Correlating Strength and Hardness of High‐Entropy Alloys
Source abstract
Abstract
Strength and hardness of metallic materials are reported to correlate in a specified form. Among various equations, yield strength is generally converted from Vickers hardness (HV) via a three‐time relation due to the simple and nondestructive nature of hardness testing. Herein, a through literature review is made and data of strength and HV for face‐centered cubic (FCC) and body‐centered cubic (BCC) high‐entropy alloys (HEA) are collected. The yield strength and HV visibly deviate from the three‐time relation, but the ultimate tensile strength and HV roughly follow the three‐time relation. New linear relationships, which are universally applied to convert HV to yield strength and ultimate tensile strength, are proposed.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: High Entropy Alloys Studies · High-Temperature Coating Behaviors · Metal and Thin Film Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education) School of Materials Science and Engineering Northeastern University Shenyang 110819 China
State Key Laboratory of Rolling and Automation Northeastern University Shenyang 110819 China
School of Materials Science and Engineering Shenyang Ligong University Shenyang 110159 China
Research Center for Metallic Wires Northeastern University Shenyang 110819 China
Funding
National Natural Science Foundation of China
References (100+)
Show source-provided references
1. 10.1016/j.msea.2015.02.04910.1016/j.msea.2015.02.049 ↗
2. 10.1016/j.jnucmat.2004.09.02410.1016/j.jnucmat.2004.09.024 ↗
3. 10.1016/j.jnucmat.2006.09.00510.1016/j.jnucmat.2006.09.005 ↗
4. 10.1007/s11665-008-9225-510.1007/s11665-008-9225-5 ↗
5. 10.1016/j.nme.2016.08.00710.1016/j.nme.2016.08.007 ↗
6. 10.1016/j.msea.2017.03.10210.1016/j.msea.2017.03.102 ↗
7. 10.1088/1757-899X/338/1/01201110.1088/1757-899X/338/1/012011 ↗
8. 10.1016/j.ijpvp.2019.03.02510.1016/j.ijpvp.2019.03.025 ↗
9. Cahoon J. R. · Metall. Trans. · 1971 · 2 · 197910.1007/BF02913433 ↗
10. 10.1007/BF0265288010.1007/BF02652880 ↗
11. 10.1016/j.msea.2011.08.06110.1016/j.msea.2011.08.061 ↗
12. Meyers M. A. · 2013 · 162
13. Tabor D. · J. Inst. Metals · 1951 · 79 · 1
14. 10.1016/j.jmst.2020.06.01810.1016/j.jmst.2020.06.018 ↗
15. 10.1126/science.abb683010.1126/science.abb6830 ↗
16. 10.1016/j.actamat.2019.12.01510.1016/j.actamat.2019.12.015 ↗
17. 10.1016/j.scriptamat.2020.06.02210.1016/j.scriptamat.2020.06.022 ↗
18. 10.1038/s41586-018-0685-y10.1038/s41586-018-0685-y ↗
19. 10.1126/science.125458110.1126/science.1254581 ↗
20. 10.1016/j.msea.2003.10.25710.1016/j.msea.2003.10.257 ↗
21. 10.1016/j.jmst.2018.09.06810.1016/j.jmst.2018.09.068 ↗
22. 10.1016/j.mtnano.2018.12.00210.1016/j.mtnano.2018.12.002 ↗
23. 10.2320/matertrans.MT-MK201900410.2320/matertrans.MT-MK2019004 ↗
24. 10.1016/j.jmst.2020.04.06210.1016/j.jmst.2020.04.062 ↗
25. 10.1016/j.scriptamat.2019.01.01610.1016/j.scriptamat.2019.01.016 ↗
26. 10.1016/j.mtla.2018.10.01510.1016/j.mtla.2018.10.015 ↗
27. 10.1039/C8NR03573C10.1039/C8NR03573C ↗
28. 10.1016/j.msea.2017.09.08910.1016/j.msea.2017.09.089 ↗
29. 10.1007/s40195-020-01045-910.1007/s40195-020-01045-9 ↗
30. 10.1016/j.actamat.2018.03.06510.1016/j.actamat.2018.03.065 ↗
31. 10.2320/matertrans.MF20193610.2320/matertrans.MF201936 ↗
32. 10.1016/j.mser.2018.06.00110.1016/j.mser.2018.06.001 ↗
33. 10.1016/j.jmst.2019.12.02310.1016/j.jmst.2019.12.023 ↗
34. 10.1016/j.msea.2020.14039810.1016/j.msea.2020.140398 ↗
35. 10.1016/j.msea.2016.08.11810.1016/j.msea.2016.08.118 ↗
36. 10.1016/j.matdes.2018.10757610.1016/j.matdes.2018.107576 ↗
37. 10.1016/j.jallcom.2019.01.21310.1016/j.jallcom.2019.01.213 ↗
38. 10.1016/j.scriptamat.2018.11.04210.1016/j.scriptamat.2018.11.042 ↗
