A Novel Fe‐Mn‐Si Shape Memory Alloy With Improved Shape Recovery Properties by VC Precipitation
Source abstract
Abstract
In this work, a nominally new Fe-Mn-Si based shape memory alloy with a small amount of VC was designed. After an optimized thermo-mechanical treatment, a shape recovery of more than 90% after an elongation of 4% could be achieved when the alloys were heated up to 225°C. In addition, high recovery stresses of up to 380 MPa could be obtained after heating to 225°C, whereas 330 MPa were obtained after heating to 160°C.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Shape Memory Alloy Transformations
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (21)
Show source-provided references
1. 10.1016/0001-6160(82)90030-X10.1016/0001-6160(82)90030-X ↗
2. 10.1016/0921-5093(91)90277-T10.1016/0921-5093(91)90277-T ↗
3. Inagaki H. · Z. Metallkd. · 1992 · 83 · 90
4. 10.1007/BF0264732610.1007/BF02647326 ↗
5. 10.4028/www.scientific.net/MSF.56-58.65510.4028/www.scientific.net/MSF.56-58.655 ↗
6. 10.1016/0956-716X(95)00049-210.1016/0956-716X(95)00049-2 ↗
7. 10.1016/S0921-5093(99)00290-710.1016/S0921-5093(99)00290-7 ↗
8. 10.1016/S1359-6462(01)00978-210.1016/S1359-6462(01)00978-2 ↗
9. Kajiwara S. · J. Phys. IV France · 2001 · 11 · 199
10. 10.2320/matertrans.43.58510.2320/matertrans.43.585 ↗
11. 10.1051/jp4:200390410.1051/jp4:2003904 ↗
12. Susan F. · Mater. Trans. · 2005 · 45 · 930
13. 10.1016/j.msea.2006.01.09810.1016/j.msea.2006.01.098 ↗
14. Janke L. · J. Mater. Struct. · 2005 · 38 · 577
15. 10.1016/j.conbuildmat.2005.01.03810.1016/j.conbuildmat.2005.01.038 ↗
16. 10.1007/BF0247955110.1007/BF02479551 ↗
17. 10.1016/j.msea.2005.08.05410.1016/j.msea.2005.08.054 ↗
18. Wang D. F. · Mater. Sci. Eng. A · 2002 · 287 · 604
19. 10.1016/S1359-6454(00)00187-710.1016/S1359-6454(00)00187-7 ↗
20. 10.1016/j.msea.2003.10.35710.1016/j.msea.2003.10.357 ↗
21. 10.1016/j.actamat.2005.04.03510.1016/j.actamat.2005.04.035 ↗