Twist Extrusion as a Potent Tool for Obtaining Advanced Engineering Materials: A Review
Source abstract
Abstract
Twist extrusion (TE) is one of the most popular techniques of severe plastic deformation, aiming at imparting to a material a tailored microstructure and the associated property improvement. The article provides a survey of the literature on the mechanics of TE and the effect it has on the structure, texture, and the attendant properties of various materials, including metals and alloys, powder materials, and polymers. Special emphasis is placed on vortex flow during TE and its hitherto unexplored potential for producing micro‐ and macrostructures that promise superior properties of the materials. In particular, the possibility of creating novel hybrid materials with chiral inner architecture is demonstrated. The survey is concluded by a presentation of examples of practical applications of TE.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Microstructure and mechanical properties · Metallurgy and Material Forming · Metal Forming Simulation Techniques
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Donetsk Institute for Physics and Engineering named after A.A. Galkin National Academy of Sciences of Ukraine pr. Nauki 46, Kyiv 03028 Ukraine
Laboratory of Excellence for Design of Metal Alloys for Light Structures (DAMAS) Université de Lorraine Île du Saulcy Metz cedex 01, F‐57045 France
Institute of Nanotechnology (INT), Karlsruhe Institute of Technology (KIT) Hermann‐von‐Helmholtz‐Platz 1, Eggenstein‐Leopoldshafen 76344 Germany
Centre for Advanced Hybrid Materials, Department of Materials Science and Engineering Monash University Clayton VIC 3800 Australia
Laboratory of Hybrid Nanostructured Materials NUST MISIS Leninsky prospect 4 Moscow 119490 Russia
Laboratory of Excellence for Design of Alloy Metals for low‐Mass Structures (DAMAS) Université de Lorraine, Île du Saulcy Metz cedex 01, F‐57045 France
Laboratoire d'Etude des Microstructures et de Mécanique des Matériaux ('LEM3') UMR 7239, CNRS / Université de Lorraine F‐57045 Metz France
Center for Advanced Aerospace Materials, POSTECH Pohang, 790–784 Republic of Korea
Department of Materials Science and Engineering POSTECH Pohang, 790–784 Republic of Korea
GT‐CNRS UMI 2958 Georgia Tech Lorraine Metz, 57070 France
References (100+)
Show source-provided references
1. 10.1007/s11837-006-0213-710.1007/s11837-006-0213-7 ↗
2. 10.1007/s11837-016-1820-610.1007/s11837-016-1820-6 ↗
3. 10.1016/j.actamat.2012.10.03810.1016/j.actamat.2012.10.038 ↗
4. 10.1007/s11431-012-4954-y10.1007/s11431-012-4954-y ↗
5. 10.1016/j.cirp.2008.09.00510.1016/j.cirp.2008.09.005 ↗
6. 10.1016/0921-5093(95)09705-810.1016/0921-5093(95)09705-8 ↗
7. 10.1016/j.pmatsci.2006.02.00310.1016/j.pmatsci.2006.02.003 ↗
8. Bridgman P. W. · Phys. Rev · 1935 · 48 · 15
9. 10.1016/j.pmatsci.2008.03.00210.1016/j.pmatsci.2008.03.002 ↗
10. 10.1016/S1359-6454(98)00365-610.1016/S1359-6454(98)00365-6 ↗
11. Galeyev R. M. · Russ. Metall · 1990 · 4 · 97
12. 10.4131/jshpreview.9.10910.4131/jshpreview.9.109 ↗
13. Beygelzimer Y. · 2002 · 297
14. Beygelzimer Y. · 2002 · 43
15. 10.1007/s11665-015-1731-710.1007/s11665-015-1731-7 ↗
16. 10.1016/S1003-6326(15)63823-710.1016/S1003-6326(15)63823-7 ↗
17. Li Y. · Adv. Energy Sci. Technol · 2013 · 2676
18. Li W. · 2013 · 2218
19. 10.1016/j.matdes.2012.07.04710.1016/j.matdes.2012.07.047 ↗
20. 10.1016/j.msea.2012.03.05510.1016/j.msea.2012.03.055 ↗
21. 10.2478/amm-2014-006010.2478/amm-2014-0060 ↗
22. Boehm R. · 2005
23. 10.1002/adem.20150008310.1002/adem.201500083 ↗
24. 10.1080/21663831.2015.103481210.1080/21663831.2015.1034812 ↗
25. 10.1007/s11661-015-3298-110.1007/s11661-015-3298-1 ↗
26. 10.1016/j.matlet.2015.07.00810.1016/j.matlet.2015.07.008 ↗
27. 10.1016/j.measurement.2016.07.08510.1016/j.measurement.2016.07.085 ↗
28. 10.1177/095440541351960610.1177/0954405413519606 ↗
29. Kumar V. S. S. · 2013
30. Sahai A. · 2013 · 283
31. Raj K. H. · 2010 · 507
32. 10.1007/s10845-014-0879-610.1007/s10845-014-0879-6 ↗