39. 10.1016/j.msea.2018.01.04510.1016/j.msea.2018.01.045 ↗
40. 10.1016/j.matchar.2018.09.02910.1016/j.matchar.2018.09.029 ↗
41. 10.1016/j.actamat.2018.02.04810.1016/j.actamat.2018.02.048 ↗
42. 10.1016/j.matdes.2017.07.05410.1016/j.matdes.2017.07.054 ↗
43. 10.1016/j.msea.2017.02.06810.1016/j.msea.2017.02.068 ↗
44. 10.1016/j.intermet.2016.09.00310.1016/j.intermet.2016.09.003 ↗
45. 10.1016/j.msea.2015.03.10910.1016/j.msea.2015.03.109 ↗
46. 10.1016/j.actamat.2015.06.02510.1016/j.actamat.2015.06.025 ↗
47. 10.1016/j.actamat.2013.09.03710.1016/j.actamat.2013.09.037 ↗
48. 10.1016/j.jallcom.2013.12.21010.1016/j.jallcom.2013.12.210 ↗
49. 10.1016/j.addma.2020.10120210.1016/j.addma.2020.101202 ↗
50. 10.1016/j.msea.2018.11.14310.1016/j.msea.2018.11.143 ↗
51. 10.1016/j.actamat.2018.12.01510.1016/j.actamat.2018.12.015 ↗
52. 10.1016/j.msea.2017.06.08610.1016/j.msea.2017.06.086 ↗
53. 10.1016/j.wear.2020.20336810.1016/j.wear.2020.203368 ↗
54. 10.1016/j.jallcom.2020.15415910.1016/j.jallcom.2020.154159 ↗
55. 10.1016/j.jallcom.2019.15327310.1016/j.jallcom.2019.153273 ↗
56. 10.1016/j.jallcom.2020.15599710.1016/j.jallcom.2020.155997 ↗
57. H.Zhou Master Thesis Southeast University2018.
58. 10.1016/j.scriptamat.2014.11.03710.1016/j.scriptamat.2014.11.037 ↗
59. 10.1016/j.msea.2019.05.02810.1016/j.msea.2019.05.028 ↗
60. 10.1016/j.jallcom.2018.09.39010.1016/j.jallcom.2018.09.390 ↗
61. 10.3390/ma1109155710.3390/ma11091557 ↗
62. 10.1007/s11661-018-4607-210.1007/s11661-018-4607-2 ↗
63. 10.1007/s10853-018-2322-410.1007/s10853-018-2322-4 ↗
64. Bartolomeu F. · Addit. Manuf. · 2017 · 16 · 81
65. 10.1016/j.msea.2012.07.08910.1016/j.msea.2012.07.089 ↗
66. 10.1016/j.scriptamat.2005.01.02310.1016/j.scriptamat.2005.01.023 ↗
67. 10.1016/j.intermet.2019.10667310.1016/j.intermet.2019.106673 ↗
68. 10.1016/j.actamat.2011.01.01710.1016/j.actamat.2011.01.017 ↗
69. 10.1016/j.intermet.2011.03.02610.1016/j.intermet.2011.03.026 ↗
70. 10.1016/j.actamat.2016.03.01510.1016/j.actamat.2016.03.015 ↗
71. Bektes M. · Chin. J. Phys. · 2004 · 42 · 733
72. 10.1007/s11249-016-0805-510.1007/s11249-016-0805-5 ↗
73. Vander Voort G. F. · Adv. Mater. Process. · 2012 · 170 · 28
74. 10.1080/10426914.2020.180204510.1080/10426914.2020.1802045 ↗
75. 10.1002/adem.20170094610.1002/adem.201700946 ↗
76. 10.1007/s13239-016-0286-610.1007/s13239-016-0286-6 ↗
77. 10.1016/j.msea.2016.12.11010.1016/j.msea.2016.12.110 ↗
78. 10.1007/s11837-015-1385-910.1007/s11837-015-1385-9 ↗
79. 10.1080/21663831.2014.95858610.1080/21663831.2014.958586 ↗
80. 10.1016/j.msea.2020.13944610.1016/j.msea.2020.139446 ↗
81. 10.1016/j.msea.2019.13868110.1016/j.msea.2019.138681 ↗
82. 10.1016/j.msea.2019.03.08810.1016/j.msea.2019.03.088 ↗
83. 10.1016/j.matdes.2017.02.07210.1016/j.matdes.2017.02.072 ↗
84. Huang Y. · Mater. Mech. Eng. · 2015 · 39 · 51
85. 10.1016/j.matdes.2018.07.04610.1016/j.matdes.2018.07.046 ↗
86. 10.1016/j.msea.2016.01.06510.1016/j.msea.2016.01.065 ↗
87. 10.3390/met1008101710.3390/met10081017 ↗
88. 10.1007/s12613-020-2040-110.1007/s12613-020-2040-1 ↗
89. 10.1016/j.jallcom.2019.15335210.1016/j.jallcom.2019.153352 ↗
90. 10.1016/j.jallcom.2018.10.23010.1016/j.jallcom.2018.10.230 ↗
91. 10.1016/j.jallcom.2016.11.18810.1016/j.jallcom.2016.11.188 ↗
92. 10.3390/e1805018910.3390/e18050189 ↗
93. 10.1016/j.actamat.2016.01.01810.1016/j.actamat.2016.01.018 ↗
94. 10.1016/j.msea.2016.07.10210.1016/j.msea.2016.07.102 ↗
95. 10.1016/j.intermet.2015.03.01310.1016/j.intermet.2015.03.013 ↗
96. 10.1016/j.matlet.2014.11.16210.1016/j.matlet.2014.11.162 ↗
97. 10.1016/j.jallcom.2014.11.06410.1016/j.jallcom.2014.11.064 ↗
98. 10.1016/j.jmmm.2014.07.02310.1016/j.jmmm.2014.07.023 ↗
99. 10.1016/j.jallcom.2014.06.09010.1016/j.jallcom.2014.06.090 ↗
100. 10.1016/j.msea.2012.12.01810.1016/j.msea.2012.12.018 ↗