Designing Ultrahigh Strength Steels with Good Ductility by Combining Transformation Induced Plasticity and Martensite Aging
Source abstract
Abstract
We present results on precipitation hardened ductile high strength maraging-TRIP steels with up to 1.5 GPa strength and good ductility. The alloys have low carbon content (0.01 wt% C), 9–15 wt% Mn, and additions of Ni, Ti, and Mo (1–2 wt%) for precipitation. Martensite aging leads to a surprising simultaneous increase in strength and total elongation for samples with 9 wt% Mn and 12 wt% Mn.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Microstructure and Mechanical Properties of Steels · Microstructure and mechanical properties · Fusion materials and technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (39)
Show source-provided references
1. 10.1016/j.scriptamat.2008.07.02010.1016/j.scriptamat.2008.07.020 ↗
2. 10.1016/j.scriptamat.2008.07.02010.1016/j.scriptamat.2008.07.020 ↗
3. 10.1016/0001-6160(53)90083-210.1016/0001-6160(53)90083-2 ↗
4. 10.1007/BF0265830910.1007/BF02658309 ↗
5. Olson G. B. · 1986 · 367
6. 10.2320/matertrans1989.32.68910.2320/matertrans1989.32.689 ↗
7. 10.1016/S0921-5093(99)00331-710.1016/S0921-5093(99)00331-7 ↗
8. 10.2355/isijinternational.39.81310.2355/isijinternational.39.813 ↗
9. 10.1002/srin.20020020610.1002/srin.200200206 ↗
10. 10.1016/j.cossms.2004.09.00610.1016/j.cossms.2004.09.006 ↗
11. 10.1016/j.actamat.2004.02.04410.1016/j.actamat.2004.02.044 ↗
12. Decker R. F. · Trans. ASM · 1962 · 55 · 58
13. Decker R. F. · 1979
14. 10.1007/BF0266819310.1007/BF02668193 ↗
15. 10.1007/BF0264606110.1007/BF02646061 ↗
16. 10.1016/0001-6160(88)90123-X10.1016/0001-6160(88)90123-X ↗
17. 10.1016/S1359-6454(99)00370-510.1016/S1359-6454(99)00370-5 ↗
18. Goldman A. J. · Trans. ASM · 1965 · 58 · 645
19. 10.1016/0036-9748(76)90110-110.1016/0036-9748(76)90110-1 ↗
20. 10.1016/j.actamat.2008.09.02510.1016/j.actamat.2008.09.025 ↗
21. 10.1146/annurev.matsci.38.060407.13031510.1146/annurev.matsci.38.060407.130315 ↗
22. 10.2320/matertrans.47.150810.2320/matertrans.47.1508 ↗
23. 10.1080/0950083041233130360910.1080/09500830412331303609 ↗
24. 10.1038/nature0174010.1038/nature01740 ↗
25. 10.1016/j.micron.2005.10.00910.1016/j.micron.2005.10.009 ↗
26. 10.1016/S0921-5093(01)00923-610.1016/S0921-5093(01)00923-6 ↗
27. 10.1016/j.actamat.2004.01.02410.1016/j.actamat.2004.01.024 ↗
28. 10.3139/146.01798310.3139/146.017983 ↗
29. 10.3139/146.01806010.3139/146.018060 ↗
30. 10.1016/j.actamat.2004.10.05110.1016/j.actamat.2004.10.051 ↗
31. 10.1016/j.scriptamat.2005.02.01610.1016/j.scriptamat.2005.02.016 ↗
32. 10.2355/isijinternational.45.172110.2355/isijinternational.45.1721 ↗
33. 10.1016/j.actamat.2005.07.00910.1016/j.actamat.2005.07.009 ↗
34. 10.1016/j.msea.2006.08.09510.1016/j.msea.2006.08.095 ↗
35. 10.1016/S1359-6462(99)00015-910.1016/S1359-6462(99)00015-9 ↗
36. 10.1016/j.scriptamat.2009.02.06210.1016/j.scriptamat.2009.02.062 ↗
37. 10.1016/j.micron.2007.12.01210.1016/j.micron.2007.12.012 ↗
38. Miller G. P. · J. Iron Steel Inst. · 1965 · 20 · 899
39. 10.1016/j.msea.2003.12.02310.1016/j.msea.2003.12.023 ↗