016/S1359-6454(02)00198-2 ↗
38. 10.1016/j.msea.2011.08.06110.1016/j.msea.2011.08.061 ↗
39. 10.1007/s11661-005-0289-710.1007/s11661-005-0289-7 ↗
40. 10.1007/BF0258621410.1007/BF02586214 ↗
41. 10.1016/j.msea.2006.12.12710.1016/j.msea.2006.12.127 ↗
42. 10.1016/S1359-6454(97)00070-010.1016/S1359-6454(97)00070-0 ↗
43. Humphreys F. · 2004
44. 10.1016/0502-8205(52)90009-910.1016/0502-8205(52)90009-9 ↗
45. 10.4028/www.scientific.net/MSF.558-559.3310.4028/www.scientific.net/MSF.558-559.33 ↗
46. Klement U. · Mater. Sci. Forum · 2012 · 702 · 928
47. 10.1016/S1359-6462(03)00393-210.1016/S1359-6462(03)00393-2 ↗
48. 10.1016/j.ijfatigue.2005.06.03510.1016/j.ijfatigue.2005.06.035 ↗