CFx Derived Carbon–FeF₂ Nanocomposites for Reversible Lithium Storage

A new synthesis by reactive intercalation of a functional material in one step, with no solid or liquid by-products, leads to the formation of uniform and nanoscale FeF2 crystallites (9–12 nm) which are clamped in a well conductive graphitic matrix. The composite shows superior performance for the storage of lithium and can be used as cathode material in batteries. Specific capacities of up to 418 mAh g−1 were measured at 40 °C after 25 cycles. As a service to our authors and readers, this journal provides supporting information supplied by the authors. Such materials are peer reviewed and may be re-organized for online delivery, but are not copy-edited or typeset. Technical support issues arising from supporting information (other than missing files) should be addressed to the authors. Please note: The publisher is not responsible for the content or functionality of any supporting information supplied by the authors. Any queries (other than missing content) should be directed to the corresponding author for the article.