33. 10.1016/j.apm.2015.09.07410.1016/j.apm.2015.09.074 ↗
34. 10.1016/j.msea.2015.11.05610.1016/j.msea.2015.11.056 ↗
35. 10.1016/j.matdes.2015.06.03410.1016/j.matdes.2015.06.034 ↗
36. 10.1016/j.matlet.2015.03.06310.1016/j.matlet.2015.03.063 ↗
37. 10.1016/j.jallcom.2014.08.03110.1016/j.jallcom.2014.08.031 ↗
38. 10.1007/s12540-014-5005-y10.1007/s12540-014-5005-y ↗
39. 10.1007/s11661-013-2165-110.1007/s11661-013-2165-1 ↗
40. 10.1007/s11665-012-0323-z10.1007/s11665-012-0323-z ↗
41. 10.1007/s11837-012-0305-510.1007/s11837-012-0305-5 ↗
42. 10.1016/j.matdes.2011.12.00910.1016/j.matdes.2011.12.009 ↗
43. 10.1016/j.msea.2011.04.09210.1016/j.msea.2011.04.092 ↗
44. 10.1007/s11837-011-0094-210.1007/s11837-011-0094-2 ↗
45. 10.1016/j.msea.2010.10.00710.1016/j.msea.2010.10.007 ↗
46. 10.4028/www.scientific.net/AMR.264-265.18310.4028/www.scientific.net/AMR.264-265.183 ↗
47. Bahadori S. R. · J. Phys · 2010 · 240 · 012132
48. Salehi M. S. · Proc. IMechE C · 2009 · 223 · 197510.1243/09544062JMES1318 ↗
49. 10.1142/S021797920804768710.1142/S0217979208047687 ↗
50. 10.1016/j.matdes.2007.07.00910.1016/j.matdes.2007.07.009 ↗
51. 10.2320/matertrans.MD20111310.2320/matertrans.MD201113 ↗
52. 10.1016/j.msea.2009.06.00510.1016/j.msea.2009.06.005 ↗
53. 10.2320/matertrans.MD20080210.2320/matertrans.MD200802 ↗
54. 10.4028/www.scientific.net/MSF.604-605.17110.4028/www.scientific.net/MSF.604-605.171 ↗
55. 10.2320/matertrans.ME20072410.2320/matertrans.ME200724 ↗
56. 10.1007/s12540-015-4577-510.1007/s12540-015-4577-5 ↗
57. 10.1007/s12540-015-4387-910.1007/s12540-015-4387-9 ↗
58. 10.1007/s11661-013-1661-710.1007/s11661-013-1661-7 ↗
59. 10.2320/matertrans.MH20131510.2320/matertrans.MH201315 ↗
60. 10.1016/j.commatsci.2012.03.03510.1016/j.commatsci.2012.03.035 ↗
61. 10.1680/emr.14.0001610.1680/emr.14.00016 ↗
62. 10.1680/emr.12.0003810.1680/emr.12.00038 ↗
63. 10.1016/j.msea.2010.11.02610.1016/j.msea.2010.11.026 ↗
64. Stolyarov V. V. · Phys. Met. Metallogr · 2005 · 99 · 204
65. Orlov D. · 2003
66. Kulagin R. · 2014
67. Beygelzimer Y. · 2017 · 202
68. Varyukhin V. · MFiNT · 2012 · 34 · 1655
69. 10.1007/s11015-014-9883-510.1007/s11015-014-9883-5 ↗
70. Usov V. · Phys. Technol. High Pressures · 2011 · 21 · 103
71. Usov V. · Phys. Technol. High Pressures · 2011 · 3 · 102
72. Shkatulyak N. · Int. J. Adv. Mater. Sci. Eng · 2014 · 3 · 15
73. Subramanian P. R. · US Patent 20080145691 A1 · 2008
74. 10.1016/S1359-6454(03)00441-510.1016/S1359-6454(03)00441-5 ↗
75. 10.1063/1.332308710.1063/1.3323087 ↗
76. Poston T. · 2012
77. 10.1016/0026-0800(87)90027-910.1016/0026-0800(87)90027-9 ↗
78. Segal V. · US Patents 20050081594 A1 · 2004
79. 10.1016/S0924-0136(02)01033-610.1016/S0924-0136(02)01033-6 ↗
80. 10.1016/j.msea.2014.06.07910.1016/j.msea.2014.06.079 ↗
81. 10.1016/j.msea.2016.04.00810.1016/j.msea.2016.04.008 ↗
82. Segal V. M. · US7096705 B2 · 2006
83. 10.1016/j.mechmat.2011.07.00910.1016/j.mechmat.2011.07.009 ↗
84. Beygelzimer Y. · Phys. Technol. High Pressures · 2007 · 17 · 100
85. 10.1016/j.jmatprotec.2010.11.00610.1016/j.jmatprotec.2010.11.006 ↗
86. 10.1016/j.msea.2009.08.05110.1016/j.msea.2009.08.051 ↗
87. 10.1016/j.scriptamat.2008.09.02910.1016/j.scriptamat.2008.09.029 ↗
88. 10.1002/adem.20090021710.1002/adem.200900217 ↗
89. Beygelzimer Y. · Phys. Technol. High Pressures · 2000 · 10 · 24
90. Y.Beygelzimer V.Varyukhin R.Kulagin O.Prokof'eva A.Reshetov Proc. 10th Int. Conf. Technol. Plast.Stahleisen GmbH Düsseldorf Germany 2011 p. 244.
91. 10.1016/j.msea.2007.12.05510.1016/j.msea.2007.12.055 ↗
92. 10.1016/j.matdes.2013.03.06610.1016/j.matdes.2013.03.066 ↗
93. 10.1016/j.jmatprotec.2008.08.02210.1016/j.jmatprotec.2008.08.022 ↗
94. 10.1016/j.msea.2010.02.07710.1016/j.msea.2010.02.077 ↗
95. 10.4028/www.scientific.net/DDF.208-209.31110.4028/www.scientific.net/DDF.208-209.311 ↗
96. 10.1115/1.403307110.1115/1.4033071 ↗
97. 10.1017/CBO978051180095510.1017/CBO9780511800955 ↗
98. 10.1093/oso/9780198503675.001.000110.1093/oso/9780198503675.001.0001 ↗
99. 10.1016/j.msea.2012.04.05310.1016/j.msea.2012.04.053 ↗
100. Beygelzimer Y. · 2003